US4487815A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Temperature resistant coating composite
Assignee: Diamond Shamrock Corp
•
Filing: 1983-03-07
•
Granted: 1984-12-11
•
Expires: 2003-03-07
Abstract
Abstract Temperature resistant substrates, and particularly metals such as ferrous metals, coated for corrosion resistance with coatings containing particulate metal and hexavalent chromium-providing substance can now be made further corrosion resistant, as well as having excellent heat resistance, with a coating composite. In the composite, the undercoating contains a boric acid component plus substantial amounts of finely-divided aluminum as particulate metal. As an adjacent top layer, a coating containing silica substance is used.
Inventors
- 👤 Terry E. Dorsett
- 👤 David P. Rininger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 06:26
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/08; C09D5/10; B; B05; B05D; B05D7/00; B05D7/14; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12049; Y10T428/12056; Y10T428/12063; Y10T428/12097; Y10T428/12104; Y10T428/12111
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
179 words
A heat-resistant and corrosion-resistant coated substrate protected with a coating composite containing particulate metal, wherein at least two adjacent layers of the coating composite are substantially resin free and comprise an undercoating and a topcoating, with the undercoating containing said particulate metal, each coating being established from compositions curable to water resistant protective coatings, with the undercoating being applied as a substantially resin free composites containing, in liquid medium, a hexavalent-chromium-providing substance, boric acid component, and particulate zinc plus particulate aluminum, with the aluminum providing greater than 15, but less than 85 percent, by weight of combined particulate zinc and aluminum and with said undercoating being applied in an amount sufficient to provide, upon curing, above 10 but not substantially above about 5000 milligrams per square foot of coated substrate of particulate metal, and with said topcoating being applied as a substantially resin free as well as particulate metal free composition containing silica substance in liquid medium in an amount sufficient to provide above about 50 milligrams per square foot of coated substrate of silica substance in cured topcoating.
Claim 2
Dependent Claim
179 words
A heat-resistant and corrosion-resistant coated substrate protected with a coating composite containing particulate metal, wherein at least two adjacent layers of the coating composite are substantially resin free and comprise an undercoating and a topcoating, with the undercoating containing said particulate metal, each coating being established from compositions curable to water resistant protective coatings, with the undercoating being applied as a substantially resin free composites containing, in liquid medium, a hexavalent-chromium-providing substance, boric acid component, and particulate zinc plus particulate aluminum, with the aluminum providing greater than 15, but less than 85 percent, by weight of combined particulate zinc and aluminum and with said undercoating being applied in an amount sufficient to provide, upon curing, above 10 but not substantially above about 5000 milligrams per square foot of coated substrate of particulate metal, and with said topcoating being applied as a substantially resin free as well as particulate metal free composition containing silica substance in liquid medium in an amount sufficient to provide above about 50 milligrams per square foot of coated substrate of silica substance in cured topcoating.
Claim 3
Dependent Claim
19 words
The coated substrate of claim 1 wherein said undercoating is the first coating on the surface of such substrate.
Claim 4
Dependent Claim
20 words
The coated substrate of claim 1 wherein the liquid medium of both said undercoating and said topcoating compositions contains water.
Claim 5
Dependent Claim
17 words
The coated substrate of claim 3 wherein said undercoating liquid medium comprises water plus high-boiling organic liquid.
Claim 6
Dependent Claim
38 words
The coated substrate of claim 1 wherein said undercoating is established from a heat-curable composition containing a boric acid component in an amount from about 0.4 percent by weight of said composition up to saturation of said component.
Claim 7
Dependent Claim
29 words
The coated substrate of claim 5 wherein said chromic acid constituent is selected from the group consisting of chromic acid, water-soluble metal salts of chromic acid, and mixtures thereof.
Claim 8
Dependent Claim
27 words
The coated substrate of claim 5 wherein said boric acid component is selected from the group consisting of orthoboric acid, metaboric acid, tetraboric acid and boron oxide.
Claim 9
Dependent Claim
22 words
The coated substrate of claim 1 wherein at least a portion of the particulate metal of said undercoating is in flake form.
