Oil-resistant, room temperature-curable organopolysiloxane composition
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1983-10-27
•
Granted: 1984-11-27
•
Expires: 2003-10-27
Abstract
Abstract The invention provides a room temperature-curable organopolysiloxane composition comprising (a) a diorganopolysiloxane terminated at both molecular chain ends with silanolic hydroxy groups, (b) a methylpolysiloxane composed of monofunctional siloxy units Me3SiO1/2 tetrafunctional siloxane units SiO2 in a specified molar ratio, (c) an organosilane or organopolysiloxane having at least three hydrolyzable groups bonded to the silicon atom(s) per molecule, (d) oxide, carbonate or hydroxycarbonate of zinc, and (e) a thiazole, thiuram or dithiocarbamate compound. The composition is curable by standing in air into a rubbery elastomer which is highly resistant against oils, e.g. engine oils and gear oils in automobiles, even at elevated temperatures.
Inventors
- 👤 Yoshio Inoue
- 👤 Takehide Okami
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 21:49
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/36; C08K5/39; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K3/24; C08K3/26; C08K5/45; C08K5/46; C08K5/47; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/14; C08G77/16; C08G77/18; C08G77/20; C08G77/22; C08G77/26; C08G77/70; Y; Y10; Y10S; Y10S528/00; Y10S528/901
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
160 words
An oil-resistant, room temperature-curable organopolysiloxane composition which comprises: (a) 100 parts by weight of a diorganopolysiloxane having a degree of polymerization of at least 5 and terminated at both molecular chain ends each with a hydroxy group directly bonded to the terminal silicon atom; (b) from 2 to 30 parts by weight of an organopolysiloxane composed of monofunctional siloxy units expressed by the general formula R 3 SiO 1/2 , in which R is a substituted or unsubstituted monovalent hydrocarbon group and tetrafunctional siloxane units expressed by the formula SiO 2 in a molar ratio of 0.5:1 to 1:1; (c) from 0.5 to 30 parts by weight of an organosilane or an organopolysiloxane having, in a molecule, at least three hydrolyzable groups bonded to the silicon atom or atoms; and (d) from 2 to 200 parts by weight of an inorganic zinc compound in a powdery form selected from the class consisting of zinc oxide, zinc carbonate and zinc hydroxycarbonate.
Claim 2
Dependent Claim
160 words
An oil-resistant, room temperature-curable organopolysiloxane composition which comprises: (a) 100 parts by weight of a diorganopolysiloxane having a degree of polymerization of at least 5 and terminated at both molecular chain ends each with a hydroxy group directly bonded to the terminal silicon atom; (b) from 2 to 30 parts by weight of an organopolysiloxane composed of monofunctional siloxy units expressed by the general formula R 3 SiO 1/2 , in which R is a substituted or unsubstituted monovalent hydrocarbon group and tetrafunctional siloxane units expressed by the formula SiO 2 in a molar ratio of 0.5:1 to 1:1; (c) from 0.5 to 30 parts by weight of an organosilane or an organopolysiloxane having, in a molecule, at least three hydrolyzable groups bonded to the silicon atom or atoms; and (d) from 2 to 200 parts by weight of an inorganic zinc compound in a powdery form selected from the class consisting of zinc oxide, zinc carbonate and zinc hydroxycarbonate.
Claim 3
Dependent Claim
40 words
The oil-resistant, room temperature-curable organopolysiloxane composition as claimed in claim 1 which further comprises: (e) from 0.1 to 20 parts by weight of an organic sulfur compound selected from the class consisting of thiazole compounds, thiuram compounds and dithiocarbamate compounds.
Claim 4
Dependent Claim
27 words
The oil-resistant, room temperature-curable organopolysiloxane composition as claimed in claim 1 wherein the group denoted by the symbol R in the component (b) is a methyl group.
Claim 5
Dependent Claim
32 words
The oil-resistant, room temperature-curable organopolysiloxane composition as claimed in claim 1 wherein the diorganopolysiloxane as the component (a) has a viscosity in the range from 25 to 500,000 centistokes at 25° C.
Claim 6
Dependent Claim
20 words
The oil-resistant, room temperature-curable organopolysiloxane composition as claimed in claim 1 wherein the diorganopolysiloxane is a dimethylpolysiloxane or a methylphenylpolysiloxane.
Claim 7
Dependent Claim
34 words
The compositions of claim 1 wherein component (a) is an α,ω-dihydroxy diorganopolysiloxane having the formula HO--SiR.sub.2 --O).sub.n OH wherein R is a substituted or unsubstituted monovalent hydrocarbon group and n is a positive integer.
Claim 8
Dependent Claim
13 words
The composition of claim 6 wherein R is alkyl, cycloalkyl, alkenyl, or aryl.
Claim 9
Dependent Claim
11 words
The composition of claim 6 wherein n is at least 5.
Claim 10
Dependent Claim
19 words
The composition of claim 6 wherein the diorganopolysiloxane has a viscosity in the range from 25 to 500,000 centistokes.
Claim 11
Dependent Claim
20 words
The composition of claim 1 wherein the hydrolyzable group is an alkoxy, organoketoxime, hydrocarbyl-substituted amino, organoamido, dihydrocarbyl aminoxy or alkenyloxy.
Claim 12
Dependent Claim
34 words
The composition of claim 10 wherein the hydrolyzable group is selected from the group consisting of methoxy, ethoxy, propoxy, isopropoxy, butoxy, acetoxime, butanonoxime, dimethylamino, diethylamino, cyclohexylamino, N-methyl acetamide, dimethyl aminoxy, diethyl aminoxy, and isopropenyloxy.
References Cited (Backward Citations)
US3696127A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-27 | 1988-05-28 | 1988-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-27 | 1992-05-28 | 1992-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-27 | 1996-05-28 | 1996-11-27 | $7700.00 | Window Closed / Lapsed |