Electrodeposition of coatings on metals to enhance adhesive bonding
Assignee: McDonnell Douglas Corp
•
Filing: 1978-06-14
•
Granted: 1979-12-25
•
Expires: 1998-06-14
Abstract
Abstract The invention is directed to the electrodeposition of a coating of an organic compound or polymer on a metal such as aluminum, and the formation of a chemical bond between the metal and the coating. In the method for electrolytically depositing such coating on the metal substrate, e.g. aluminum, the substrate is employed as the anode in a non-aqueous electrolyte containing a coating compound, preferably a carboxyl-substituted aminosilane such as gamma -aminopropyltriethoxysilane, which has been reacted with any of various anhydrides such as phthalic, maleic, or succinic anhydride, and electrodepositing a coating on the metal substrate, the organic coating formed being chemically bonded to the substrate, thereby enhancing adhesive bonding to the metal substrate or enhancing spot weldability of such substrate, such coating being strongly bonded to the substrate and being corrosion resistant.
Inventors
- 👤 Norman R. Byrd
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 10:57
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/44; C09D5/4484
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
97 words
A process for enhancing adhesive bonding of a metal substrate and permitting spot welding thereof, which comprises passing an electric current through a non-aqueous electrolyte in which a metal substrate is the anode, the metal of said substrate being active and capable of forming an organometallic compound, said electrolyte containing an organic compound selected from the classes consisting of (a) carboxyl substituted aminosilanes, (b) butylamine reaction products with phthalic anhydride, decylamine reaction products with phthalic anhydride, and carboxyl terminated butadiene-acrylonitrile copolymer, and (c) phenyl phosphonic acid, and dimethyl phosphite, as their triethylamine salts, and sulfonic acid compounds.
Claim 2
Dependent Claim
97 words
A process for enhancing adhesive bonding of a metal substrate and permitting spot welding thereof, which comprises passing an electric current through a non-aqueous electrolyte in which a metal substrate is the anode, the metal of said substrate being active and capable of forming an organometallic compound, said electrolyte containing an organic compound selected from the classes consisting of (a) carboxyl substituted aminosilanes, (b) butylamine reaction products with phthalic anhydride, decylamine reaction products with phthalic anhydride, and carboxyl terminated butadiene-acrylonitrile copolymer, and (c) phenyl phosphonic acid, and dimethyl phosphite, as their triethylamine salts, and sulfonic acid compounds.
Claim 3
Dependent Claim
16 words
The process as defined in claim 1, wherein said organic compound is a carboxyl substituted aminosilane.
Claim 4
Dependent Claim
22 words
The process as defined in claim 2, wherein said carboxyl substituted aminosilane is the reaction product of an anhydride and an aminosilane.
Claim 5
Dependent Claim
39 words
The process as defined in claim 3, wherein said anhydride is selected from the group consisting of phthalic, maleic, succinic, nonenylsuccinic and chlorendic anhydrides, benzophenone tetracarboxylic dianhydride, styrene-maleic anhydride copolymer and methyl vinyl ether-maleic anhydride copolymer, and mixtures thereof.
Claim 6
Dependent Claim
14 words
The process as defined in claim 4, wherein said aminosilane is an aminopropyl trialkoxysilane.
Claim 7
Dependent Claim
21 words
The process as defined in claim 4, wherein said aminosilane is selected from the group consisting of gamma-aminopropyltriethoxysilane, N-beta-(aminoethyl)-gamma-aminopropyltrimethoxysilane and gamma-mercaptopropyltrimethoxysilane.
Claim 8
Dependent Claim
36 words
The process as defined in claim 1, wherein said organic compound is selected from the group consisting essentially of butylamine reaction products with phthalic anhydride, decylamine reaction products with phthalic anhydride, and carboxyl terminated butadiene-acrylonitrile copolymer.
Claim 9
Dependent Claim
32 words
The process as defined in claim 1, wherein said organic compound is selected from the group consisting of phenyl phosphonic acid, and dimethyl phosphite, as their triethylamine salts, and sulfonic acid compounds.
Claim 10
Dependent Claim
25 words
The process as defined in claim 2, wherein said substrate is selected from the group consisting of aluminum, titanium, stainless steel, nickel, silver and copper.
Claim 11
Dependent Claim
46 words
The process as defined in claim 5, wherein said substrate is selected from the group consisting of aluminum, titanium, stainless steel, nickel, silver and copper, and said organic solvent is selected from the group consisting of dimethylformamide, N-methyl pyrrolidone, tetrahydrofuran, ethylene glycol, chloroform, and mixtures thereof.
Claim 12
Dependent Claim
41 words
The process as defined in claim 10, wherein said current is direct current, said voltage ranging from about 1.7 to about 100 volts, and wherein said electrodeposition is carried out for a period up to not more than about 5 minutes.
Claim 13
Dependent Claim
12 words
The process as defined in claim 11, wherein said substrate is aluminum.
