Polyvalent ion exchanged adsorbent for air separation
Assignee: Air Products and Chemicals Inc
•
Filing: 1982-11-15
•
Granted: 1984-11-06
•
Expires: 2002-11-15
Abstract
Abstract The invention relates to faujasite-containing compositions in which the original hydrogen or monovalent forms are ion exchanged to their polyvalent form and then thermally activated to promote dehydration and dehydroxylation of the faujasite while maintaining substantially the same zeolite content. The resulting compositions containing faujasites substantially in their dehydrated/dehydroxylated state have been found to have surprisingly high selectivities and capacities for the separation of air into nitrogen and oxygen.
Inventors
- 👤 Charles G. Coe
- 👤 Steven M. Kuznicki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 13:29
CPC Classifications
B; B01; B01J; B01J20/00; B01J20/02; B01J20/10; B01J20/16; B01J20/18; B01D; B01D53/00; B01D53/02; B01D53/04; B01J20/186; B01D2253/00; B01D2253/10; B01D2253/106; B01D2253/108; B01D2256/00; B01D2256/10; B01D2256/12; B01D2257/00; B01D2257/10; B01D2257/102; B01D2257/80
Claims Analysis
Total Claims: 49
Claim 1
Independent Claim
233 words
A polyvalent ion exchanged adsorbent composition comprising at least 50% by weight faujasite and the faujasite portion thereof having a majority of its exchangeable ion capacity in the polyvalent form prepared by aprocess which comprises: (a) ion exchanging said faujasite-containing composition with polyvalent ions, and (b) thermally activating the polyvalent exchanged composition to remove a substantial portion of its zeolitic water in said composition in such a manner as to produce a preponderance of said polyvalent ions in a dehydrated/dehydroxylated state under conditions to minimize the water vapor pressure throughout this step by subjecting the polyvalent exchange composition containing up to about 30% by weight of water to pressures in the range of about 0.1 to 10 atmospheres while maintaining a flow of a non-reactive purge gas at a molar mass velocity of about 0.5 to 100 kg. mole/m 2 -hr. and a residence time of no greater than about 2.5 minutes, heating said composition at a temperature ramp of 0.1° to 40° C./min. up to temperatures at least about 300° C. and no greater than 650° C. and maintaining said composition at these temperatures for a period such that the resulting nitrogen capacity and selectivity ratio of the resulting polyvalent exchanged composition for the separation of a binary mixture of oxygen and nitrogen is substantially greater than such a polyvalent ion exchanged composition that has not undergone such a thermal activation step.
Claim 2
Dependent Claim
233 words
A polyvalent ion exchanged adsorbent composition comprising at least 50% by weight faujasite and the faujasite portion thereof having a majority of its exchangeable ion capacity in the polyvalent form prepared by aprocess which comprises: (a) ion exchanging said faujasite-containing composition with polyvalent ions, and (b) thermally activating the polyvalent exchanged composition to remove a substantial portion of its zeolitic water in said composition in such a manner as to produce a preponderance of said polyvalent ions in a dehydrated/dehydroxylated state under conditions to minimize the water vapor pressure throughout this step by subjecting the polyvalent exchange composition containing up to about 30% by weight of water to pressures in the range of about 0.1 to 10 atmospheres while maintaining a flow of a non-reactive purge gas at a molar mass velocity of about 0.5 to 100 kg. mole/m 2 -hr. and a residence time of no greater than about 2.5 minutes, heating said composition at a temperature ramp of 0.1° to 40° C./min. up to temperatures at least about 300° C. and no greater than 650° C. and maintaining said composition at these temperatures for a period such that the resulting nitrogen capacity and selectivity ratio of the resulting polyvalent exchanged composition for the separation of a binary mixture of oxygen and nitrogen is substantially greater than such a polyvalent ion exchanged composition that has not undergone such a thermal activation step.
Claim 3
Dependent Claim
43 words
The composition of claim 1 wherein said ion exchange step is carried out in an aqueous medium and the partial pressure of water in the gaseous environment in contact with said composition during said thermal activation step is maintained less than 0.4 atmospheres.
Claim 4
Dependent Claim
11 words
The composition of claim 1 wherein said polyvalent ion is divalent.
Claim 5
Dependent Claim
23 words
The composition of claim 3 wherein said divalent ion is selected from the group consisting of magnesium, calcium, strontium, barium and mixtures therof.
