Rubber compositions and method
Assignee: Fredrikson & Byron PA
•
Filing: 1981-08-10
•
Granted: 1984-11-06
•
Expires: 2001-08-10
Abstract
Abstract A rubber molding composition comprising cured rubber scrap (as from automobile tires), a liquid, sulfur-curable polymeric binder, and a curing agent for the polymeric binder. The composition employs from about one to about five parts by weight of the polymeric binder per 100 parts by weight of the scrap rubber. The thus treated rubber scrap may be used in large proportions as a filler or extender for uncured rubbers.
Inventors
- 👤 Fred J. Stark, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 15:59
CPC Classifications
C; C08; C08L; C08L19/00; C08L19/003; C08L21/00; Y; Y10; Y10S; Y10S264/00; Y10S264/911; Y10S264/912
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
111 words
A substantially dry, particulate molding material comprising a uniform mixture of (a) 100 parts by weight of cured rubber particles; (b) from about 1 to about 5 parts by weight of liquid, sulfur-curable polymeric binder having ethylenic unsaturation and being soluble in hexane, benzene or a combination thereof, the binder having a viscosity at 280° F. of not greater than about one million centipoises and further characterized as being capable of softening surfaces of the cured rubber particles when applied thereto and the particles are heated; and (c) a curing agent for the polymeric binder in a quantity ranging from about 50% to about 500% by weight of the polymeric binder.
Claim 2
Dependent Claim
111 words
A substantially dry, particulate molding material comprising a uniform mixture of (a) 100 parts by weight of cured rubber particles; (b) from about 1 to about 5 parts by weight of liquid, sulfur-curable polymeric binder having ethylenic unsaturation and being soluble in hexane, benzene or a combination thereof, the binder having a viscosity at 280° F. of not greater than about one million centipoises and further characterized as being capable of softening surfaces of the cured rubber particles when applied thereto and the particles are heated; and (c) a curing agent for the polymeric binder in a quantity ranging from about 50% to about 500% by weight of the polymeric binder.
Claim 3
Dependent Claim
21 words
The composition of claim 1 in which the particle size of the cured rubber particles is finer than about 20 mesh.
Claim 4
Dependent Claim
40 words
The composition of claim 1 in which the curing agent comprises a sulfur donor for vulcanizing the polymeric binder in an amount ranging from about 0.5 to about 5 parts by weight per part by weight of the polymeric binder.
Claim 5
Dependent Claim
29 words
The composition of claim 1 in which the curing agent comprises elemental sulfur in an amount of from about 50% to about 150% by weight of the polymeric binder.
Claim 6
Dependent Claim
13 words
The composition of claim 3 in which the curing agent is a polysulfide.
Claim 7
Dependent Claim
28 words
The composition of claim 1 in which the polymeric binder comprises a copolymer of butadiene and ethylenically unsaturated monomer selected from the group consisting of styrene and acrylonitrile.
Claim 8
Dependent Claim
14 words
The composition of claim 1 wherein the polymeric binder comprises a homopolymer of butadiene.
Claim 9
Independent Claim
149 words
A method of producing a rubber-like article comprising the steps of (a) uniformly and thoroughly mixing together (i) 100 parts by weight of particulate, cured rubber; (ii) from about 1 to about 5 parts by weight of a liquid, sulfur-curable polymeric binder having ethylenic unsaturation and being soluble in hexane, benzene, or a combination thereof, the binder having a viscosity at 280° F. of not greater than about one million centipoises and further characterized of being capable as softening sufaces of the cured rubber particles when applied thereto and the particles are heated; and (iii) a curing agent for the polymeric binder in a quantity ranging from about 50% to about 500% by weight of the polymeric binder; (b) charging the composition as a substantially dry, free-flowing, particulate mass, to a compression mold; and (c) molding the composition under heat and pressure to form a solid, strong molded article.
Claim 10
Independent Claim
149 words
A method of producing a rubber-like article comprising the steps of (a) uniformly and thoroughly mixing together (i) 100 parts by weight of particulate, cured rubber; (ii) from about 1 to about 5 parts by weight of a liquid, sulfur-curable polymeric binder having ethylenic unsaturation and being soluble in hexane, benzene, or a combination thereof, the binder having a viscosity at 280° F. of not greater than about one million centipoises and further characterized of being capable as softening sufaces of the cured rubber particles when applied thereto and the particles are heated; and (iii) a curing agent for the polymeric binder in a quantity ranging from about 50% to about 500% by weight of the polymeric binder; (b) charging the composition as a substantially dry, free-flowing, particulate mass, to a compression mold; and (c) molding the composition under heat and pressure to form a solid, strong molded article.
Claim 11
Independent Claim
173 words
A method of producing a rubber-like article comprising the steps of (a) uniformly and thoroughly blending together (i) 100 parts by weight of particulate, cured rubber; (ii) from about 1 to about 5 parts by weight of a liquid, sulfur-curable polymeric binder having ethylenic unsaturation and being soluble in hexane, benzene or a combination thereof, the binder having a viscosity at 280° F. of not greater than about one million centipoises and further characterized as being capable of softening surfaces of the cured rubber particles when applied thereto and the particles are heated; and (iii) a curing agent for the polymeric binder in an amount not less than about 50% by weight of the polymeric binder, thereby providing a generally dry, particulate composition; (b) Combining the particulate composition with uncured rubber, the resulting composition containing from about 25% to about 75% of the uncured rubber and from about 75% to about 25% of the particulate composition; and (c) molding the resulting composition under heat and pressure to form a solid, strong molded article.