Claim 10
Dependent Claim
43 words
The coated substrate of claim 1 wherein said undercoating contains not above about 500 milligrams per square foot of coated substrate of chromium, with the coating containing a weight ratio of chromium, as chromium, to particulate metal of not substantially above about 0.5:1.
Claim 11
Dependent Claim
28 words
The coated substrate of claim 1 wherein said topcoating upon curing provides not substantially above about 2000 milligrams per square foot of coated substrate of said silica substance.
Claim 12
Dependent Claim
31 words
The coated substrate of claim 1 wherein said aluminum provides greater than 25 percent, but less than 75 percent, by weight, of the combined particulate zinc and aluminum in said undercoating.
Claim 13
Dependent Claim
24 words
The coated substrate of claim 11 wherein said aluminum provides less than about 65 percent by weight of the combined particulate zinc and aluminum.
Claim 14
Independent Claim
173 words
The method of protecting a substrate with a heat-resistant as well as corrosion-resistant coating, which method comprises: (a) establishing a substantially resin free, hexavalent-chromium-containing coating composition in liquid medium; (b) admixing with said coating composition a boric acid component; (c) providing said coating composition with a particulate metal constituent containing particulate zinc plus particulate aluminum wherein aluminum provides greater than 15, but less than 85 percent, by weight, of the combined particulate zinc plus aluminum; (d) applying the resulting coating composition to the substrate as an undercoating in an amount sufficient to provide, upon curing, above 10 but not substantially above about 5000 milligrams per square foot of coated substrate of particulate metal; (e) vaporizing volatile substituents from said undercoating; (f) applying a particulate metal free as well as substantially resin free topcoating composition, containing silica substance in liquid medium, on the undercoated substrate and in an amount sufficient to provide above about 50 milligrams per square foot of coated substrate of silica substance in cured topcoating; and (g) curing said applied topcoating.
Claim 15
Independent Claim
173 words
The method of protecting a substrate with a heat-resistant as well as corrosion-resistant coating, which method comprises: (a) establishing a substantially resin free, hexavalent-chromium-containing coating composition in liquid medium; (b) admixing with said coating composition a boric acid component; (c) providing said coating composition with a particulate metal constituent containing particulate zinc plus particulate aluminum wherein aluminum provides greater than 15, but less than 85 percent, by weight, of the combined particulate zinc plus aluminum; (d) applying the resulting coating composition to the substrate as an undercoating in an amount sufficient to provide, upon curing, above 10 but not substantially above about 5000 milligrams per square foot of coated substrate of particulate metal; (e) vaporizing volatile substituents from said undercoating; (f) applying a particulate metal free as well as substantially resin free topcoating composition, containing silica substance in liquid medium, on the undercoated substrate and in an amount sufficient to provide above about 50 milligrams per square foot of coated substrate of silica substance in cured topcoating; and (g) curing said applied topcoating.
Claim 16
Dependent Claim
29 words
The method of claim 13 wherein said volatile substituents are vaporized in step (e) by subjecting said undercoating to elevated temperature for a sufficient time to cure said undercoating.
Claim 17
Dependent Claim
44 words
The method of claim 13 wherein said volatile substituents are vaporized from the undercoating by heating at a temperature above about 350° F. and said topcoating is cured by heating at a temperature within the range from about 200° F. to about 800° F.
Claim 18
Dependent Claim
32 words
The method of claim 13 wherein said undercoating is established as a dry and water-resistant undercoating by vaporizing volatile substituents at elevated temperature, and said topcoating is thereafter applied without intermediate cooling.
References Cited (Backward Citations)
US3423229A
Cited
US3656975A
Cited
US3907608A
Cited
US4229495A
Cited
JPS53125239A
Cited
US4266975A
Cited
US4365003A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-11 | 1988-06-11 | 1988-12-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-11 | 1992-06-11 | 1992-12-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-11 | 1996-06-11 | 1996-12-11 | $7700.00 | Window Closed / Lapsed |