Claim 6
Dependent Claim
11 words
The composition of claim 4 wherein the divalent ion is calcium.
Claim 7
Dependent Claim
29 words
The composition of claim 1 wherein said molar mass velocity is at least about 10 kg. mole/m 2 -hr. and a residence time of at least about 0.1 minute.
Claim 8
Dependent Claim
41 words
The composition of claim 1 wherein said polyvalent exchanged composition is subjected to an initial drying step at temperatures of no greater than 200° C. to remove a substantial portion of the surface water before carrying out said thermal activation step.
Claim 9
Dependent Claim
20 words
The composition of claim 7 which contains no more than about 2% by weight of water after said drying step.
Claim 10
Dependent Claim
37 words
The composition of claim 8 wherein said molar mass velocity is in the range of about 0.5 to 10 kg. mole/m. 2 -hr. and said residence time is in the range of about 0.0025 to 0.1 min.
Claim 11
Dependent Claim
35 words
The composition of claim 8 wherein said linear velocity is in the range of about 10 to 100 kg. mole/m. 2 -hr. and said residence time in the range of about 0.1 to 2.5 min.
Claim 12
Dependent Claim
20 words
The composition of claim 1 wherein said thermal activation step is carried out to temperatures of at least 350° C.
Claim 13
Dependent Claim
36 words
The composition of claim 1 wherein the polyvalent ion is calcium and the exchange step is carried out so that the faujasitic portion has at least 80% of its exchangeable ion capacity in the calcium form.
Claim 14
Dependent Claim
46 words
The composition of claim 12 wherein at least 70% by weight of the material is a faujasite having a silicon to aluminum ratio of approximately 1 up to about 2 and the balance of the composition is either a non-faujasite zeolite or an inert solid material.
Claim 15
Dependent Claim
49 words
The composition of claim 13 which has a selectivity ratio at 30° C. least 9 in the limit of low partial pressure of about 80% nitrogen and about 20% oxygen adsorbate and a nitrogen capacity at 30° C. of greater than about 0.4 millimols per gram of said composition.
Claim 16
Dependent Claim
29 words
The composition of claim 1 wherein its zeolite content is maintained to at least about 70% of its initial value which it had prior to said thermal activation step.
Claim 17
Dependent Claim
17 words
The use of the composition of claim 1 in the separation of air into nitrogen and oxygen.
Claim 18
Dependent Claim
20 words
The use of the composition of claim 1 in the adsorption of nitrogen from a mixture of gases containing nitrogen.
Claim 19
Dependent Claim
13 words
The composition of claim 1 wherein said zeolite is X type of zeolite.
Claim 20
Dependent Claim
164 words
A calcium ion exchanged composition comprising at least 70% by weight faujasite having a silicon to aluminum ratio of approximately 1 up to about 2 and the faujasite portion thereof having at least 80% of its exchangeable ion capacity in the calcium form prepared by a process which comprises: (a) exchanging said material with calcium ions in an aqueous system, and (b) thermally activating the calcium exchanged composition to remove a substantial portion of the zeolitic water and the hydration spheres surrounding the cations in said material by heating said composition at a temperature ramp of no greater than 40° C. per minuter while maintaining a flow of a nonreactive gas through said composition at a linear velocity of about 0.5 to 100 kg. mole/m. 2 -hr. and a residence time of about 0.0025 to 2.5 minutes up to a temperature in the range of 400° to 500° C. and maintaining the composition at these temperatures for a period of at least 12 hours.
Claim 21
Dependent Claim
164 words
A calcium ion exchanged composition comprising at least 70% by weight faujasite having a silicon to aluminum ratio of approximately 1 up to about 2 and the faujasite portion thereof having at least 80% of its exchangeable ion capacity in the calcium form prepared by a process which comprises: (a) exchanging said material with calcium ions in an aqueous system, and (b) thermally activating the calcium exchanged composition to remove a substantial portion of the zeolitic water and the hydration spheres surrounding the cations in said material by heating said composition at a temperature ramp of no greater than 40° C. per minuter while maintaining a flow of a nonreactive gas through said composition at a linear velocity of about 0.5 to 100 kg. mole/m. 2 -hr. and a residence time of about 0.0025 to 2.5 minutes up to a temperature in the range of 400° to 500° C. and maintaining the composition at these temperatures for a period of at least 12 hours.
