US4141144A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Dental material and method for controlling tooth lustre
Assignee: Individual
•
Filing: 1977-01-26
•
Granted: 1979-02-27
•
Expires: 1997-01-26
Abstract
Abstract The dental material of the present invention comprises a polymerizable binder, a polymerization agent and an additive comprising finely divided particles of muscovite mica in a range of from about 1 to 20 percent by weight of the dental material for direct dental filling and restoration applications and in a range of from about 1 to 30 percent for cosmetically treating the surface of a tooth as a veneer or paint-on.
Inventors
- 👤 Stewart J. Lustgarten
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 23:38
CPC Classifications
A; A61; A61K; A61K6/00; A61K6/80; A61K6/884; A61K6/887
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
65 words
A dental material comprising in combination; a polymerizable resin binder wherein said binder is at least one acrylic monomer, an agent for polymerizing said binder, an inorganic filler and an additive for controlling the hue and lustre of said material, said additive comprising finely divided particles of translucent muscovite mica in a concentration of between about 1 to about 20% by weight of said material.
Claim 2
Dependent Claim
65 words
A dental material comprising in combination; a polymerizable resin binder wherein said binder is at least one acrylic monomer, an agent for polymerizing said binder, an inorganic filler and an additive for controlling the hue and lustre of said material, said additive comprising finely divided particles of translucent muscovite mica in a concentration of between about 1 to about 20% by weight of said material.
Claim 3
Dependent Claim
25 words
A dental material as defined in claim 1 wherein said mica particles are within a size range of between about 1 to about 50 microns.
Claim 4
Dependent Claim
38 words
A dental material as defined in claim 2 wherein a predetermined proportion of said mica particles of up to 100% are coated with a material selected from the group consisting of titanium dioxide, bismuth oxychloride and zirconium dioxide.
Claim 5
Dependent Claim
33 words
A dental material as defined in claim 4 wherein said polymerizable binder is selected from the group consisting of: methacrylic esters, cyanoacrylates, 2,2-bis[4-3-methacryloxy-2-hydroxypropoxy)-phenyl]-propane (BIS-GMA) and the reaction product of N-phenylglycine and glycidyl methacrylate.
Claim 6
Dependent Claim
31 words
A dental material as defined in claim 5 wherein said inorganic filler is selected from the group consisting of silica, glass beads, aluminum oxide, fused silica, fused quartz and crystalline quartz.
Claim 7
Dependent Claim
30 words
A dental material as defined in claim 5 wherein said polymerizable binder comprises 2,2-bis[4-3-methacryloxy-2-hydroxypropoxy)-phenyl]propane (BIS-GMA) and wherein said mateial further comprises a reactive diluent; an activator and a peroxide catalyst.
Claim 8
Dependent Claim
23 words
A dental material as defined in claim 6 wherein said filler particles and said mica particles are treated with a organosilane keying agent.
Claim 9
Independent Claim
67 words
A method for controlling the hue and lustre of a dental filling or restoration containing a polymerizable monomer composition wherein said monomer is at least one acrylic monomer including an inorganic filler as a portion of said composition comprising the step of; adding finely divided particles of transluclent muscovite mica to said composition in a range of between about 1 to 20% by weight of said composition.
Claim 10
Independent Claim
67 words
A method for controlling the hue and lustre of a dental filling or restoration containing a polymerizable monomer composition wherein said monomer is at least one acrylic monomer including an inorganic filler as a portion of said composition comprising the step of; adding finely divided particles of transluclent muscovite mica to said composition in a range of between about 1 to 20% by weight of said composition.
Claim 11
Dependent Claim
27 words
A dental material as defined in claim 1 wherein said mica particles is in a concentration of between about 1 to 4% by weight of said material.
Claim 12
Dependent Claim
25 words
A method as defined in claim 8 wherein said mica is selected within a particle size range of from about 1 to about 50 microns.
Claim 13
Dependent Claim
38 words
A method as defined in claim 10 wherein a predetermined proportion of said particles of mica of up to 100% are coated with a material selected from the group consisting of titanium dioxide, bismuth oxychloride and zirconium dioxide.
Claim 14
Dependent Claim
29 words
A method as defined in claim 11 wherein the hue shade of said composition is controlled by varying the weight ratio of said titanium dioxide coating to said mica.
Claim 15
Dependent Claim
29 words
A method as defined in claim 11 wherein the hue shade of said composition is controlled by varying the particle size concentration of said additive within said size range.
Claim 16
Independent Claim
86 words
A method for cosmetically treating the the surface of a tooth so as to establish a predetermined hue and lustre comprising forming a material composition containing a polymerizable resin binder wherein said binder is at least one acrylic monomer and an agent for polymerizing said binder, adding finely divided particles of muxcovite mica to said composition within a range of between about 1 to 30% by weight of said material composition and applying a thin film of said material composition to the surface of a tooth.
Claim 17
Independent Claim
86 words
A method for cosmetically treating the the surface of a tooth so as to establish a predetermined hue and lustre comprising forming a material composition containing a polymerizable resin binder wherein said binder is at least one acrylic monomer and an agent for polymerizing said binder, adding finely divided particles of muxcovite mica to said composition within a range of between about 1 to 30% by weight of said material composition and applying a thin film of said material composition to the surface of a tooth.
Claim 18
Dependent Claim
35 words
A method as claimed in claim 14 further comprising adding an inorganic filler selected from the group consisting of silica, glass beads, aluminum oxide, fused silica, fused quartz and crystalline quartz to said material composition.
Claim 19
Dependent Claim
30 words
A method as claimed in claim 15 wherein said particles of mica are coated with a material selected from the class consisting of titanium dioxide, zirconium dioxide and bismuth oxychloride.
Claim 20
Dependent Claim
25 words
A method as claimed in claim 16 wherein a predetermined proportion of said mica particles of up to 100% thereof are coated with titanium dioxide.
Claim 21
Dependent Claim
30 words
A method as claimed in claim 17 wherein the hue shade of said material composition is controlled by varying the weight ratio of said titanium dioxide coating to said mica.
Claim 22
Dependent Claim
30 words
A method as claimed in claim 17 wherein the hue shade of said material composition is controlled by varying the particle size concentration of said additive within said size range.
Claim 23
Dependent Claim
20 words
A method as defined in claim 14 wherein about 8% by weight of said additive is added to said material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-26 | 1982-08-28 | 1983-02-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-26 | 1986-08-28 | 1987-02-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-26 | 1990-08-28 | 1991-02-27 | $7700.00 | Window Closed / Lapsed |