Electrolytic production of aluminum using a composite cathode
Assignee: Alcoa Corp
•
Filing: 1980-07-21
•
Granted: 1981-12-29
•
Expires: 2000-07-21
Abstract
Abstract A metal such as aluminum is produced by electrolysis of a compound of the metal in a solvent or bath such as molten salt. Electrolysis is carried out by passing a current from an anode to a cathode between which the solvent bath is situated. The cathode is composed of a composite comprising graphite and a refractory hard metal such as titanium diboride. The properties and performance of the composite cathode are improved through careful manufacturing controls and selectivity with respect to electrode configuration and cell operating conditions.
Inventors
- 👤 Subodh K. Das
- 👤 Perry A. Foster, Jr.
- 👤 Gregory J. Hildeman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 09:34
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/5607; C04B35/52; C04B35/528; C04B35/532; C04B35/58; C04B35/58007; C04B35/5805; C04B35/58064; C04B35/58071; C04B35/58078; C04B35/58085; C04B35/58092; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B35/634; C04B35/63496; C04B41/00; C04B41/009; C04B41/45; C04B41/50; C04B41/5053; C04B41/51; C04B41/5133; C04B41/80; C04B41/81; C04B41/85; C04B41/87; C04B41/88; C25; C25C; C25C3/00; C25C3/06; C25C3/08; C04B2235/00; C04B2235/65; C04B2235/66; C04B2235/666
Claims Analysis
Total Claims: 40
Claim 1
Independent Claim
148 words
A method for the production of metal in an electrolytic cell comprising electrolyzing a bath comprising a compound of the metal dissolved in a molten solvent by passing electric current between one or more anode and one or more cathode surfaces to produce said metal which collects as a molten pool upon a base cathode surface, wherein the improvement comprises providing one or more cathode surfaces extending outwardly from said base cathode surface toward each anode, said cathode surfaces being provided as composite surface regions comprising graphite impregnated with refractory hard metal and by providing a composite mixture comprising carbonaceous binder and refractory hard metal and graphitizing said composite mixture at a temperature of at least 2350° C. in a non-oxidizing atmosphere to convert carbonaceous material therein to the graphitic structure and produce a unitary continuous graphite structure impregnated with refractory hard metal at said cathode surface region.
Claim 2
Independent Claim
148 words
A method for the production of metal in an electrolytic cell comprising electrolyzing a bath comprising a compound of the metal dissolved in a molten solvent by passing electric current between one or more anode and one or more cathode surfaces to produce said metal which collects as a molten pool upon a base cathode surface, wherein the improvement comprises providing one or more cathode surfaces extending outwardly from said base cathode surface toward each anode, said cathode surfaces being provided as composite surface regions comprising graphite impregnated with refractory hard metal and by providing a composite mixture comprising carbonaceous binder and refractory hard metal and graphitizing said composite mixture at a temperature of at least 2350° C. in a non-oxidizing atmosphere to convert carbonaceous material therein to the graphitic structure and produce a unitary continuous graphite structure impregnated with refractory hard metal at said cathode surface region.
Claim 3
Dependent Claim
12 words
The method according to claim 1 wherein said metal produced is aluminum.
Claim 4
Dependent Claim
22 words
The method according to claim 1 wherein said composite cathode surface region extends through said molten metal pool and into said bath.
Claim 5
Dependent Claim
24 words
The method according to claim 3 wherein said composite cathode surface includes a hollow portion adapted for holding an additional pool of molten metal.
Claim 6
Dependent Claim
24 words
The method according to claim 3 wherein a plurality of such cathode surface regions extends from said molten metal pool toward each anode surface.
Claim 7
Dependent Claim
32 words
The method according to claim 1 wherein said composite cathode surface region extends into said molten metal pool upon the base cathode and the electrolyte bath, but not extending into said bath.
Claim 8
Dependent Claim
24 words
The method according to claim 6 wherein a plurality of such cathode surface regions extends from said molten metal pool toward each anode surface.
Claim 9
Dependent Claim
22 words
The method according to claim 1 wherein said composite surface region is provided as an outward layer over a substantially carbonaceous core.
