Silicate treatment for coated substrate

Claim 2

A coated metal substrate protected with an undercoating/topcoating composite which is resin-free and contains particulate metal, with the proviso that only the undercoating of the composite contains the particulate metal while the total of the coating composite is substantially resin-free, each coating being established from compositions curable to water resistant protective coatings, with the undercoating being applied as a substantially resin free composition containing, in liquid medium, a hexavalent-chromium-providing substance plus the particulate metal and in an amount sufficient to provide, upon curing, above 10 but not substantially above about 5000 milligrams per square foot of coated substrate of particulate metal, and said topcoating being substantially resin free and containing silica substance in liquid medium in an amount sufficient to provide above about 50 milligrams per square foot of coated substrate of silica substance in cured coating.

Claim 3

The coated metal substrate of claim 1 characterized by having said undercoating as the first coating on the surface of said substrate.

Claim 4

The coated metal substrate of claim 1 further characterized by having a liquid medium of both said undercoating and said subsequent coating containing water.

Claim 5

The coated metal substrate of claim 3 wherein said undercoating liquid medium comprises water plus high-boiling organic liquid.

Claim 6

The coated metal substrate of claim 1 wherein said undercoating is established from a heat-curable composition.

Claim 7

The coated metal substrate of claim 5 wherein said undercoating is obtained after heating at a temperature above about 350° F. and said topcoating is obtained after heating at a temperature within the range from about 200° F. to about 1000° F.

Claim 8

The coated metal substrate of claim 1 wherein at least a portion of the particulate metal of said undercoating is in flake form.

Claim 9

The coated metal substrate of claim 1 wherein said undercoating contains not above about 500 milligrams per square foot of coated substrate of chromium, with the coating containing a weight ratio of chromium, as chromium, to particulate metal of not substantially above about 0.5:1.

Claim 10

The coated metal substrate of claim 1 wherein said topcoating upon curing provides not substantially above about 2000 milligrams per square foot of coated substrate of said silica substance.

Claim 13

The method of claim 10 wherein said undercoating is heat cured prior to application of said topcoating.

Claim 14

The method of claim 10 wherein said undercoating is established, by heating, as a dry and water-resistant undercoating, and said topcoating is thereafter applied without intermediate cooling.

Claim 15

In the method of preparing a corrosion resistant coated metal substrate protected with a pulverulent-metal-containing undercoating/topcoating composite, where only the undercoating contains the pulverulent metal, and where said substrate has as said undercoating a substantially resin free coating extablished from a heat-curable composition containing a hexavelent-chromium-providing substance and said coating contains above 10 but not substantially above about 5000 milligrams per square foot of coated substrate of pulverulent metal and not above about 500 milligrams per square foot of coated substrate of chromium, with the coating containing a weight ratio of chromium, as chromium, to pulverulent metal of non-substantially above about 0.5:1, the improvement which comprises: (a) supplying as a topcoating on said established coating a substantially resin free silica substance composition curable to a water resistant protective coating and containing from about 0.5 to about 50 weight percent solids in liquid medium, said composition being applied in an amount sufficient to provide from about 50 to about 2000 milligrams per square foot of coated substrate of silica substance; and (b) curing the applied topcoat composition to said water resistant protective coating.

Claim 16

In the method of preparing a corrosion resistant coated metal substrate protected with a pulverulent-metal-containing undercoating/topcoating composite, where only the undercoating contains the pulverulent metal, and where said substrate has as said undercoating a substantially resin free coating extablished from a heat-curable composition containing a hexavelent-chromium-providing substance and said coating contains above 10 but not substantially above about 5000 milligrams per square foot of coated substrate of pulverulent metal and not above about 500 milligrams per square foot of coated substrate of chromium, with the coating containing a weight ratio of chromium, as chromium, to pulverulent metal of non-substantially above about 0.5:1, the improvement which comprises: (a) supplying as a topcoating on said established coating a substantially resin free silica substance composition curable to a water resistant protective coating and containing from about 0.5 to about 50 weight percent solids in liquid medium, said composition being applied in an amount sufficient to provide from about 50 to about 2000 milligrams per square foot of coated substrate of silica substance; and (b) curing the applied topcoat composition to said water resistant protective coating.

Claim 17

The method of claim 13 wherein said topcoating is cured at a temperature within the range from about 200° F. to about 1000° F.