Abstract
Abstract A process of treating an anodic oxide film wherein a base material of a valve metal is anodized to form the anodic oxide film thereon, which is then impregnated with a polymerizable organic metal compound and thereafter subjected to polymerization of the compound, whereby the micropores of the anodic oxide film are filled and sealed with the polymerized organometallic compound. According to this process, there is provided a base material having an anodic oxide film impregnated with polymerized organometallic compound which is excellent in heat resistance, heat radiance, and electrical insulation, and hence the base material is useful for the printed wiring board, electrically-insulative heat sink, heat-resistant insulated wire and the like.
Inventors
- 👤 Seizo Murayama
- 👤 Kazuo Isawa
- 👤 Masatsugu Maejima
- 👤 Takayoshi Usuki
- 👤 Kohichi Saruwatari
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 06:08
CPC Classifications
H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/05; H05K1/053; C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/18; C25D11/24; C25D11/246; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/46; H05K2203/00; H05K2203/03; H05K2203/0315; H05K2203/11; H05K2203/1147
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
218 words
A process of treating an anodic oxide film, comprising the steps of: (a) anodizing an aluminum or aluminum alloy base material in an electrolytic solution containing ammonium ions present in a concentration from about 5 to about 80 g/l, at a temperature of about 5° to about 40° C. with a current density in the range of about 0.5 to about 10 A/dm 2 , thereby forming an anodic oxide film thereon, the anodic oxide film having micropores therein; (b) dissolving a polymerizable organometallic compound in a solvent selected from the group consisting of an organic solvent, water and mixtures thereof, the organometallic compound being represented by the formula: x.sub.n MR.sub.m wherein: X is an organic functional group selected from vinyl, amino, mercapto, epoxy, methyl, and phenyl groups; M is a metallic atom selected from Si, Ti, Zr, Al, B, P, Ge, and Sn; R is a hydrolyzable organic group selected from alkoxy and acetoxy groups; and n+m=3, 4, 5 or 6; (c) after the step (b), impregnating the anodic oxide film by electrophoresis or electropermeation with the organometallic compound dissolved in the solvent material of step (b); and (d) polymerizing and hardening the organometallic compound impregnated into the anodic oxide film, thereby filling and sealing the micropores of the anodic oxide film with a polymerized organometallic compound.
Claim 2
Dependent Claim
218 words
A process of treating an anodic oxide film, comprising the steps of: (a) anodizing an aluminum or aluminum alloy base material in an electrolytic solution containing ammonium ions present in a concentration from about 5 to about 80 g/l, at a temperature of about 5° to about 40° C. with a current density in the range of about 0.5 to about 10 A/dm 2 , thereby forming an anodic oxide film thereon, the anodic oxide film having micropores therein; (b) dissolving a polymerizable organometallic compound in a solvent selected from the group consisting of an organic solvent, water and mixtures thereof, the organometallic compound being represented by the formula: x.sub.n MR.sub.m wherein: X is an organic functional group selected from vinyl, amino, mercapto, epoxy, methyl, and phenyl groups; M is a metallic atom selected from Si, Ti, Zr, Al, B, P, Ge, and Sn; R is a hydrolyzable organic group selected from alkoxy and acetoxy groups; and n+m=3, 4, 5 or 6; (c) after the step (b), impregnating the anodic oxide film by electrophoresis or electropermeation with the organometallic compound dissolved in the solvent material of step (b); and (d) polymerizing and hardening the organometallic compound impregnated into the anodic oxide film, thereby filling and sealing the micropores of the anodic oxide film with a polymerized organometallic compound.
Claim 3
Dependent Claim
29 words
The process as claimed in claim 1 in which the current density of anodization step (a) is in the range of about 1.5 to about 5 A/dm 2 .
Claim 4
Dependent Claim
25 words
The process as claimed in claim 1 in which the base material is an aluminum-silicon alloy containing not more than about 20% by weight silicon.
Claim 5
Dependent Claim
218 words
A process of treating an anodic oxide film, comprising the steps of: (a) anodizing an aluminum or aluminum alloy base material in an electrolytic solution containing sodium ions present in a concentration from about 1 to about 30 g/l, at a temperature of about 5° to about 40° C. with a current density in the range of about 0.5 to about 10 A/dm 2 , thereby forming an anodic oxide film thereon, the anodic oxide film having micropores therein; (b) dissolving a polymerizable organometallic compound in a solvent selected from the group consisting of an organic solvent, water and mixtures thereof, the organometallic compound being represented by the formula: x.sub.n MR.sub.m wherein: X is an organic functional group selected from vinyl, amino, mercapto, epoxy, methyl, and phenyl groups; M is a metallic atom selected from Si, Ti, Zr, Al, B, P, Ge, and Sn; R is a hydrolyzable organic group selected from alkoxy and acetoxy groups; and n+m=3, 4, 5 or 6; (c) after the step (b), impregnating the anodic oxide film by electrophoresis or electropermeation with the organometallic compound dissolved in the solvent material of step (b); and (d) polymerizing and hardening the organometallic compound impregnated into the anodic oxide film, thereby filling and sealing the micropores of the anodic oxide film with a polymerized organometallic compound.
