US4478706A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Zeolite L catalyst for reforming
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1984-02-06
•
Granted: 1984-10-23
•
Expires: 2004-02-06
Abstract
Abstract An improved reforming catalyst employing a zeolite L support is provided by soaking the zeolite L in an alkali solution having a pH of at least 11 for a time and at a temperature effective to increase the period of time over which the catalytic activity of the catalyst is maintained.
Inventors
- 👤 Abraham D. Cohen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 10:32
CPC Classifications
C; C10; C10G; C10G35/00; C10G35/04; C10G35/06; C10G35/095; B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/60; B01J29/61; B01J29/62
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
140 words
A reforming process for producing aromatic hydrocarbons from a hydrocarbon feedstock containing paraffins of at least C 6 comprising: contacting the hydrocarbon feedstock plus added hydrogen at elevated temperatures with a catalyst which comprises a zeolite having exchangeable cations of which at least 90% are metal ions selected from the group consisting of sodium, lithium, potassium, rubidium, barium and cesium and containing at least one metal selected from the group consisting of Group VIII of the periodic table of elements and having a dehydrocyclizing effect, said zeolite produced by soaking a type L zeolite prior to calcining the dehydrocyclizing metal loaded zeolite in an alkali solution having a pH of at least 11 for a time and at a temperature effective to increase the period of time over which the catalytic activity of the catalyst is maintained under reforming conditions.
Claim 2
Dependent Claim
140 words
A reforming process for producing aromatic hydrocarbons from a hydrocarbon feedstock containing paraffins of at least C 6 comprising: contacting the hydrocarbon feedstock plus added hydrogen at elevated temperatures with a catalyst which comprises a zeolite having exchangeable cations of which at least 90% are metal ions selected from the group consisting of sodium, lithium, potassium, rubidium, barium and cesium and containing at least one metal selected from the group consisting of Group VIII of the periodic table of elements and having a dehydrocyclizing effect, said zeolite produced by soaking a type L zeolite prior to calcining the dehydrocyclizing metal loaded zeolite in an alkali solution having a pH of at least 11 for a time and at a temperature effective to increase the period of time over which the catalytic activity of the catalyst is maintained under reforming conditions.
Claim 3
Dependent Claim
25 words
Process of claim 1 wherein the alkali soak is carried out to preferentially remove silica from the type L zeolite without substantial loss of crystallinity.
Claim 4
Dependent Claim
18 words
Process of claim 2 wherein 0.1 to 15 weight % of the silica is removed from said zeolite.
Claim 5
Dependent Claim
73 words
Process of claim 1 wherein the alkali soak is effective to increase by at least 50 hours the time period over which catalytic activity is maintained, based on a standardized test utilizing a hydrocarbon feedstock containing 60 weight % hexane, 30 weight % 3-methylpentane, and 10 weight % methylcyclopentane and on reforming conditions of about 500° C., 690 KPa, space velocity of 2.5 W/W/HR and an H/ 2 oil mole ratio of 6.
Claim 6
Dependent Claim
46 words
Process of claim 1 wherein the alkali of the alkali solution has a cation chosen from the group consisting of sodium, potassium, rubidium, cesium, strontium, barium and mixtures thereof and has an anion chosen from the group consisting of hydroxide, carbonate, phosphate, borate and mixtures thereof.
Claim 7
Dependent Claim
12 words
Process of claim 5 wherein the alkali solution is an aqueous solution.
Claim 8
Dependent Claim
42 words
Process of claim 6 wherein the soaking is carried out under agitation, the pH of the alkali solution is 13 to 16, the temperature of soaking is between 25° and 120° C. and the soaking time is between 2 and 80 hours.
Claim 9
Dependent Claim
21 words
Process of claim 7 wherein the alkali is chosen from the group consisting of potassium hydroxide, cesium hydroxide and rubidium hydroxide.
Claim 10
Dependent Claim
19 words
Process of claim 8 further comprising washing the soaked zeolite to remove excess alkali, followed by drying the zeolite.
Claim 11
Dependent Claim
48 words
Process of claim 1 wherein the zeolite catalyst contains at least one alkali metal selected from the group consisting of potassium, rubidium and cesium and contains from 0.1 to 6.0% by weight of at least one dehydrocyclizing metal selected from the group consisting of platinum, palladium and iridium.
Claim 12
Dependent Claim
23 words
Process of claim 10 wherein the zeolite additionally contains at least one metal chosen from the group consisting of rhenium, tin and germanium.
Claim 13
Dependent Claim
17 words
Process of claim 10 wherein the zeolite contains potassium and 0.2 to 5% by weight of platinum.
Claim 14
Dependent Claim
10 words
Process of claim 10 wherein the zeolite further contains sulfur.
Claim 15
Dependent Claim
17 words
Process of claim 1 wherein the zeolite is charged with the dehydrocyclizing metal after the alkali soak.
Claim 16
Dependent Claim
15 words
Process of claims 1, 4, 8, 10 or 14 further comprising shaping the soaked zeolite.
Claim 17
Dependent Claim
41 words
Process of claim 1 wherein the reforming conditions comprise temperatures of 450° to 520° C.; pressure of 517 KPa to 1.2 MPa; hourly liquid space velocity of 1 to 10 W/W/HR; and H 2 /oil mole ratio of 4 to 10.
Claim 18
Dependent Claim
94 words
Process of claims 1, 3, 7, 8 or 12 wherein the alkali soak is effective to increase the time to at least 250 hours over which the catalytic activity of the catalyst is maintained at a level of at least a 40 weight % conversion to aromatics, based on a standardized test utilizing a hydrocarbon feedstock containing 60 weight % hexane, 30 weight % 3-methylpentane and 10 weight % methylcyclopentane and on reforming conditions of about 500° C., 690 KPa, space velocity of 2.5 W/W/HR and an H 2 /oil mole ratio of 6.
Claim 19
Dependent Claim
19 words
Process of claim 17 wherein the alkali soak is effective to maintain catalytic activity for at least 300 hours.
References Cited (Backward Citations)
US3216789A
Cited
US3326797A
Cited
US3374182A
Cited
US3382039A
Cited
CA984367A
Cited
US3929669A
Cited
US3953365A
Cited
US3979335A
Cited
US4104320A
Cited
US4100262A
Cited
EP0040276A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-23 | 1988-04-23 | 1988-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-23 | 1992-04-23 | 1992-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-23 | 1996-04-23 | 1996-10-23 | $7700.00 | Window Closed / Lapsed |