Stable polyamic acids
Assignee: Elantas PDG Inc
•
Filing: 1980-06-30
•
Granted: 1984-12-11
•
Expires: 2000-06-30
Abstract
Abstract A stable solution of an aromatic polyamic acid of controlled molecular weight, of the type capable of being converted to polyimides, which undergoes relatively little change in viscosity or gelling over extended periods of time at room temperature. Such solution may be prepared by reacting impure aromatic dianhydride with aromatic diamine in a suitable solvent where the ratio of active aromatic diamines is approximately equimolar. Such solution may also be prepared by a two step process which comprises: Step I-Reacting a dianhydride of high purity (99+%) with a diamine in a molar ratio of about 0.95/1 dianhydride/diamine to yield a viscosity below about 10,000 cps, for example from about 2,000 to 6,000 at about a 10-15% solution. Step II-Then adding to I about 0.05 mole of a less pure dianhydride such as from about 97-99% pure dianhydride to yield a 10-15% solution of polyamic acid having a viscosity of about 10,000 cps.
Inventors
- 👤 Daniel J. Lange
- 👤 Daniel J. Marquardt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 00:58
CPC Classifications
C; C08; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/1003; C08G73/1007; C08G73/1028; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678; Y10T428/31681
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
210 words
A two step process of preparing a shelf stable polyamic acid solution resulting from the reaction of an aromatic tetracarboxylic acid dianhydride and an aromatic diamine in an organic solvent which is inert to the system and is a solvent for at least one of the reactants and the product, a solution of said polyamic acid in a solvent consisting of 80% N-methyl pyrrolidone and 20% of a hydrocarbon solvent of boiling range 310°-345° F. having a viscosity of about 10,000 cps at a concentration of about 10-15% which comprises: Step I--reacting an aromatic tetracarboxylic dianhydride of high purity with an aromatic diamine in a molar ratio of about 0.95/1 dianhydride/diamine in an organic reaction solvent which is insert to the system and is a solvent for at least one of the reactants and the product to yield a polyamic acid having a viscosity below about 10,000 cps in about 10-15% solution thereof in a solvent mixture consisting of 80% N-methyl pyrrolidone and 20% of a hydrocarbon solvent of boiling range 310°-345° F.; Step II--then adding to the Step I product about 0.05 mole of a less pure dianhydride to yield a polyamic acid having a viscosity of about 10,000 cps in about a 10-15% solution in said solvent mixture.
Claim 2
Dependent Claim
210 words
A two step process of preparing a shelf stable polyamic acid solution resulting from the reaction of an aromatic tetracarboxylic acid dianhydride and an aromatic diamine in an organic solvent which is inert to the system and is a solvent for at least one of the reactants and the product, a solution of said polyamic acid in a solvent consisting of 80% N-methyl pyrrolidone and 20% of a hydrocarbon solvent of boiling range 310°-345° F. having a viscosity of about 10,000 cps at a concentration of about 10-15% which comprises: Step I--reacting an aromatic tetracarboxylic dianhydride of high purity with an aromatic diamine in a molar ratio of about 0.95/1 dianhydride/diamine in an organic reaction solvent which is insert to the system and is a solvent for at least one of the reactants and the product to yield a polyamic acid having a viscosity below about 10,000 cps in about 10-15% solution thereof in a solvent mixture consisting of 80% N-methyl pyrrolidone and 20% of a hydrocarbon solvent of boiling range 310°-345° F.; Step II--then adding to the Step I product about 0.05 mole of a less pure dianhydride to yield a polyamic acid having a viscosity of about 10,000 cps in about a 10-15% solution in said solvent mixture.
Claim 3
Dependent Claim
23 words
The process of claim 1 where the viscosity of the Step I product in said solvent mixture is about 2,000 to 6,000 cps.
Claim 4
Dependent Claim
147 words
A two step process of preparing the polyamic acid solution of claim 1 which comprises: Step I--reacting a high purity aromatic dianhydride selected from the group consisting of pyromellitic dianhydride, benzophenone dianhydride and mixtures thereof with an aromatic diamine in a molar ratio of about 0.95/1 dianhydride/diamine in an organic reaction solvent which is inert to the system and is a solvent for at least one of the reactants and the product to yield a polyamic acid having a viscosity below about 10,000 cps in about a 10-15% solution thereof in a solvent mixture consisting of 80% N-methyl pyrrolidone and 20% of a hydrocarbon solvent of boiling range 310°-345° F.,; Step II--then adding to the Step I product about 0.05 mole of a less pure dianhydride to yield a polyamic acid having a viscosity of about 10,000 cps in about a 10-15% solution in said solvent mixture.
Claim 5
Dependent Claim
23 words
The process of claim 3 where the viscosity of the Step I product is about 2,000 to 6,000 cps in said solvent mixture.
Claim 6
Dependent Claim
145 words
A two step process of preparing the polyamic acid solution of claim 3 which comprises Step I--reacting a high purity aromatic dianhydride selected from the group consisting of pyromellitic dianhydride, benzophenone dianhydride and mixtures thereof with oxydianiline in a molar ratio of about 0.95/1 dianhydride/oxydianiline in an organic reaction solvent which is inert to the system and is a solvent for at least one of the reactants and the product to yield a polyamic acid having a viscosity of about 10,000 cps in about a 10-15% solution thereof in a solvent mixture consisting of 80% N-methyl pyrrolidone and 20% of a hydrocarbon solvent of boiling range 310°-345° F.; Step II--then adding to the Step I product about 0.05 mole of a less pure dianhydride to yield a polyamic acid having a viscosity of about 10,000 cps in about a 10-15% solution in said solvent mixture.
Claim 7
Dependent Claim
25 words
The process of claim 5 wherein said reaction solvent consists of 80% N-methyl pyrrolidone and 20% of a hydrocarbon solvent of boiling range 310°-345° F.
Claim 8
Dependent Claim
19 words
The process of claim 5 where the viscosity of the Step I product is about 2,000 to 6,000 cps.
References Cited (Backward Citations)
US3179614A
Cited
US3179634A
Cited
US3179631A
Cited
US3179632A
Cited
US3179633A
Cited
US3629180A
Cited
US3663510A
Cited
US3652500A
Cited
US3663492A
Cited
US3891601A
Cited
US3770686A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-11 | 1988-06-11 | 1988-12-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-11 | 1992-06-11 | 1992-12-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-11 | 1996-06-11 | 1996-12-11 | $7700.00 | Window Closed / Lapsed |