Claim 6
Dependent Claim
218 words
A process of treating an anodic oxide film, comprising the steps of: (a) anodizing an aluminum or aluminum alloy base material in an electrolytic solution containing sodium ions present in a concentration from about 1 to about 30 g/l, at a temperature of about 5° to about 40° C. with a current density in the range of about 0.5 to about 10 A/dm 2 , thereby forming an anodic oxide film thereon, the anodic oxide film having micropores therein; (b) dissolving a polymerizable organometallic compound in a solvent selected from the group consisting of an organic solvent, water and mixtures thereof, the organometallic compound being represented by the formula: x.sub.n MR.sub.m wherein: X is an organic functional group selected from vinyl, amino, mercapto, epoxy, methyl, and phenyl groups; M is a metallic atom selected from Si, Ti, Zr, Al, B, P, Ge, and Sn; R is a hydrolyzable organic group selected from alkoxy and acetoxy groups; and n+m=3, 4, 5 or 6; (c) after the step (b), impregnating the anodic oxide film by electrophoresis or electropermeation with the organometallic compound dissolved in the solvent material of step (b); and (d) polymerizing and hardening the organometallic compound impregnated into the anodic oxide film, thereby filling and sealing the micropores of the anodic oxide film with a polymerized organometallic compound.
Claim 7
Dependent Claim
29 words
The process as claimed in claim 4 in which the current density of anodization step (a) is in the range of about 1.5 to about 5 A/dm 2 .
Claim 8
Dependent Claim
25 words
The process as claimed in claim 4 in which the base material is an aluminum-silicon alloy containing not more than about 20% by weight silicon.
Claim 9
Dependent Claim
212 words
A process of treating an anodic oxide film, comprising the steps of: (a) anodizing an aluminum or aluminum alloy base material in an electrolytic solution containing from about 4 to about 25% by weight of oxalic acid at a temperature of about 20° to about 50° C. and a current density of about 0.5 to about 10 A/dm 2 to form an anodic oxide film thereon, the anodic oxide film having micropores therein; (b) dissolving a polymerizable organometallic compound in a solvent selected from the group consisting of an organic solvent, water and mixtures thereof, the organometallic compound being represented by the formula: x.sub.n MR.sub.m wherein: X is an organic functional group selected from vinyl, amino, mercapto, epoxy, methyl, and phenyl groups; M is a metallic atom selected from Si, Ti, Zr, Al, B, P, Ge, and Sn; R is a hydrolyzable organic group selected from alkoxy and acetoxy groups; and n+m=3, 4, 5 or 6; (c) after the step (b), impregnating the anodic oxide film by electrophoresis or electropermeation with the organometallic compound dissolved in the solvent material of step (b); and (d) polymerizing and hardening the organometallic compound impregnated into the anodic oxide film, thereby filling and sealing the micropores of the anodic oxide film with a polymerized organometallic compound.
Claim 10
Dependent Claim
212 words
A process of treating an anodic oxide film, comprising the steps of: (a) anodizing an aluminum or aluminum alloy base material in an electrolytic solution containing from about 4 to about 25% by weight of oxalic acid at a temperature of about 20° to about 50° C. and a current density of about 0.5 to about 10 A/dm 2 to form an anodic oxide film thereon, the anodic oxide film having micropores therein; (b) dissolving a polymerizable organometallic compound in a solvent selected from the group consisting of an organic solvent, water and mixtures thereof, the organometallic compound being represented by the formula: x.sub.n MR.sub.m wherein: X is an organic functional group selected from vinyl, amino, mercapto, epoxy, methyl, and phenyl groups; M is a metallic atom selected from Si, Ti, Zr, Al, B, P, Ge, and Sn; R is a hydrolyzable organic group selected from alkoxy and acetoxy groups; and n+m=3, 4, 5 or 6; (c) after the step (b), impregnating the anodic oxide film by electrophoresis or electropermeation with the organometallic compound dissolved in the solvent material of step (b); and (d) polymerizing and hardening the organometallic compound impregnated into the anodic oxide film, thereby filling and sealing the micropores of the anodic oxide film with a polymerized organometallic compound.
Claim 11
Dependent Claim
29 words
The process as claimed in claim 7 in which the current density of anodization step (a) is in the range of about 1.5 to about 5 A/dm 2 .
Claim 12
Dependent Claim
25 words
The process as claimed in claim 7 in which the base material is an aluminum-silicon alloy containing not more than about 20% by weight silicon.
References Cited (Backward Citations)
US3202591A
Cited
US3340161A
Cited
US3622473A
Cited
US3711313A
Cited
US4130466A
Cited
US4180442A
Cited
US4318939A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-20 | 1988-05-21 | 1988-11-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-20 | 1992-05-21 | 1992-11-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-20 | 1996-05-21 | 1996-11-20 | $7700.00 | Window Closed / Lapsed |