Claim 10
Dependent Claim
78 words
The method according to claim 1 wherein said electrolytic cell is a Hall type cell and said cell bath is a fluoroaluminate type and wherein alumina is electrolytically reduced to produce aluminum which collects as a molten pool upon said base cathode, and wherein a plurality of said composite cathode surface regions corresponds to each anode surface, said composite cathode surface regions extending outwardly from said cathode base toward said anode surface and into said molten aluminum pool.
Claim 11
Dependent Claim
19 words
The method according to claim 9 wherein said composite cathode surface region contains 5 to 60% refractory hard metal.
Claim 12
Dependent Claim
97 words
The method according to claim 1 wherein said electrolytic cell is a Hall type cell and said cell bath is a fluoroaluminate type and wherein alumina is electrolytically reduced to produce aluminum which collects as a molten pool upon said base cathode, and wherein the electric current is passed through said bath from one or more anodes to a plurality of said composite cathode surface regions corresponding to each anode surface, said composite cathode surface regions extending outwardly from said base cathode toward said anode surface and through said molten aluminum pool and into said cell bath.
Claim 13
Dependent Claim
19 words
The method according to claim 4 wherein said composite cathode surface region contains 60% to 99% refractory hard metal.
Claim 14
Dependent Claim
43 words
The method according to claim 4 wherein said composite cathode surface region contains 90 to 98% refractory hard metal and is produced by graphitizing a mixture comprising said refractory hard metal in particulate form and a carbonaceous binder without adding carbonaceous particulate thereto.
Claim 15
Dependent Claim
16 words
The method according to claim 13 wherein said graphitizing is carried out at over 2400° C.
Claim 16
Dependent Claim
30 words
The method according to claim 1 wherein said refractory hard metal is selected from the carbides, silicides and nitrides of the fourth, fifth and sixth groups of the Periodic Table.
Claim 17
Dependent Claim
20 words
The method according to claim 1 wherein said refractory hard metal is selected from the borides of titanium and zirconium.
Claim 18
Dependent Claim
28 words
The method according to claim 1 wherein said refractory hard metal in said composite mixture comprises TiB 2 provided in particulate form passing through a 325 mesh screen.
Claim 19
Dependent Claim
41 words
The method according to claim 1 wherein said graphitization is effected at temperatures of over 2400° C. and the graphite structure so produced exhibits an L c dimension greater than 400 A and a d 002 dimension less than 3.4 A.
Claim 20
Dependent Claim
31 words
The method according to claim 1 wherein said cathode surface is coated with metallic aluminum or an aluminum compound convertible to aluminum before used as an electrode in said electrolytic cell.
Claim 21
Dependent Claim
20 words
The method according to claim 1 wherein said composite surface region includes a coating consisting substantially of refractory hard metal.
Claim 22
Dependent Claim
27 words
The method according to claim 1 wherein prior to said graphitizing said composite is baked and then impregnated with pitch and again baked to increase its density.
Claim 23
Dependent Claim
19 words
The method according to claim 21 wherein said pitch contains refractory hard metal and impregnates such into said composite.
Claim 24
Dependent Claim
17 words
The method according to claim 1 wherein said electrolytic cell electrolyzes a chloroaluminate electrolyte to produce aluminum.
Claim 25
Dependent Claim
15 words
The method according to claim 1 wherein said composite mixture contains added particulate carbonaceous material.
Claim 26
Independent Claim
196 words
A method for the production of aluminum in an electrolytic cell comprising electrolyzing a molten fluoroaluminate salt bath containing aluminum oxide dissolved therein by passing electric current between one or more anodic and one or more cathodic surfaces to electrolyze said bath therebetween to produce molten aluminum which collects beneath said salt bath as a molten pool, wherein the improvement comprises providing one or more cathodic surfaces protruding from a base cathode beneath said molten aluminum pool and into said molten aluminum pool, the surface regions of said protruding cathode surfaces being provided as a composite comprising graphite impregnated with a refractory hard metal selected from the group consisting of the borides of titanium and zirconium, and provided by providing a composite mixture containing said refractory hard metal in particulate form and a carbonaceous binder to form a compact, baking to drive off volatiles from said compact without changing its internal structure and thereafter graphitizing said composite to convert carbonaceous material therein into graphite, said graphitization being carried out at temperatures over 2350° C. in a non-oxidizing atmosphere to produce at said cathode surface regions a substantially unitary continuous graphite structure impregnated with refractory hard metal.