Claim 22
Dependent Claim
37 words
The composition of claim 19 wherein the calcium exchanged composition is first subjected to a drying step at temperatures no greater than 200° C. to remove a substantial portion of the water before the thermal activation step.
Claim 23
Dependent Claim
27 words
The composition of claim 20 wherein the ion exchange step is carried out in an aqueous solution containing an excess of a water soluble salt of calcium.
Claim 24
Dependent Claim
19 words
The composition in claim 21 wherein the calcium salt is calcium chloride, calcium nitrate, calcium oxide or mixtures thereof.
Claim 25
Dependent Claim
54 words
The composition of claim 19 wherein the pressure of the thermal activation step is in the range of about 1 to 10 atmospheres, said molar mass velocity is in the range of about 1 to 10 kg. mole/m. 2 hr. and said residence time is in the range of about 0.01 to 0.1 min.
Claim 26
Dependent Claim
53 words
The composition of claim 19 wherein the pressure of the thermal activation step is in the range of about 1 to 10 atmospheres, said molar mass velocity is in the range of about 10 to 100 kg. mole/m. 2 -hr. and said residence time in the range of about 0.1 to 2 min.
Claim 27
Dependent Claim
175 words
A polyvalent ion exchanged adsorbent composition for the separation of a binary mixture of nitrogen and oxygen comprising at least 50% by weight faujasite and the faujasite portion thereof having a majority of its exchangeable ion capacity in the polyvalent form prepared by a process which comprises: (a) ion exchanging said faujasite-containing composition with polyvalent ions in an aqueous medium, and (b) thermally activating the polyvalent exchanged composition to remove a substantial portion of its zeolitic water in said composition in such a manner as to produce a preponderance of said polyvalent ions in a dehydrated/dehydroxylated state under conditions to minimize the water vapor pressure in the gaseous environment in contact with said composition throughout this thermal activation step to less than about 0.4 atmospheres at temperatures above 150° C. such that the resulting nitrogen capacity and selectivity ratio of the resulting polyvalent exchanged composition for the separation of a binary mixture of oxygen and nitrogen is substantially greater than such a polyvalent ion exchanged composition that has not undergone such a thermal activation step."
Claim 28
Dependent Claim
175 words
A polyvalent ion exchanged adsorbent composition for the separation of a binary mixture of nitrogen and oxygen comprising at least 50% by weight faujasite and the faujasite portion thereof having a majority of its exchangeable ion capacity in the polyvalent form prepared by a process which comprises: (a) ion exchanging said faujasite-containing composition with polyvalent ions in an aqueous medium, and (b) thermally activating the polyvalent exchanged composition to remove a substantial portion of its zeolitic water in said composition in such a manner as to produce a preponderance of said polyvalent ions in a dehydrated/dehydroxylated state under conditions to minimize the water vapor pressure in the gaseous environment in contact with said composition throughout this thermal activation step to less than about 0.4 atmospheres at temperatures above 150° C. such that the resulting nitrogen capacity and selectivity ratio of the resulting polyvalent exchanged composition for the separation of a binary mixture of oxygen and nitrogen is substantially greater than such a polyvalent ion exchanged composition that has not undergone such a thermal activation step."
Claim 29
Dependent Claim
26 words
The composition of claim 25 wherein said polyvalent ion is a divalent ion selected from the group consisting of magnesium, calcium, strontium, barium and mixtures thereof.
Claim 30
Dependent Claim
11 words
The composition of claim 26 wherein the divalent ion is calcium.
Claim 31
Dependent Claim
41 words
The composition of claim 25 wherein said polyvalent exchanged composition is subjected to an initial drying step at temperatures of no greater than 200° C. to remove a substantial portion of the surface water before carrying out said thermal activation step.
Claim 32
Dependent Claim
20 words
The composition of claim 25 wherein said thermal activation step is carried out to temperatures of at least 350° C.
Claim 33
Dependent Claim
36 words
The composition of claim 25 wherein the polyvalent ion is calcium and the exchange step is carried out so that the faujasitic portion has at least 80% of its exchangeable ion capacity in the calcium form.
Claim 34
Dependent Claim
46 words
The composition of claim 30 wherein at least 70% by weight of the material is a faujasite having a silicon to aluminum ratio of approximately 1 up to about 2 and the balance of the composition is either a non-faujasite zeolite or an inert solid material.
