Reclaimed vulcanized rubber
Assignee: Setech International Ltd
•
Filing: 1977-06-01
•
Granted: 1978-11-14
•
Expires: 1997-06-01
Abstract
Abstract Vulcanized rubber is reclaimed by treating pieces of the rubber to render a surface layer of each piece plastic while the inner core of the piece remains non-plastic. A chemical reagent can be used in the treatment, but it is preferred to render the surface layers of the rubber pieces plastic by a heat treatment which involves direct exposure of the pieces of rubber to either a flame or a heated gas. In a preferred embodiment of the invention vulcanized rubber pieces are dropped under gravity into a flame so that any attached textile residues are burnt away simultaneously with the plasticizing of the surface layers of the pieces, and the heated pieces then enter a stream of cold air which quenches the heat treatment. Vulcanized rubber articles made from the rubber reclaimed by the method of the invention have improved properties as compared with articles made by the conventional methods of reusing vulcanized rubber.
Inventors
- 👤 Derek W. Sear
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 05:27
CPC Classifications
C; C08; C08L; C08L17/00; C08J; C08J11/00; C08J11/04; C08J11/10; C08J3/00; C08J2321/00; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62; Y10; Y10S; Y10S264/00; Y10S264/911; Y10S264/912
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
63 words
A method of reclaiming vulcanised rubber which comprises the step of searing the surface of vulcanised rubber by direct application thereto of at least one flame for a time insufficient for the vulcanised rubber to ignite and thereby causing a surface layer of the vulcanised rubber to be rendered plastic by devulcanisation whilst an inner core of the rubber remains vulcanised and non-plastic.
Claim 2
Dependent Claim
37 words
A method according to claim 1 which comprises the step of causing a flame derieved from a gas/air burner to pass over the vulcanised rubber at a speed such that the rubber fumes but does not ignite.
Claim 3
Dependent Claim
45 words
A method according to claim 1 which comprises the steps of causing vulcanised rubber crumb to fall under gravity into the blue zone of a flame derived from a pressure fed gas/air burner and thereafter quenching the rubber crumb by a stream of cooling air.
Claim 4
Dependent Claim
33 words
A method according to claim 1 which comprises the step of causing vulcanised rubber crumb to fall under gravity into the blue zone of a flame derived from a pressure fed butane/air burner.
Claim 5
Dependent Claim
39 words
A method according to claim 3 wherein the rubber crumb is a rubber crumb obtained from tires and includes textile residues, and wherein the textile fibres in the rubber crumb are removed therefrom by the action of the flame.
Claim 6
Independent Claim
84 words
A method of reclaiming vulcanised rubber which comprises the step of causing the surfaces of vulcanised rubber crumb to be seared by exposing the vulcanised rubber crumb directly heated gases which gases directly heat the rubber crumb to a temperature at which the surface of the rubber sears, the exposure being for a time insufficient for burning to commence, whereby the surface layers of the rubber crumb are rendered plastic by devulcanisation, whilst the inner cores of the rubber crumb remain vulcanised and nonplastic.
Claim 7
Dependent Claim
51 words
A method according to claim 6 wherein the vulcanised rubber crumb is exposed to the said temperature by causing the vulcanised rubber crumb to fall through a reaction chamber to which heated gases are fed, such that the heated gases rise through the reaction chamber whilst the rubber crumb fall therethrough.
Claim 8
Dependent Claim
25 words
A method according to claim 7 wherein the heated gases are fed to the reaction chamber at a temperature of the order of 900° C.
Claim 9
Dependent Claim
20 words
A method according to claim 5 whereing the rubber crumb is capable of passing through a sieve of 30 mesh/inch.
Claim 10
Dependent Claim
20 words
A method according to claim 5 wherein the rubber crumb has a maximum size of the order of 0.5 mm.
References Cited (Backward Citations)
US1963943A
Cited
GB580051A
Cited
US2648097A
Cited
US2795820A
Cited
GB1034028A
Cited
US3368013A
Cited
US3678016A
Cited
US3703488A
Cited
GB1278258A
Cited
GB1283866A
Cited
US3767601A
Cited
GB1405170A
Cited
US4029550A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-13 | 1982-05-15 | 1982-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-13 | 1986-05-15 | 1986-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-13 | 1990-05-15 | 1990-11-14 | $7700.00 | Window Closed / Lapsed |