Process for making vulcanized carbon black-reinforced bromobutyl rubber films
Assignee: Polysar Ltd
•
Filing: 1984-03-16
•
Granted: 1984-12-04
•
Expires: 2004-03-16
Abstract
Abstract A process is provided for preparing a vulcanized carbon black-reinforced chloro- or bromobutyl rubber film comprising admixing a polyfunctional amine vulcanization system with a carbon black-reinforced chloro- or bromobutyl rubber latex containing one or more selected emulsifiers, forming a film from the resulting mixture, drying said film and heating the dried film to provide the vulcanized film. The process may be used in the manufacture of coatings, dipped goods and chemical resistant impermeable treated fabrics.
Inventors
- 👤 Erhardt Fischer
- 👤 Douglas C. Edwards
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:35
CPC Classifications
D; D06; D06M; D06M15/00; D06M15/693; C; C08; C08K; C08K3/00; C08K3/02; C08K3/04; C08K5/00; C08K5/16; C08K5/17
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
192 words
A process for making a vulcanized carbon black-reinforced chloro- or bromobutyl rubber film comprising: (a) admixing a polyfunctional amine vulcanization system with a carbon black-reinforced chloro- or bromobutyl rubber latex wherein said latex contains an emulsifier selected from (i) ammonium and alkali metal C 12-24 fatty acid soaps and mixtures of any two or more of said soaps, (ii) ammonium and alkali metal salts of polyethoxylated sulfates of C 6-20 alkyl alcohols wherein the number of ethoxylate units is from about 2 to about 50, and (iii) polyethoxylated C 6-14 alkylphenoxy ethanols and the ammonium and alkali metal salts of the sulfates thereof wherein the number of ethoxylate units is from about 2 to about 150; (b) forming a film from the resulting mixture; (c) drying said film in air at a temperature of from about 20° to about 80° C. for a time sufficient to remove essentially all of the water from said film; and (d) heating the dried film for a time of from about 3 to about 15 minutes at a temperature of from about 100° to about 175° C. to cause the formation of said vulcanized rubber film.
Claim 2
Dependent Claim
192 words
A process for making a vulcanized carbon black-reinforced chloro- or bromobutyl rubber film comprising: (a) admixing a polyfunctional amine vulcanization system with a carbon black-reinforced chloro- or bromobutyl rubber latex wherein said latex contains an emulsifier selected from (i) ammonium and alkali metal C 12-24 fatty acid soaps and mixtures of any two or more of said soaps, (ii) ammonium and alkali metal salts of polyethoxylated sulfates of C 6-20 alkyl alcohols wherein the number of ethoxylate units is from about 2 to about 50, and (iii) polyethoxylated C 6-14 alkylphenoxy ethanols and the ammonium and alkali metal salts of the sulfates thereof wherein the number of ethoxylate units is from about 2 to about 150; (b) forming a film from the resulting mixture; (c) drying said film in air at a temperature of from about 20° to about 80° C. for a time sufficient to remove essentially all of the water from said film; and (d) heating the dried film for a time of from about 3 to about 15 minutes at a temperature of from about 100° to about 175° C. to cause the formation of said vulcanized rubber film.
Claim 3
Dependent Claim
76 words
The process according to claim 1 wherein the rubber is bromobutyl rubber, the amount of carbon black used is from about 10 to about 70 parts by dry weight, the amount of said emulsifier used is from about 5 to about 15 parts by dry weight, and the amount of said vulcanization system used is from about 0.1 to about 20 parts by dry weight, all based on 100 parts by dry weight of bromobutyl rubber.
Claim 4
Dependent Claim
76 words
The process according to claim 1 wherein the rubber is chlorobutyl rubber, the amount of carbon black used is from about 10 to about 70 parts by dry weight, the amount of said emulsifier used is from about 5 to about 15 parts by dry weight, and the amount of said vulcanization system used is from about 0.1 to about 20 parts by dry weight, all based on 100 parts by dry weight of chlorobutyl rubber.
Claim 5
Dependent Claim
13 words
The process according to claim 2 wherein the emulsifier is selected from (i).
Claim 6
Dependent Claim
61 words
The process according to claim 4 wherein the amount of carbon black is from about 35 to about 50 parts, the amount of emulsifier is from about 7 to about 14 parts, the amount of vulcanization system is from about 0.5 to about 10 parts, and wherein the temperature used in step (d) is from about 130° to about 175° C.
Claim 7
Dependent Claim
48 words
The process according to claim 3 wherein the amount of emulsifier is from about 7 to about 10 parts, the amount of vulcanization system is from about 0.5 to about 5 parts, and wherein the temperature used in step (d) is from about 155° to about 175° C.
Claim 8
Dependent Claim
12 words
The process according to claim 5 wherein said emulsifier is potassium oleate.
Claim 9
Dependent Claim
12 words
Tne process according to claim 6 wherein said emulsifier is potassium oleate.
References Cited (Backward Citations)
US2944038A
Cited
US2964489A
Cited
US2983705A
Cited
US3011996A
Cited
US2983706A
Cited
US2983707A
Cited
US3062767A
Cited
US2984642A
Cited
US3534123A
Cited
US3646166A
Cited
US3898253A
Cited
US4256857A
Cited
US3998772A
Cited
US4357432A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-12-04 | 1988-06-04 | 1988-12-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-12-04 | 1992-06-04 | 1992-12-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-12-04 | 1996-06-04 | 1996-12-04 | $7700.00 | Window Closed / Lapsed |