Claim 35
Dependent Claim
29 words
The composition of claim 25 wherein its zeolite content is maintained to at least about 70% of its initial value which it had prior to said thermal activation step.
Claim 36
Dependent Claim
13 words
The composition of claim 25 wherein said zeolite is X type of zeolite.
Claim 37
Dependent Claim
23 words
The composition of claim 33 wherein said polyvalent ions are selected from the group consisting of magnesium, calcium, strontium, barium and mixtures thereof.
Claim 38
Dependent Claim
12 words
The composition of claim 34 wherein said polyvalent ions are calcium ions.
Claim 39
Dependent Claim
47 words
The composition of claim 25 wherein said zeolitic component content is at least 75% by weight X type of zeolite and the balance is a material selected from the group consisting of an A-type of zeolite, and inert clay binder, other inert solid materials and mixtures thereof.
Claim 40
Independent Claim
152 words
A method of preparing a crystalline aluminosilicate zeolite which comprises: (a) selecting a zeolite, the major portion of which is a faujasite having a silicon to aluminum ratio in the range of approximately 1 and up to about 2 in either its hydrogen or its metallic form. (b) exchanging at least a major portion of said hydrogen or metal cations of a polyvalent metal, and (c) thermally activating the exchanged zeolite to remove a substantial portion of the zeolitic water and the hydration spheres surrounding the zeolite cations therein by subjecting said exchanged zeolite containing up to about 30% by weight water to a vacuum of less than about 0.1 atmospheres and heating said composition at a temperature ramp of 0.1° to 40° C./min up to temperatures in the range of about 400° to 500° C. and maintaining said composition at these temperatures for a period of at least about 6 hours.
Claim 41
Independent Claim
152 words
A method of preparing a crystalline aluminosilicate zeolite which comprises: (a) selecting a zeolite, the major portion of which is a faujasite having a silicon to aluminum ratio in the range of approximately 1 and up to about 2 in either its hydrogen or its metallic form. (b) exchanging at least a major portion of said hydrogen or metal cations of a polyvalent metal, and (c) thermally activating the exchanged zeolite to remove a substantial portion of the zeolitic water and the hydration spheres surrounding the zeolite cations therein by subjecting said exchanged zeolite containing up to about 30% by weight water to a vacuum of less than about 0.1 atmospheres and heating said composition at a temperature ramp of 0.1° to 40° C./min up to temperatures in the range of about 400° to 500° C. and maintaining said composition at these temperatures for a period of at least about 6 hours.
Claim 42
Dependent Claim
23 words
The method of claim 37 wherein said polyvalent metal is selected from the group consisting of magnesium, calcium, strontium, barium and mixtures thereof.
Claim 43
Dependent Claim
27 words
The method of claim 37 wherein step (b) is carried out until at least 90% of the exchangeable cations in the zeolite are in the calcium form.
Claim 44
Dependent Claim
14 words
The method of claim 37 wherein said vacuum is less than 100 mm Hg.
Claim 45
Dependent Claim
42 words
The method of claim 37 wherein the zeolite from step (b) is dried to remove a substantial portion of its surface water at temperatures of no greater than 200° C. and thermally activating the dried zeolite as set forth in step (c).
Claim 46
Dependent Claim
15 words
The method of claim 41 wherein the drying temperature is no greater than 120° C.
Claim 47
Dependent Claim
45 words
The method of claim 37 wherein the dried zeolite is placed in an adsorption zone for the adsorption of nitrogen from a mixture of gases containing nitrogen and said zeolite in the adsorption zone is thermally activated in accordance with the procedures of step (c).
Claim 48
Dependent Claim
12 words
The method of claim 43 wherein said mixture of gases is air.
Claim 49
Dependent Claim
43 words
The method of claim 37 wherein said zeolite contains at least 75% by weight X type of zeolite and the balance material selected from the group consisting of an A-type of zeolite, and inert clay binder, other inert solid materials and mixtures thereof.
References Cited (Backward Citations)
DE110478C
Cited
US2882244A
Cited
US3140932A
Cited
US3140933A
Cited
US3313091A
Cited
US4322394A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-06 | 1988-05-07 | 1988-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-06 | 1992-05-07 | 1992-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-06 | 1996-05-07 | 1996-11-06 | $7700.00 | Window Closed / Lapsed |