Process for radical polymerizing acrylic monomers
Assignee: Nitto Denko Corp
•
Filing: 1983-02-18
•
Granted: 1984-12-11
•
Expires: 2003-02-18
Abstract
Abstract A process for polymerizing acrylic monomers is disclosed. The process involves providing a reactor which is generally in the shape of a screw type reactor having temperature control means thereon. The reactor is continually charged with a supply of acrylic monomers having a viscosity of 10 poises or less at ordinary temperature. The acrylic monomers are continually moved through the reactor by turning of the screw within the reactor in order to cause the acrylic monomers to continually contact renewed surfaces within the reactor. The temperature in the reactor is controlled within two or more zones within the reactor in order to increase the viscosity of the acrylic monomers in the reactor by rapid polymerization within an initial area and then allow polymerization to proceed to one or more additional areas in the reactor to a prescribed rate of conversion. Polymerized product is continuously removed from the reactor.
Inventors
- 👤 Naoki Matsuoka
- 👤 Hiroshi Matsumoto
- 👤 Yutaka Hori
- 👤 Yoshio Miki
- 👤 Kenji Sano
- 👤 Ichiro Ijichi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:46
CPC Classifications
B; B01; B01J; B01J19/00; B01J19/18; B01J19/20
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
194 words
A process for radical polymerizing acrylic monomers, comprising the steps of: providing a reactor having a temperature control means thereon; continuously charging the reactor with a supply of acrylic monomers having a viscosity of 10 poises or less at ordinary temperatures wherein the acrylic monomers comprise at least 50% by weight of alkyl esters of acrylic acids; continuously conveying the supply of acrylic monomer through a conveyance course of the reactor thereby causing the supply to continuously contact renewed surfaces of the reactor wherein the viscosity gradient in the reactor is not less than 100/min; controlling the temperature of the supply in the reactor such that the viscosity of the supply in the reactor can be increased by rapid polymerization of the acrylic monomers in the first half of the reactor to at least 100 poises and the polymerization thereof can proceed up to a prescribed rate of conversion in a secondary area of the reactor wherein the temperature in the first half of the reactor is 40° to 120° C. and the temperature in the secondary area of the reactor is 60° to 150° C.; and continuously recovering polymerized product from the reactor.
Claim 2
Dependent Claim
194 words
A process for radical polymerizing acrylic monomers, comprising the steps of: providing a reactor having a temperature control means thereon; continuously charging the reactor with a supply of acrylic monomers having a viscosity of 10 poises or less at ordinary temperatures wherein the acrylic monomers comprise at least 50% by weight of alkyl esters of acrylic acids; continuously conveying the supply of acrylic monomer through a conveyance course of the reactor thereby causing the supply to continuously contact renewed surfaces of the reactor wherein the viscosity gradient in the reactor is not less than 100/min; controlling the temperature of the supply in the reactor such that the viscosity of the supply in the reactor can be increased by rapid polymerization of the acrylic monomers in the first half of the reactor to at least 100 poises and the polymerization thereof can proceed up to a prescribed rate of conversion in a secondary area of the reactor wherein the temperature in the first half of the reactor is 40° to 120° C. and the temperature in the secondary area of the reactor is 60° to 150° C.; and continuously recovering polymerized product from the reactor.
Claim 3
Dependent Claim
20 words
A process as claimed in claim 1, wherein the reactor is in the form of a single screw extruder reactor.
Claim 4
Dependent Claim
19 words
A process as claimed in claim 1, wherein the reactor is in the form of a twin extruder reactor.
Claim 5
Dependent Claim
44 words
A process as claimed in claim 2, wherein the single screw extruder reactor is comprised of a screw contained within a barrel in such a manner that as the screw is turned the acrylic monomer is moved through the reactor on the conveyance course.
Claim 6
Dependent Claim
33 words
A process as claimed in claim 2, wherein the distance between the outer portions of the screw and the inner diameter of the barrel is within the range of 0.5 to 2 mm.
Claim 7
Dependent Claim
35 words
A process as claimed in claim 1, wherein the reactor is further charged with an initiator in an amount of 0.1 to 1 part by weight per 100 parts by weight of the acrylic monomers.
Claim 8
Dependent Claim
32 words
A process as claimed in claim 1, wherein the reactor further includes additives in an amount of 25 parts by weight or less per 100 parts by weight of the acrylic monomers.
Claim 9
Dependent Claim
21 words
A process as claimed in claim 1, wherein the prescribed rate of conversion is within the range of 93 to 93%.
Claim 10
Dependent Claim
33 words
A process as claimed in claim 3, wherein the distance between the outer portions of the screw and the inner diameter of the barrel is within the range of 0.5 to 2 mm.
Claim 11
Dependent Claim
14 words
A process as claimed in claim 6, wherein the initiator is a redox initiator.
Claim 12
Dependent Claim
18 words
A process as claimed in claim 1, wherein the velocity gradient of the reactor is 3000 to 50,000/min.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-11 | 1988-06-11 | 1988-12-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-11 | 1992-06-11 | 1992-12-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-11 | 1996-06-11 | 1996-12-11 | $7700.00 | Window Closed / Lapsed |