Aqueous copolyester dispersions suited for the subbing of polyester film
Assignee: Agfa Gevaert NV
•
Filing: 1982-10-26
•
Granted: 1984-10-23
•
Expires: 2002-10-26
Abstract
Abstract An aqueous copolyester dispersion suitable for the subbing of polyester film without use of organic solvents wherein the copolyester contains recurring ester groups derived from ethylene glycol and an acid mixture essentially consisting of 20 to 60 mole % of isophthalic acid, 6 to 10 mole % of sulphoisophthalic acid whose sulfo group is in salt from, 0.05 to 1 mole % of an aromatic polycarboxylic acid compound having at least three carboxylic acid groups, which compound is not capable of forming intramolecularly an anhydride and includes at least two carboxylated aromatic nuclei, and the balance of terephthalic acid; the copolyester has a glass transition temperature of at least 50° C. and an intrinsic viscosity of from 0.15 to 0.45 dl/g when measured at 25° C. in a mixture of phenol/o-dichlorobenzene (60/40 by volume).
Inventors
- 👤 Lucien J. Van Gossum
- 👤 August M. Marien
- 👤 Walter F. De Winter
- 👤 Etienne A. Van Thillo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 13:37
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/68; C08G63/688; C08G63/6884; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/043; C08J7/044; C08J7/056; G; G03; G03C; G03C1/00; G03C1/76; G03C1/91; G03C1/93; C08J2367/00; C08J2367/02; C08J2467/00; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/254; Y10T428/28; Y10T428/2835; Y10T428/31504; Y10T428/31652; Y10T428/31667; Y10T428/31678; Y10T428/31681; Y10T428/31685; Y10T428/31786; Y10T428/31794
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
136 words
A subbed polyester film comprising a polyester film base and directly affixed thereto a dried subbing layer of a copolyester applied from an aqueous dispersion and derived from ethylene glycol and an acid mixture consisting essentially of 20-60 mole % of isophthalic acid, 6-10 mole % of sulphoisophthalic acid whose sulpho group is in salt form, 0.05 to 1 mole % of an aromatic polycarboxylic acid compound having at least three carboxylic acid groups which is not capable of forming intramolecularly an anhydride and includes at least two carboxylated aromatic nuclei, and the balance of terephthalic acid, said copolyester having a glass transition temperature of at least 50° C. and an intrinsic viscosity of from 0.15 to 0.45 dl/g when measured at 25° C. in a mixture of phenol/o-dichlorobenzene in a ratio of 60/40 by volume.
Claim 2
Dependent Claim
136 words
A subbed polyester film comprising a polyester film base and directly affixed thereto a dried subbing layer of a copolyester applied from an aqueous dispersion and derived from ethylene glycol and an acid mixture consisting essentially of 20-60 mole % of isophthalic acid, 6-10 mole % of sulphoisophthalic acid whose sulpho group is in salt form, 0.05 to 1 mole % of an aromatic polycarboxylic acid compound having at least three carboxylic acid groups which is not capable of forming intramolecularly an anhydride and includes at least two carboxylated aromatic nuclei, and the balance of terephthalic acid, said copolyester having a glass transition temperature of at least 50° C. and an intrinsic viscosity of from 0.15 to 0.45 dl/g when measured at 25° C. in a mixture of phenol/o-dichlorobenzene in a ratio of 60/40 by volume.
Claim 3
Dependent Claim
26 words
Polyester film according to claim 1, wherein the sulpho group is represented by --SO 3 M wherein M is an alkali metal or an onium group.
Claim 4
Dependent Claim
56 words
Polyester film according to claim 1 wherein said copolyester has an intrinsic viscosity of from 0.20 to 0.45 dl/g, measured at 25° C. in a mixture of phenol/o-dichlorobenzene in a ratio of 60/40 by volume, and the dispersed phase of said dispersion is formed of particles having an average particle size not larger than 50 nm.
Claim 5
Dependent Claim
33 words
Polyester film according to claim 1, wherein said aromatic polycarboxylic acid compound is a polycarboxylic acid compound having at least four carboxylic acid groups which is not capable of forming intramolecularly an anhydride.
Claim 6
Dependent Claim
60 words
Polyester film according to claim 4, wherein said aromatic polycarboxylic acid compound corresponds to the following general formula: ##STR6## wherein X represents a chemical bond or a bivalent atom or bivalent group of atoms including oxygen, alkylene, carbonyl, sulphonyl, --NHSO 2 --, --NHCONH-- or a --NH--Q--Y--Q--NH-- group wherein Q represents carbonyl or sulphonyl and Y represents a bivalent organic group.
Claim 7
Dependent Claim
21 words
Polyester film according to claim 1, wherein the dispersion contains the copolyester in a concentration of at least 20% by weight.
Claim 8
Dependent Claim
23 words
Polyester film according to claim 1, where the dispersion contains a surface-active coating agent, colloidal silica, an embossing agent and/or an adhesion-improving agent.
Claim 9
Dependent Claim
21 words
Polyester film according to claim 1, wherein said film base is longitudinally stretched after the coating and drying of said dispersion.
Claim 10
Dependent Claim
27 words
Polyester film according to claim 8, comprising an additional subbing layer essentially consisting of gelatin and a plasticizing agent therefor and superimposed upon said first subbing layer.
Claim 11
Dependent Claim
36 words
Polyester film according to claim 8, comprising a further layer superimposed on said subbing layer and containing a polymer or copolymer containing free carboxylic acid groups and serving as binder material for a dye or pigment.
Claim 12
Dependent Claim
14 words
Polyester film according to claim 9, comprising an exterior photographic gelatin-containing silverhalide emulsion layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-23 | 1988-04-23 | 1988-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-23 | 1992-04-23 | 1992-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-23 | 1996-04-23 | 1996-10-23 | $7700.00 | Window Closed / Lapsed |