Claim 27
Independent Claim
196 words
A method for the production of aluminum in an electrolytic cell comprising electrolyzing a molten fluoroaluminate salt bath containing aluminum oxide dissolved therein by passing electric current between one or more anodic and one or more cathodic surfaces to electrolyze said bath therebetween to produce molten aluminum which collects beneath said salt bath as a molten pool, wherein the improvement comprises providing one or more cathodic surfaces protruding from a base cathode beneath said molten aluminum pool and into said molten aluminum pool, the surface regions of said protruding cathode surfaces being provided as a composite comprising graphite impregnated with a refractory hard metal selected from the group consisting of the borides of titanium and zirconium, and provided by providing a composite mixture containing said refractory hard metal in particulate form and a carbonaceous binder to form a compact, baking to drive off volatiles from said compact without changing its internal structure and thereafter graphitizing said composite to convert carbonaceous material therein into graphite, said graphitization being carried out at temperatures over 2350° C. in a non-oxidizing atmosphere to produce at said cathode surface regions a substantially unitary continuous graphite structure impregnated with refractory hard metal.
Claim 28
Dependent Claim
17 words
The method according to claim 25 wherein said protruding cathode surfaces terminate within said molten aluminum pool.
Claim 29
Dependent Claim
29 words
The method according to claim 26 wherein said improved cathode surface regions contain 5 to 60% refractory hard metal and wherein said composite mixture provided contains added carbonaceous particulate.
Claim 30
Dependent Claim
23 words
The method according to claim 25 wherein said protruding cathode surfaces extend through said molten aluminum pool and into the overlying salt bath.
Claim 31
Dependent Claim
19 words
The method according to claim 28 wherein said improved cathode surface regions contain 60 to 99% refractory hard metal.
Claim 32
Dependent Claim
28 words
The method according to claim 28 wherein said composite cathode surface region contains 90 to 98% refractory hard metal and said graphitizing is carried out over 2400° C.
Claim 33
Dependent Claim
20 words
The method according to claim 30 wherein said composite surface region includes a coating consisting substantially of refractory hard metal.
Claim 34
Dependent Claim
20 words
The method according to claim 28 wherein said composite surface region includes a coating consisting substantially of refractory hard metal.
Claim 35
Dependent Claim
16 words
The method according to claim 28 wherein said graphitizing is carried out at over 2400° C.
Claim 36
Dependent Claim
24 words
The method according to claim 25 wherein said composite cathode surface includes a hollow portion adapted for holding an additional pool of molten metal.
Claim 37
Dependent Claim
16 words
The method according to claim 25 wherein said provided composite mixture includes added particulate carbonaceous material.
Claim 38
Dependent Claim
24 words
The method according to claim 35 wherein prior to said graphitizing said composite is baked and then impregnated with pitch to densify said graphite.
Claim 39
Dependent Claim
41 words
The method according to claim 36 wherein prior to said graphitizing said composite is baked and then impregnated with pitch and again baked to increase its density and wherein said pitch contains refractory hard metal and impregnates such into said composite.
Claim 40
Dependent Claim
35 words
The method according to claim 25 wherein said improved cathode surface region prior to use in said cell is coated with aluminum or an aluminum compound which provides such coating when starting up said cell.
References Cited (Backward Citations)
US2997744A
Cited
US3156639A
Cited
US3400061A
Cited
US3471380A
Cited
US3661736A
Cited
US3856650A
Cited
US4071420A
Cited
US4121983A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-28 | 1985-06-29 | 1985-12-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-28 | 1989-06-29 | 1989-12-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-28 | 1993-06-29 | 1993-12-29 | $7700.00 | Window Closed / Lapsed |