Patent US4481470A successfully refreshed from Google Patents.
US4481470A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for determining the hardness of strain hardening articles of tungsten-nickel-iron alloy
Assignee: ENERGY United States, Department of
•
Filing: 1981-07-29
•
Granted: 1984-11-06
•
Expires: 2001-07-29
Abstract
Abstract The present invention is directed to a rapid nondestructive method for determining the extent of strain hardening in an article of tungsten-nickel-iron alloy. The method comprises saturating the article with a magnetic field from a permanent magnet, measuring the magnetic flux emanating from the article, comparing the measurements of the magnetic flux emanating from the article with measured magnetic fluxes from similarly shaped standards of the alloy with known amounts of strain hardening to determine the hardness.
Inventors
- 👤 Steven A. Wallace
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:02
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/72
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
159 words
A method for measuring the extent of cross-sectional strain hardening along the length of an elongated cold-worked article formed of tungsten-nickel-iron alloy, consisting of the steps of passing the article through a magnetic field emanating from a permanent magnet to saturate a cross-sectional portion of the article with magnetic flux, measuring the magnetic flux emanating from the article to determine the extent of the distortion in the magnetic field due to the presence of the cross-sectional portion of the article therein with the extent of distortion being indicative of and increasing with the degree of strain hardening through the cross-sectional portion of the article within the magnetic field, and comparing the measurements of magnetic flux taken along the length of the article with measurements of magnetic flux taken from a standard of the alloy of known cross-sectional hardness and of a similar configuration to provide measurements of cross-sectional hardness through cross sections of the article along the length thereof.
Claim 2
Independent Claim
159 words
A method for measuring the extent of cross-sectional strain hardening along the length of an elongated cold-worked article formed of tungsten-nickel-iron alloy, consisting of the steps of passing the article through a magnetic field emanating from a permanent magnet to saturate a cross-sectional portion of the article with magnetic flux, measuring the magnetic flux emanating from the article to determine the extent of the distortion in the magnetic field due to the presence of the cross-sectional portion of the article therein with the extent of distortion being indicative of and increasing with the degree of strain hardening through the cross-sectional portion of the article within the magnetic field, and comparing the measurements of magnetic flux taken along the length of the article with measurements of magnetic flux taken from a standard of the alloy of known cross-sectional hardness and of a similar configuration to provide measurements of cross-sectional hardness through cross sections of the article along the length thereof.
Claim 3
Dependent Claim
30 words
The method claimed in claim 1, wherein the article comprises 85 to 95 wt. % tungsten and the remainder nickel and iron in a nickel-iron ratio of 5:5 to 8:2.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-06 | 1988-05-07 | 1988-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-06 | 1992-05-07 | 1992-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-06 | 1996-05-07 | 1996-11-06 | $7700.00 | Window Closed / Lapsed |