US4482382A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Pouring repair material for mortar or the like wall
Assignee: JFE Engineering Corp
•
Filing: 1983-05-16
•
Granted: 1984-11-13
•
Expires: 2003-05-16
Abstract
Abstract The pouring repair material for mortar or the like wall characterized in that it consists essentially of a synthetic resin emulsion, cement and slags with particle size less than 0.5 mm, and in that the weight ratios P/C, C/S and W/C are adjusted to 0.1 to 3, 1.5 to 2.5 and 0.35 to 0.40, wherein P designates solid contents of the synthetic resin, C cement, S slags and W water.
Inventors
- 👤 Hisayasu Kanayama
- 👤 Yoshiaki Sasaki
- 👤 Naoki Furuno
- 👤 Yoshitaka Sasaoka
- 👤 Osamu Tokita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:33
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02; C04B2111/00; C04B2111/72; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/91
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
82 words
A fluid pouring repair material for mortar or the like wall which consists of a synthetic resin emulsion, hydraulic cement and aggregate slags with particle size less than 0.5 mm, and water as required to satisfy the following weight ratios wherein the weight ratios P/C, C/S and W/C are within the range of 0.1 to 0.3, 1.5 to 2.5 and 0.35 to 0.40, respectively, wherein P designates the solid content of the synthetic resin emulsion, C cement, S slags and W water.
Claim 2
Dependent Claim
82 words
A fluid pouring repair material for mortar or the like wall which consists of a synthetic resin emulsion, hydraulic cement and aggregate slags with particle size less than 0.5 mm, and water as required to satisfy the following weight ratios wherein the weight ratios P/C, C/S and W/C are within the range of 0.1 to 0.3, 1.5 to 2.5 and 0.35 to 0.40, respectively, wherein P designates the solid content of the synthetic resin emulsion, C cement, S slags and W water.
Claim 3
Dependent Claim
24 words
A pouring repair material for mortar or the like wall as claimed in claim 1 wherein the P/C ratio is from 0.1 to 0.2.
Claim 4
Dependent Claim
24 words
A pouring repair material for mortar or the like wall as claimed in claim 1 wherein the W/C ratio is from 0.360 to 0.390.
Claim 5
Dependent Claim
41 words
A fluid pouring material for mortar or the like wall according to claim 1 said synthetic resin emulsion contains an added filler in an amount within the range of 1.0 to 3.0 wt. percent of the solid contents of synthetic resin.
Claim 6
Dependent Claim
41 words
A composition according to claim 4 wherein said filler is selected from the group consisting of silica having a particle size range of from about 10 to about 40 μm and asbestos having a particle size of about 0.025 μmφ×5 μm.
Claim 7
Dependent Claim
34 words
A composition according to claim 1 wherein said synthetic resin is selected from the group consisting of an ethylene-vinyl acetate copolymer, a styrene-butadiene copolymer, and a styrene-butadiene copolymer partially modified with methacrylic acid ester.
Claim 8
Dependent Claim
13 words
A composition according to claim 1 wherein said hydraulic cement is Portland cement.
Claim 9
Dependent Claim
15 words
A composition according to claim 1 wherein said hydraulic cement is blast furnace slag cement.
Claim 10
Independent Claim
134 words
A method for repairing a blister in a composite wall comprising a concrete base wall and a decorative mortar wall coating wherein said blister is formed by separation of the decorative wall coating from the base wall leaving a space therebetween which comprises injecting through an opening in said decorative wall into the space formed by the blister a fluid composition consisting a hydraulic cement, water, synthetic resin emulsion, and aggregate slag having a particle size less than about 0.5 mm in the ratios P/C, C/S and W/C within the range of 0.1 to 0.3, 1.5 to 2.5 and 0.35 to 0.40, respectively, wherein P designates the solid content of the synthetic resin emulsion, C cement, S slags, and W water, thereby forming an adhesive bond between said base wall and said wall coating.
Claim 11
Independent Claim
134 words
A method for repairing a blister in a composite wall comprising a concrete base wall and a decorative mortar wall coating wherein said blister is formed by separation of the decorative wall coating from the base wall leaving a space therebetween which comprises injecting through an opening in said decorative wall into the space formed by the blister a fluid composition consisting a hydraulic cement, water, synthetic resin emulsion, and aggregate slag having a particle size less than about 0.5 mm in the ratios P/C, C/S and W/C within the range of 0.1 to 0.3, 1.5 to 2.5 and 0.35 to 0.40, respectively, wherein P designates the solid content of the synthetic resin emulsion, C cement, S slags, and W water, thereby forming an adhesive bond between said base wall and said wall coating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-13 | 1988-05-14 | 1988-11-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-13 | 1992-05-14 | 1992-11-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-13 | 1996-05-14 | 1996-11-13 | $7700.00 | Window Closed / Lapsed |