Process for preparing film of poly{[benzo(1,2-d:4,5-d')bisthiazole-2,6-diyl]-1,4-phenylene}, its cis isomer or mixtures thereof

Claim 2

A process for preparing film of poly{[benzo(1,2-d:4,5-d')bisthiazole-2,6-diyl]-1,4-phenylene}, its cis isomer or mixtures thereof comprising: (a) forming a solution of poly{[benzo(1,2-d:4,5-d')bisthiazole-2,6-diyl]-1,4-phenylene}, its cis isomer or mixtures therof; (b) extruding a film of the solution on a casting roll which rotates at a surface speed greater than the speed of extrusion thereby yielding a stretch of from about 100 to about 2400%; (c) washing the film; (d) subjecting the film to a temperature in the range of from about 100° to about 150° C. for from about 5 to about 30 seconds; and (e) recovering the film.

Claim 3

The process of claim 1 wherein the solution comprises from about 5 to about 15% by weight of poly{[benzo(1,2-d:4,5-d')bisthiazole-2,6-diyl]-1,4-phenylene}, its cis isomer or mixtures thereof.

Claim 4

The process of claim 2 wherein the solution is formed by dissolving the poly{[benzo(1,2-d:4,5-d')bisthiazole-2,6-diyl]1,4-phenylene}, its cis isomer or mixtures thereof in a solvent selected from the group consisting of polyphosphoric acid, dehydrating phosphate acids and mixtures thereof.

Claim 5

The process of claim 3 wherein the casting roll has a surface speed of from about 1 to about 10 meters per min.

Claim 6

The process of claim 4 wherein the casting roll is contacted with a coagulation bath comprised of an aqueous solution containing from about 0 to about 10% by weight of a material selected from the group consisting of phosphoric acid and methanol.

Claim 7

The process of claim 5 wherein the film is washed with a liquid selected from the group consisting of water and methanol.

Claim 8

The process of claim 6 wherein heating of the film is conducted in an atmosphere comprised of nitrogen.

Claim 9

The process of claim 1 wherein the film is comprised of poly{[benzo(1,2-d:4,5-d')bisthiazole-2,6-diyl]-1,4-phenylene}.

Claim 10

A process for preparing film of poly{[benzo(1,2-d:4,5-d')bisthiazole-2,6-diyl]-1,4-phenylene}, its cis isomer or mixtures thereof comprising: (a) forming a reaction mixture comprising the reactants 2,5-diamino-1,4-benzenedithiol dihydrochloride or 2,4-diamino-1,5-benzenedithiol dihydrochloride or mixtures thereof and terephthalic acid and a reaction medium selected from the group consisting of polyphosphoric acid, dehydrating phosphate acids and mixtures thereof; (b) polymerizing the reactants whereby a solution of poly{[benzo(1,2-d:4,5-d')bisthiazole-2,6-diyl]-1,4-phenylene}, its cis isomer or mixtures thereof is formed; (c) extruding a film of the solution on a casting roll which rotates at a surface speed greater than the speed of extrusion thereby yielding a stretch of from about 100 to about 2400%; (d) washing the film; (e) subjecting the film to a temperature in the range of from about 100° to about 150° C. for from about 5 to about 30 seconds; and (f) recovering the film.

Claim 11

A process for preparing film of poly{[benzo(1,2-d:4,5-d')bisthiazole-2,6-diyl]-1,4-phenylene}, its cis isomer or mixtures thereof comprising: (a) forming a reaction mixture comprising the reactants 2,5-diamino-1,4-benzenedithiol dihydrochloride or 2,4-diamino-1,5-benzenedithiol dihydrochloride or mixtures thereof and terephthalic acid and a reaction medium selected from the group consisting of polyphosphoric acid, dehydrating phosphate acids and mixtures thereof; (b) polymerizing the reactants whereby a solution of poly{[benzo(1,2-d:4,5-d')bisthiazole-2,6-diyl]-1,4-phenylene}, its cis isomer or mixtures thereof is formed; (c) extruding a film of the solution on a casting roll which rotates at a surface speed greater than the speed of extrusion thereby yielding a stretch of from about 100 to about 2400%; (d) washing the film; (e) subjecting the film to a temperature in the range of from about 100° to about 150° C. for from about 5 to about 30 seconds; and (f) recovering the film.

Claim 12

The process of claim 9 wherein the reaction mixture comprises 2,5-diamino-1,4-benzenedithiol dihydrochloride and weight of terephthalic acid in about equimolar amounts.

Claim 13

The process of claim 10 wherein polymerizing the reactants is performed at a temperature in the range of from about 150° to about 220° C. and a pressure of from about 720 to about 800 mm.Hg.

Claim 14

The process of claim 11 wherein polymerizing the reactants is performed in an atmosphere selected from the group consisting of nitrogen, helium, argon, neon, krypton, carbon dioxide and mixtures thereof.

Claim 15

The process of claim 12 wherein the casting roll has a surface speed of from about 1 to about 10 m./min.

Claim 16

The process of claim 13 wherein the casting roll is contacted with a coagulation bath comprised of an aqueous solution containing from about 0 to about 10% by weight of a material selected from the group consisting of phosphoric acid and methanol.

Claim 17

The process of claim 14 wherein the film is washed with a liquid selected from the group consisting of water and methanol.

Claim 18

The process of claim 15 wherein heating the film is conducted in an atmosphere comprised of nitrogen.