Method of making refractory hard metal containing tiles for aluminum cell cathodes
Assignee: Rio Tinto Aluminium Ltd
•
Filing: 1983-01-28
•
Granted: 1984-11-06
•
Expires: 2003-01-28
Abstract
Abstract This invention relates to electrolytic reduction cells for aluminum production wherein tiles have been placed upon the cathode surfaces to improve the cell operation. These tiles have aluminum-wettable surfaces, which reduce electrical losses and increase cathode life. The tiles are produced from a mixture of refractory hard metal (RHM), a thermosetting resin, carbonaceous fillers and carbonaceous additives. The tiles are physically formed, polymerized and/or cross linked, and carbonized to form a tile which can be inserted into a cell. The tile may have the RHM homogeneously dispersed throughout the tile structure, or it may have the RHM concentrated in layered form.
Inventors
- 👤 William M. Buchta
- 👤 Dennis C. Nagle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 03:45
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/645; C04B35/515; C04B35/52; C04B35/56; C04B35/5607; C04B35/5611; C04B35/5622; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; C04B35/58078; C04B35/626; C04B35/63; C04B35/632; C04B35/634; C04B35/63448; C04B35/63472; C04B35/63476; C25; C25C; C25C3/00; C25C3/06; C25C3/08
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
81 words
A method for preparing an aluminum-wettable cathode surface, which method comprises: (a) preparing a molding composition of Refractory Hard Material, carbonaceous filler having a particle size less than 100 mesh, and a thermosetting resinous binder system having a char yield greater than 25 percent; (b) hot-pressing said composition to the surface of a cathode block to form a cured, adherent surface layer thereupon; and (c) carbonizing said surface layer to a carbonaceous matrix containing Refractory Hard Material, bonded by amorphous carbon.
Claim 2
Independent Claim
81 words
A method for preparing an aluminum-wettable cathode surface, which method comprises: (a) preparing a molding composition of Refractory Hard Material, carbonaceous filler having a particle size less than 100 mesh, and a thermosetting resinous binder system having a char yield greater than 25 percent; (b) hot-pressing said composition to the surface of a cathode block to form a cured, adherent surface layer thereupon; and (c) carbonizing said surface layer to a carbonaceous matrix containing Refractory Hard Material, bonded by amorphous carbon.
Claim 3
Dependent Claim
43 words
The method of claim 1, wherein said Refractory Hard Material comprises from about 20 to about 70 percent by weight of the molding composition, and is selected from the group consisting of titanium diboride, titanium carbide, zirconium diboride, zirconium carbide, and alloys thereof.
Claim 4
Dependent Claim
13 words
The method of claim 2, wherein said Refractory Hard Material is titanium diboride.
Claim 5
Dependent Claim
23 words
The method of claim 3, wherein said titanium diboride comprises from about 30 to about 60 percent by weight of said molding composition.
Claim 6
Dependent Claim
26 words
The method of claim 1, wherein the thermosetting resinous binder system comprises resin selected from the group consisting of phenolic, polyphenylene, heterocyclic, silicone, and alkyd resins.
Claim 7
Dependent Claim
19 words
The method of claim 5, wherein said resinous binder system has a char yield greater than about 50 percent.
Claim 8
Dependent Claim
27 words
The method of claim 1, wherein said molding composition further comprises a carbonaceous additive having a particle size of from about -4 mesh to about +100 mesh.
Claim 9
Dependent Claim
47 words
The method of claim 7, wherein the molding composition comprises from about 20 to about 70 percent by weight titanium deboride, from about 1 to about 60 percent by weight carbonaceous filler and additive, and from about 20 to about 60 percent by weight resinous binder system.
Claim 10
Independent Claim
94 words
A method for forming an aluminum-wettable cathode surface, which method comprises: (a) preparing a molding composition of Refractory Hard Material, carbonaceous filler having a particle size less than 100 mesh, and a thermosetting resinous binder system having a char yield greater than 25 percent; (b) hot pressing said composition to form a cured, rigid element comprising Refractory Hard Material in a carbonaceous matrix; (c) further heating said element to fully carbonize said matrix without graphitizing the carbon present in the binder system; and (d) adhering the thus carbonized element to a carbon cathode block.
Claim 11
Independent Claim
94 words
A method for forming an aluminum-wettable cathode surface, which method comprises: (a) preparing a molding composition of Refractory Hard Material, carbonaceous filler having a particle size less than 100 mesh, and a thermosetting resinous binder system having a char yield greater than 25 percent; (b) hot pressing said composition to form a cured, rigid element comprising Refractory Hard Material in a carbonaceous matrix; (c) further heating said element to fully carbonize said matrix without graphitizing the carbon present in the binder system; and (d) adhering the thus carbonized element to a carbon cathode block.
Claim 12
Dependent Claim
42 words
The method of claim 9, wherein said Refractory Hard Material comprises from about 20 to about 70 percent by weight of the molding composition, and is selected from the group consisting of titanium deboride, titanium carbide, zirconium diboride, zirconium carbide, alloys thereof.
Claim 13
Dependent Claim
13 words
The method of claim 10, wherein said Refractory Hard Material is titanium diboride.
Claim 14
Dependent Claim
23 words
The method of claim 11, wherein said titanium diboride comprises from about 30 to about 60 percent by weight of said molding composition.
