Method of coloring bakeable porcelain dental restorations
Assignee: Individual
•
Filing: 1982-11-01
•
Granted: 1984-11-06
•
Expires: 2002-11-01
Abstract
Abstract A method is provided of coloring bakeable porcelain dental restorations. A plurality of pigmented coloring solutions is provided for application to a porcelain restoration. Each coloring solution comprises a pigment of low temperature porcelain-fusable powder and a substantially clear carrier liquid that supports a dispersion of said pigment and vaporizes when the restoration is baked. A film of the coloring solution is coated onto said restoration and then cured. The steps of coating the restoration and curing the film are repeated as necessary to match the color of the restoration to the color of a patient's teeth. The coated restoration is then baked to fuse the pigment to the porcelain and vaporize the cured carrier liquid.
Inventors
- 👤 Asami Tanaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 22:03
CPC Classifications
A; A61; A61C; A61C13/00; A61C13/08; A61C13/082; A61C19/00
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
235 words
A method of coloring the porcelain of bakeable porcelain dental restorations, comprising: (a) providing cureable coloring solutions for application to the non-metallic porcelain portion of said restoration, each solution comprising a different color pigment of low temperature porcelain-fuseable powder and a substantially clear vaporizable cureable carrier liquid to support a dispersion of said pigment, said carrier liquid being impervious to water or saliva when cured; (b) coating at least a portion of said porcelain restoration with a film of one of said coloring solutions to closely match the color of said restoration to the color of a patient's existing tooth; (c) curing said film at non-elevated temperatures on said porcelain restoration prior to the application of a subsequent film, said cured film being substantially clear, dry, impervious to water or saliva, undisturbed by handling and capable of being recoated without disturbing earlier applied and cured coats; (d) recoating at least a portion of said previously applied and cured film with a predetermined number of said coloring solutions until a desired coloration is obtained, each film recoating being cured prior to the application of a subsequent film coating whereby each previous film coating is not disturbed by a subsequent film coating; and (e) baking said restoration with said predetermined number of films thereon at a temperature sufficiently high to vaporize said carrier liquid and to fuse said pigment to said restoration, thereby permanently coloring said restoration.
Claim 2
Independent Claim
235 words
A method of coloring the porcelain of bakeable porcelain dental restorations, comprising: (a) providing cureable coloring solutions for application to the non-metallic porcelain portion of said restoration, each solution comprising a different color pigment of low temperature porcelain-fuseable powder and a substantially clear vaporizable cureable carrier liquid to support a dispersion of said pigment, said carrier liquid being impervious to water or saliva when cured; (b) coating at least a portion of said porcelain restoration with a film of one of said coloring solutions to closely match the color of said restoration to the color of a patient's existing tooth; (c) curing said film at non-elevated temperatures on said porcelain restoration prior to the application of a subsequent film, said cured film being substantially clear, dry, impervious to water or saliva, undisturbed by handling and capable of being recoated without disturbing earlier applied and cured coats; (d) recoating at least a portion of said previously applied and cured film with a predetermined number of said coloring solutions until a desired coloration is obtained, each film recoating being cured prior to the application of a subsequent film coating whereby each previous film coating is not disturbed by a subsequent film coating; and (e) baking said restoration with said predetermined number of films thereon at a temperature sufficiently high to vaporize said carrier liquid and to fuse said pigment to said restoration, thereby permanently coloring said restoration.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein said pigment comprises a metal oxide suitable for use with porcelain.
Claim 4
Dependent Claim
29 words
The method of claim 1 wherein said carrier liquid vaporizes at a temperature approximately equal to or less than the temperature at which said pigment fuses to said restoration.
Claim 5
Dependent Claim
20 words
The method of claim 1 wherein said pigment fuses to said porcelain at a temperature greater than about 1000° F.
Claim 6
Dependent Claim
13 words
The method of claim 1 wherein said carrier liquid is an organic material.
Claim 7
Dependent Claim
17 words
The method of claim 1 wherein said carrier liquid vaporizes at a temperature of about 1000° F.
Claim 8
Dependent Claim
16 words
The method of claim 1 wherein said carrier liquid is not soluble in water or saliva.
Claim 9
Dependent Claim
16 words
The method of claim 1 wherein said carrier liquid comprises at least in part, liquid acetate.
Claim 10
Dependent Claim
13 words
The method of claim 1 wherein said carrier liquid cures at room temperature.
Claim 11
Dependent Claim
20 words
The method of claim 1 wherein said carrier liquid cures in less than one minute when coated on a substrate.
Claim 12
Dependent Claim
18 words
The method of claim 1 wherein said coloring solutions are coated on said restoration with a brush-like applicator.
