Abstract A process for producing ethylene-propylene block copolymer by the use of a catalyst employed for producing isotactic polypropylene is provided. This process is characterized in that a gas phase polymerization of propylene is substantially carried out in the presence of the catalyst obtained by combining a titanium trichloride composition with an average particle size of 10˜100 μ and an organic aluminum to form the propylene polymer segment with a specific surface area more than 0.015 m 2 /g at a yield of more than 3,000 g per 1 g of the titanium trichloride composition in the first step, and then a gas phase polymerization of a mixture of polypropylene and ethylene is successively carried out in the second step to form the copolymer segment with a copolymerization ratio of propylene:ethylene being 5˜80 weight %:95˜20 weight %, wherein the polymerized amount of the second step is 10-40% of total polymerized amount and wherein normal hexane extraction ratio (75° C., 1 hour) of the ethylene-propylene block copolymer powders obtained is 1˜10 weight %. The process of the present invention is one having an extremely high productivity industrially, and the modified polypropylene obtained has a superior low-temperature-impact strength and brittle temperature.
In a process for producing ethylene-propylene block copolymer by the use of a catalyst employed for producing isotactic polypropylene, the process for producing a modified polypropylene which is characterized in that a gas phase polymerization of propylene is substantially carried out in the presence of the catalyst obtained by combining a titanium trichloride composition with an average particle size of 10˜100μ and an organic aluminum to form the propylene polymer segment with a specific surface area more than 0.015 m 2 /g at an yield of more than 3,000 g per 1 g of the titanium trichloride composition in the first step, and then a gas phase polymerization of a mixture of polypropylene and ethylene is successively carried out in the second step to form the copolymer segment with a copolymerization ratio of propylene:ethylene being 5˜80 weight %:95˜20 weight %, wherein the polymerized amount of the second step is 10˜40% of total polymerized amount and wherein normal hexane extraction ratio (75° C., 1 hour) of the ethylene-propylene block copolymer powders obtained is 1˜ 10 weight %.
Claim 2
Dependent Claim
176 words
In a process for producing ethylene-propylene block copolymer by the use of a catalyst employed for producing isotactic polypropylene, the process for producing a modified polypropylene which is characterized in that a gas phase polymerization of propylene is substantially carried out in the presence of the catalyst obtained by combining a titanium trichloride composition with an average particle size of 10˜100μ and an organic aluminum to form the propylene polymer segment with a specific surface area more than 0.015 m 2 /g at an yield of more than 3,000 g per 1 g of the titanium trichloride composition in the first step, and then a gas phase polymerization of a mixture of polypropylene and ethylene is successively carried out in the second step to form the copolymer segment with a copolymerization ratio of propylene:ethylene being 5˜80 weight %:95˜20 weight %, wherein the polymerized amount of the second step is 10˜40% of total polymerized amount and wherein normal hexane extraction ratio (75° C., 1 hour) of the ethylene-propylene block copolymer powders obtained is 1˜ 10 weight %.
Claim 3
Dependent Claim
56 words
The process according to claim 1, wherein the titanium trichloride composition is one obtained by reacting titanium tetrachloride, an organic aluminum compound and an organic ether and treating them with titanium tetrachloride, an ether compound or a reaction product of titanium tetrachloride and an ether compound, and wherein the organic aluminum compound is diethyl aluminum chloride.
Claim 4
Dependent Claim
21 words
The process according to claim 2, wherein less than 0.15 (molar ratio) of triethyl aluminum is used per diethyl aluminum chloride.
Claim 5
Dependent Claim
44 words
The process according to claim 1, wherein the titanium trichloride composition is prepared from the reaction product obtained by reacting magnesium hydroxide with aluminum chloride, as well as ethyl benzoate, silicon tetrachloride and titanium tetrachloride, and wherein the organic aluminum compound is triethyl aluminum.
Claim 6
Dependent Claim
22 words
The process according to claim 4, wherein from 0.01 to 0.25 (molar ratio) of methyl para toluate is used per triethyl aluminum.