Direct metal brazing to cermet feedthroughs
Assignee: United States, ENERGY THE, Department of
•
Filing: 1982-07-29
•
Granted: 1984-12-18
•
Expires: 2002-07-29
Abstract
Abstract An improved method for brazing metallic components to a cermet surface in an alumina substrate eliminates the prior art metallized layer over the cermet via and adjoining alumina surfaces. Instead, a nickel layer is applied over the cermet surface only and metallic components are brazed directly to this nickel coated cermet surface. As a result, heretofore unachievable tensile strength joints are produced. In addition, cermet vias with their brazed metal components can be spaced more closely in the alumina substrate because of the elimination of the prior art metallized alumina surfaces.
Inventors
- 👤 Albert C. Hopper, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:40
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/001; B23K1/00; B23K1/20; Y; Y10; Y10S; Y10S228/00; Y10S228/903
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
74 words
In a method of brazing a metal component to an exposed outer surface of a cermet via in an alumina substrate, which comprises (a) cleaning the cermet via surface to be brazed, (b) applying a metallized layer. and (c) brazing a metal component to the metallized area, the improvement wherein, step (b) consists essentially of applying a nickel layer over the cermet via surface but substantially not beyond said surface onto the alumina substrate.
Claim 2
Dependent Claim
74 words
In a method of brazing a metal component to an exposed outer surface of a cermet via in an alumina substrate, which comprises (a) cleaning the cermet via surface to be brazed, (b) applying a metallized layer. and (c) brazing a metal component to the metallized area, the improvement wherein, step (b) consists essentially of applying a nickel layer over the cermet via surface but substantially not beyond said surface onto the alumina substrate.
Claim 3
Dependent Claim
28 words
A method of claim 1 wherein the metal component brazed to the cermet via is in direct contact with the cermet via only and not the alumina substrate.
Claim 4
Dependent Claim
19 words
A method of claim 1 or 2 wherein the cermet surface is cleaned by mechanical means in step (a).
Claim 5
Dependent Claim
19 words
A method of claim 1 or 2 wherein the nickel layer thickness is about 0.0005 to about 0.001 inch.
Claim 6
Dependent Claim
64 words
A method of claim 1 comprising; cleaning the cermet via surface by microblasting; applying a 0.0005 to 0.001 inch nickel layer to the cermet via surface by electroplating followed by sinter vacuum firing at about 650° C. for at least one hour; and brazing a metal lead to the nickel plated cermet via, the lead not extending beyond the surface of the cermet via.
Claim 7
Dependent Claim
49 words
An alumina substrate having a metal component brazed thereto, comprising, an alumina substrate having an exposed cermet via surface thereon, a nickel layer covering said cermet via surface but substantially not extending over said adjoining alumina substrate, and a metal component brazed to said nickel coated cermet via surface.
Claim 8
Dependent Claim
49 words
An alumina substrate having a metal component brazed thereto, comprising, an alumina substrate having an exposed cermet via surface thereon, a nickel layer covering said cermet via surface but substantially not extending over said adjoining alumina substrate, and a metal component brazed to said nickel coated cermet via surface.
Claim 9
Dependent Claim
29 words
An alumina substrate of claim 6 wherein said brazed metal component covers substantially all of said nickel coated cermet via surface but substantially does not extend beyond said surface.
Claim 10
Dependent Claim
14 words
An alumina substrate of claim 6 wherein said metal component is an electrical lead.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-18 | 1988-06-18 | 1988-12-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-18 | 1992-06-18 | 1992-12-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-18 | 1996-06-18 | 1996-12-18 | $7700.00 | Window Closed / Lapsed |