Claim 15
Dependent Claim
26 words
The method of claim 12, wherein the thermosetting resinous binder system comprises resin selected from the group consisting of phenolic, polyphenylene, heterocyclic, silicone, and alkyd resins.
Claim 16
Dependent Claim
19 words
The method of claim 13, wherein said resinous binder system has a char yield greater than about 50 percent.
Claim 17
Dependent Claim
27 words
The method of claim 14, wherein said molding composition further comprises a carbonaceous additive having a particle size of from about -4 mesh to about +100 mesh.
Claim 18
Dependent Claim
47 words
The method of claim 15, wherein the molding composition comprises from about 20 to about 70 percent by weight titanium diboride, from about 1 to about 60 percent by weight carbonaceous filler and additive, and from about 20 to about 60 percent by weight resinous binder system.
Claim 19
Independent Claim
101 words
A method for forming an aluminum-wettable cathode surface, which method comprises: (a) preparing a molding composition of Refractory Hard Material, carbonaceous filler having a particle size less than 100 mesh, and a thermosetting resinous binder system having a char yield greater than 25 percent; (b) hot pressing said composition to form a cured, rigid element comprising Refractory Hard Material in a carbonaceous matrix; (c) adhering said rigid element to a carbon cathode block; and (d) carbonizing said element in situ to form a carbon block having a surface layer comprising Refractory Hard Material in a carbonaceous matrix bonded by amorphous carbon.
Claim 20
Independent Claim
101 words
A method for forming an aluminum-wettable cathode surface, which method comprises: (a) preparing a molding composition of Refractory Hard Material, carbonaceous filler having a particle size less than 100 mesh, and a thermosetting resinous binder system having a char yield greater than 25 percent; (b) hot pressing said composition to form a cured, rigid element comprising Refractory Hard Material in a carbonaceous matrix; (c) adhering said rigid element to a carbon cathode block; and (d) carbonizing said element in situ to form a carbon block having a surface layer comprising Refractory Hard Material in a carbonaceous matrix bonded by amorphous carbon.
Claim 21
Independent Claim
99 words
A method for preparing an aluminum-wettable cathode surface, which method comprises: (a) preparing a molding composition of Refractory Hard Material, carbonaceous filler, and a thermosetting resinous binder system having a char yield greater than 25 percent; (b) preparing a carbon mixture of carbonaceous filler and thermosetting resinous binder system; (c) hot-pressing and carbonizing a layered structure of said molding composition and said carbon mixture to form a unitary layered element of Refractory Hard Material in a carbonaceous matrix, and carbon; and (d) adhering said element to a carbon cathode block with said Refractory Hard Material containing carbonaceous matrix exposed.
Claim 22
Independent Claim
99 words
A method for preparing an aluminum-wettable cathode surface, which method comprises: (a) preparing a molding composition of Refractory Hard Material, carbonaceous filler, and a thermosetting resinous binder system having a char yield greater than 25 percent; (b) preparing a carbon mixture of carbonaceous filler and thermosetting resinous binder system; (c) hot-pressing and carbonizing a layered structure of said molding composition and said carbon mixture to form a unitary layered element of Refractory Hard Material in a carbonaceous matrix, and carbon; and (d) adhering said element to a carbon cathode block with said Refractory Hard Material containing carbonaceous matrix exposed.
Claim 23
Dependent Claim
43 words
The method of claim 18, wherein said Refractory Hard Material comprises from about 20 to about 70 percent by weight of the molding composition, and is selected from the group consisting of titanium diboride, titanium carbide, zirconium diboride, zirconium carbide, and alloys thereof.
Claim 24
Dependent Claim
13 words
The method of claim 19, wherein said Refractory Hard Material is titanium diboride.
Claim 25
Dependent Claim
24 words
The method of claim 20, wherein said resinous binder system is selected from the group consisting of phenolic, polyphenylene, heterocyclic, silicone, and alkyd resins.
Claim 26
Dependent Claim
35 words
The method of claim 21, wherein at least one of the molding composition and the carbon mixture further comprises a carbonaceous additive having a particle size of from about -4 mesh to about +100 mesh.
Claim 27
Dependent Claim
47 words
The method of claim 20, wherein the molding composition comprises from about 20 to about 70 percent by weight titanium diboride, from about 1 to about 60 percent by weight carbonaceous filler and additive, and from about 20 to about 60 percent be weight resinous binder system.
Claim 28
Dependent Claim
17 words
The method of claim 20, wherein said layered structure is hot-pressed in-situ on the carbon cathode block.
Claim 29
Dependent Claim
45 words
The method of claim 24, wherein said layered structure is carbonized to form an element having a layer of Refractory Hard Material in a carbonaceous matrix bonded by amorphous carbon, and a layer of carbon directly in contact and bonded to the carbon cathode block.
References Cited (Backward Citations)
US3400061A
Cited
US3492208A
Cited
US3616045A
Cited
US3661736A
Cited
US4093524A
Cited
US4333813A
Cited
US4308114A
Cited
US4376029A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-06 | 1988-05-07 | 1988-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-06 | 1992-05-07 | 1992-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-06 | 1996-05-07 | 1996-11-06 | $7700.00 | Window Closed / Lapsed |