Claim 14
Dependent Claim
19 words
The process as defined in claim 9, including applying an organic adhesive to said electrodeposited coating, on said substrate.
Claim 15
Dependent Claim
34 words
A metal substrate containing an organic electrodeposited coating which is chemically bonded to said substrate to enhance adhesive bonding and also permitting spot welding of said substrate, produced by the process of claim 2.
Claim 16
Dependent Claim
34 words
A metal substrate containing an organic electrodeposited coating which is chemically bonded to said substrate to enhance adhesive bonding and also permitting spot welding of said substrate, produced by the process of claim 3.
Claim 17
Dependent Claim
34 words
A metal substrate containing an organic electrodeposited coating which is chemically bonded to said substrate to enhance adhesive bonding and also permitting spot welding of said substrate, produced by the process of claim 6.
Claim 18
Dependent Claim
34 words
A metal substrate containing an organic electrodeposited coating which is chemically bonded to said substrate to enhance adhesive bonding and also permitting spot welding of said substrate, produced by the process of claim 10.
Claim 19
Dependent Claim
34 words
A metal substrate containing an organic electrodeposited coating which is chemically bonded to said substrate to enhance adhesive bonding and also permitting spot welding of said substrate, produced by the process of claim 11.
Claim 20
Dependent Claim
34 words
A metal substrate containing an organic electrodeposited coating which is chemically bonded to said substrate to enhance adhesive bonding and also permitting spot welding of said substrate, produced by the process of claim 12.
Claim 21
Dependent Claim
25 words
The process as defined in claim 1, wherein said substrate is selected from the group consisting of aluminum, titanium, stainless steel, nickel, silver and copper.
Claim 22
Dependent Claim
28 words
The process as defined in claim 20 wherein said organic solvent is selected from the group consisting of dimethylformamide, N-methyl pyrrolidone, tetrahydrofuran, ethylene glycol, chloroform, and mixtures thereof.
Claim 23
Dependent Claim
34 words
A metal substrate containing an organic electrodeposited coating which is chemically bonded to said substrate to enhance adhesive bonding and also permitting spot welding of said substrate, produced by the process of claim 1.
Claim 24
Dependent Claim
100 words
A process for enhancing adhesive bonding of a metal substrate and permitting spot welding thereof, which comprises passing an electric current through a non-aqueous electrolyte in which a metal substrate is the anode, the metal of said substrate being active and capable of forming an organometallic compound, said electrolyte containing an organic compound having a labile hydrogen, and capable of generating an anion during electrolysis, and an inert organic solvent for said compound, and electrodepositing a coating of said compound on said metal substrate wherein said anion is reacted with and is chemically bonded to the metal of said substrate.
Claim 25
Dependent Claim
100 words
A process for enhancing adhesive bonding of a metal substrate and permitting spot welding thereof, which comprises passing an electric current through a non-aqueous electrolyte in which a metal substrate is the anode, the metal of said substrate being active and capable of forming an organometallic compound, said electrolyte containing an organic compound having a labile hydrogen, and capable of generating an anion during electrolysis, and an inert organic solvent for said compound, and electrodepositing a coating of said compound on said metal substrate wherein said anion is reacted with and is chemically bonded to the metal of said substrate.
Claim 26
Dependent Claim
25 words
The process as defined in claim 23, wherein said substrate is selected from the group consisting of aluminum, titanium, stainless steel, nickel, silver and copper.
Claim 27
Dependent Claim
28 words
The process as defined in claim 23, wherein said organic solvent is selected from the group consisting of dimethylformamide, N-methyl pyrrolidone, tetrahydrofuran, ethylene glycol, chloroform, and mixtures thereof.
Claim 28
Dependent Claim
16 words
The process as defined in claim 23, wherein said current is direct current or alternating current.
Claim 29
Dependent Claim
23 words
The process as defined in claim 23, wherein said electrodeposition is carried out at voltage ranging from about 1 to about 300 volts.
Claim 30
Dependent Claim
24 words
The process as defined in claim 27, wherein said electrodeposition is carried out for a period up to not more than about 5 minutes.
Claim 31
Dependent Claim
23 words
The process as defined in claim 24, wherein said electrodeposition is carried out at voltage ranging from about 1 to about 300 volts.
Claim 32
Dependent Claim
19 words
The process as defined in claim 23, including applying an organic adhesive to said electrodeposited coating, on said substrate.
Claim 33
Dependent Claim
14 words
The process as defined in claim 30, wherein said adhesive is an epoxy adhesive.
Claim 34
Dependent Claim
34 words
A metal substrate containing an organic electrodeposited coating which is chemically bonded to said substrate to enhance adhesive bonding and also permitting spot welding of said substrate, produced by the process of claim 23.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-24 | 1983-06-25 | 1983-12-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-24 | 1987-06-25 | 1987-12-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-24 | 1991-06-25 | 1991-12-25 | $7700.00 | Window Closed / Lapsed |