Lead gallate glasses
Assignee: Corning Glass Works
•
Filing: 1983-03-21
•
Granted: 1984-11-20
•
Expires: 2003-03-21
Abstract
Abstract This invention is directed to the preparation of glasses in the PbO--Ga 2 O 3 field exhibiting good infrared transmitting characteristics out to wavelengths of 8 microns. The binary glasses consist essentially, by weight, of about 15-28% Ga 2 O 3 and 72-85% PbO. However, the preferred glasses contain up to 85% Bi 2 O 3 and consist essentially as included within the area generally encompassed by the curve in FIG. 2.
Inventors
- 👤 William H. Dumbaugh, Jr.
- 👤 Brian P. Tyndell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 10:34
CPC Classifications
C; C03; C03C; C03C4/00; C03C4/10; C03C3/00; C03C3/12; C03C3/122; Y; Y10; Y10S; Y10S501/00; Y10S501/90; Y10S501/901; Y10S501/904
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
41 words
A stable binary glass exhibiting refractive indices greater than 2.4 and infrared transmitting characteristics out to wavelengths of 8 microns consisting, expressed in terms of weight percent on the oxide basis, of about 15-28% Ga 2 O 3 and 72-85% PbO.
Claim 2
Dependent Claim
41 words
A stable binary glass exhibiting refractive indices greater than 2.4 and infrared transmitting characteristics out to wavelengths of 8 microns consisting, expressed in terms of weight percent on the oxide basis, of about 15-28% Ga 2 O 3 and 72-85% PbO.
Claim 3
Dependent Claim
59 words
A stable ternary glass exhibiting infrared transmitting characteristics out to 8 microns consisting essentially, expressed in terms of weight percent on the oxide basis, as included within the area generally encompassed by the curve in FIG. 2 of about 10-85% PbO, 5-30% Ga 2 O 3 , and including Bi 2 O 3 in amounts not more than 85%.
Claim 4
Dependent Claim
59 words
A stable ternary glass exhibiting infrared transmitting characteristics out to 8 microns consisting essentially, expressed in terms of weight percent on the oxide basis, as included within the area generally encompassed by the curve in FIG. 2 of about 10-85% PbO, 5-30% Ga 2 O 3 , and including Bi 2 O 3 in amounts not more than 85%.
Claim 5
Dependent Claim
84 words
An infrared transmitting glass according to claim 2 also containing up to 30% total of the following components in the indicated proportions selected from the group of: ______________________________________
Cs.sub.2 O
0-20 Rb.sub.2 O
0-5
HgO 0-30 HfO.sub.2
0-5
Tl.sub.2 O.sub.3
0-20 Al.sub.2 O.sub.3
0-3
Sb.sub.2 O.sub.3
0-10 ZnO 0-5
TeO.sub.2
0-10 K.sub.2 O
0-2
Cr.sub.2 O.sub.3
0-5 In.sub.2 O.sub.3
0-10
MnO.sub.2
0-5 SiO.sub.2
0-2
CuO 0-2 ZrO.sub.2
0-5
CdO 0-12 Nb.sub.2 O.sub.5
0-5
GeO.sub.2
0-5 Ta.sub.2 O.sub.5
0-5
Na.sub.2 O
0-2 Halogen 0-5
______________________________________
Claim 6
Dependent Claim
13 words
An infrared transmitting glass according to claim 3 wherein said halogen is chloride.
References Cited (Backward Citations)
US2853393A
Cited
US3188216A
Cited
US3507646A
Cited
US3531271A
Cited
US3607388A
Cited
US3723141A
Cited
US3837868A
Cited
US3947089A
Cited
DD158896A1
Cited
US4407061A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-20 | 1988-05-21 | 1988-11-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-20 | 1992-05-21 | 1992-11-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-20 | 1996-05-21 | 1996-11-20 | $7700.00 | Window Closed / Lapsed |