Claim 13
Dependent Claim
22 words
The method of claim 1 wherein the curing of said coating of said coloring solution removably binds said pigment to said procelain.
Claim 14
Dependent Claim
22 words
The method of claim 1 wherein portions of said coating of cured solution are manually removed without damaging the underlying porcelain substrate.
Claim 15
Independent Claim
246 words
A method of coloring bakeable procelain dental restorations, comprising: (a) providing cureable coloring solutions for application to the porcelain of said restoration, each solution comprising a different color pigment of low temperature porcelain-fusable powder and a substantially clear fast-curing vaporizable carrier liquid to support a dispersion of said pigment, said carrier liquid being impervious to water or saliva when cured; (b) coating at least a portion of said porcelain restoration with a film of one of said coloring solutions to alter the color of said porcelain restoration to closely match the color of a patient's existing tooth; (c) curing said applied film at non-elevated temperatures prior to the application of a subsequent film, said cured film being substantially clear, dry, impervious to water or saliva, undisturbed by handling and capable of being recoated without disturbing earlier applied and cured coats; (d) manually removing any unnecessary portion of said coating of cured solution; (e) recoating at least a portion of said previously applied and cured film with a predetermined number of films of one or more of said coloring solutions until a desired coloration is obtained, each film coating being cured prior to the application of a subsequent film coating whereby a previously applied film is not disturbed by a subsequent coating; and (f) baking said restoration with said predetermined number of films thereon at a temperature sufficiently high to vaporize said carrier liquid and to fuse said pigment to said restoration, thereby permanently coloring said restoration.
Claim 16
Independent Claim
246 words
A method of coloring bakeable procelain dental restorations, comprising: (a) providing cureable coloring solutions for application to the porcelain of said restoration, each solution comprising a different color pigment of low temperature porcelain-fusable powder and a substantially clear fast-curing vaporizable carrier liquid to support a dispersion of said pigment, said carrier liquid being impervious to water or saliva when cured; (b) coating at least a portion of said porcelain restoration with a film of one of said coloring solutions to alter the color of said porcelain restoration to closely match the color of a patient's existing tooth; (c) curing said applied film at non-elevated temperatures prior to the application of a subsequent film, said cured film being substantially clear, dry, impervious to water or saliva, undisturbed by handling and capable of being recoated without disturbing earlier applied and cured coats; (d) manually removing any unnecessary portion of said coating of cured solution; (e) recoating at least a portion of said previously applied and cured film with a predetermined number of films of one or more of said coloring solutions until a desired coloration is obtained, each film coating being cured prior to the application of a subsequent film coating whereby a previously applied film is not disturbed by a subsequent coating; and (f) baking said restoration with said predetermined number of films thereon at a temperature sufficiently high to vaporize said carrier liquid and to fuse said pigment to said restoration, thereby permanently coloring said restoration.
Claim 17
Dependent Claim
17 words
The method of claim 14 wherein said pigment comprises a metal oxide suitable for use with porcelain.
Claim 18
Dependent Claim
29 words
The method of claim 14 wherein said carrier liquid vaporizes at a temperature approximately equal to or less than the temperature at which said pigment fuses to said restoration.
Claim 19
Dependent Claim
20 words
The method of claim 14 wherein said pigment fuses to said porcelain at a temperature greater than about 1000° F.
Claim 20
Dependent Claim
13 words
The method of claim 14 wherein said carrier liquid is an organic material.
Claim 21
Dependent Claim
17 words
The method of claim 14 wherein said carrier liquid vaporizes at a temperature of about 1000° F.
Claim 22
Dependent Claim
16 words
The method of claim 14 wherein said carrier liquid comprises at least in part, liquid acetate.
Claim 23
Dependent Claim
13 words
The method of claim 14 wherein said carrier liquid cures at room temperature.
Claim 24
Dependent Claim
20 words
The method of claim 14 wherein said carrier liquid cures in less than one minute when coated on a substrate.
Claim 25
Dependent Claim
18 words
The method of claim 14 wherein said coloring solutions are coated on said restoration with a brush-like applicator.
Claim 26
Dependent Claim
22 words
The method of claim 14 wherein the curing of said coating of said coloring solution removably binds said pigment to said procelain.
Claim 27
Dependent Claim
22 words
The method of claim 14 wherein portions of said coating of cured solution are manually removed without damaging the underlying porcelain substrate.
References Cited (Backward Citations)
US2682480A
Cited
US3089782A
Cited
US3218711A
Cited
US4107348A
Cited
US4141144A
Cited
US4207678A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-06 | 1988-05-07 | 1988-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-06 | 1992-05-07 | 1992-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-06 | 1996-05-07 | 1996-11-06 | $7700.00 | Window Closed / Lapsed |