Claim 12
Independent Claim
173 words
A method of producing a rubber-like article comprising the steps of (a) uniformly and thoroughly blending together (i) 100 parts by weight of particulate, cured rubber; (ii) from about 1 to about 5 parts by weight of a liquid, sulfur-curable polymeric binder having ethylenic unsaturation and being soluble in hexane, benzene or a combination thereof, the binder having a viscosity at 280° F. of not greater than about one million centipoises and further characterized as being capable of softening surfaces of the cured rubber particles when applied thereto and the particles are heated; and (iii) a curing agent for the polymeric binder in an amount not less than about 50% by weight of the polymeric binder, thereby providing a generally dry, particulate composition; (b) Combining the particulate composition with uncured rubber, the resulting composition containing from about 25% to about 75% of the uncured rubber and from about 75% to about 25% of the particulate composition; and (c) molding the resulting composition under heat and pressure to form a solid, strong molded article.
Claim 13
Dependent Claim
26 words
The method of claim 9 in which the polymeric binder and curing agent are first mixed together and are then blended with the particulate cured rubber.
Claim 14
Dependent Claim
19 words
The method of claim 9 in which the molding pressure is sufficient to substantially eliminate air from the composition.
Claim 15
Dependent Claim
19 words
The method of claim 9 in which the molding pressure is insufficient to substantially eliminate air from the composition.
Claim 16
Dependent Claim
10 words
The molded product resulting from the method of claim 9.
Claim 17
Dependent Claim
17 words
A molding composition comprising a uniform blend of uncured rubber with the molding material of claim 1.
Claim 18
Dependent Claim
27 words
The molding composition of claim 14 in which the concentration of the molding material is in the range of from about 25% to about 90% by weight.
Claim 19
Dependent Claim
134 words
A molding composition comprising a uniform blend of from about 75% to about 25% by weight of an uncured rubber, and about 25% to about 75% by weight of a filler material comprising (a) 100 parts by weight of cured rubber particles; (b) from about 1 to about 5 parts by weight of a liquid, sulfur-curable polymeric binder having ethylenic unsaturation and being soluble in hexane, benzene, or a combination thereof, the binder having a viscosity at 280° F. of not greater than about one million centipoises and further characterized as being capable of softening surfaces of the cured rubber particles when applied thereto and the particles are heated; and (c) A curing agent for the polymeric binder in a quantity ranging from about 50% to about 500% by weight of the polymeric binder.
Claim 20
Dependent Claim
134 words
A molding composition comprising a uniform blend of from about 75% to about 25% by weight of an uncured rubber, and about 25% to about 75% by weight of a filler material comprising (a) 100 parts by weight of cured rubber particles; (b) from about 1 to about 5 parts by weight of a liquid, sulfur-curable polymeric binder having ethylenic unsaturation and being soluble in hexane, benzene, or a combination thereof, the binder having a viscosity at 280° F. of not greater than about one million centipoises and further characterized as being capable of softening surfaces of the cured rubber particles when applied thereto and the particles are heated; and (c) A curing agent for the polymeric binder in a quantity ranging from about 50% to about 500% by weight of the polymeric binder.
Claim 21
Dependent Claim
133 words
A molding composition comprising a uniform blend of from about 75% to about 25% by weight of an uncured rubber, and about 25% to about 75% by weight of a filler material comprising (a) 100 parts by weight of cured rubber particles; (b) from about 1 to about 5 parts by weight of a liquid, sulfur-curable polymeric binder having ethylenic unsaturation and being soluble in hexane, benzene or a combination thereof, the binder having a viscosity at 280° F. of not greater than about one million centipoises and further characterized by being capable of softening surfaces of the cured rubber particles when applied thereto and the particles are heated; and (c) a curing agent for the polymeric binder in a quantity of not less than about 50% by weight of the polymeric binder.
Claim 22
Dependent Claim
133 words
A molding composition comprising a uniform blend of from about 75% to about 25% by weight of an uncured rubber, and about 25% to about 75% by weight of a filler material comprising (a) 100 parts by weight of cured rubber particles; (b) from about 1 to about 5 parts by weight of a liquid, sulfur-curable polymeric binder having ethylenic unsaturation and being soluble in hexane, benzene or a combination thereof, the binder having a viscosity at 280° F. of not greater than about one million centipoises and further characterized by being capable of softening surfaces of the cured rubber particles when applied thereto and the particles are heated; and (c) a curing agent for the polymeric binder in a quantity of not less than about 50% by weight of the polymeric binder.
Claim 23
Dependent Claim
30 words
The molding composition of claim 17 wherein said cured rubber particles are selected from the group consisting of styrene-butadiene rubbers, neoprene rubbers, nitrile rubbers, butyl rubbers and ethylene propylene-diene rubbers.
References Cited (Backward Citations)
US3281389A
Cited
US3489710A
Cited
US3726944A
Cited
US4125578A
Cited
US4101463A
Cited
US4257925A
Cited
US4304885A
Cited
US4244841A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-06 | 1988-05-07 | 1988-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-06 | 1992-05-07 | 1992-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-06 | 1996-05-07 | 1996-11-06 | $7700.00 | Window Closed / Lapsed |