Patent US4477964A successfully refreshed from Google Patents.
US4477964A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making p-i-n photodiodes
Assignee: Nokia Bell Labs
•
Filing: 1983-10-03
•
Granted: 1984-10-23
•
Expires: 2003-10-03
Abstract
Abstract Photodiodes (10) are fabricated in a single step diffusion process which exploits the characteristic of certain acceptors to form an anomalous diffusion profile (VI) including shallow and deep fronts (VIa and b) joined by an upwardly concave segment (VIc). By performing this type of diffusion into a low-doped n--type body (12) with a carrier concentration (VII) below that of the concave segment, a p+-p- junction (15) is formed at the depth of the concave segment and a p--n- junction (17) is formed at a greater depth. The zone (16) between the junctions is at least partially depleted and forms the active region of a p+-p--n- photodiode. Specifically described are InP:Cd photodiodes.
Inventors
- 👤 Aland K. Chin
- 👤 Bulusu V. Dutt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 20:18
CPC Classifications
H; H10; H10F; H10F77/00; H10F77/10; H10F77/12; H10F77/124; H10F30/00; H10F30/20; H10F30/21; H10F30/22; H10F30/223; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/544; Y10; Y10S; Y10S252/00; Y10S252/95; Y10S438/00; Y10S438/914
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
186 words
A method of fabricating a photodiode (10) having a depleted i-type active region (16) of a predetermined thickness bounded by a p-i type first junction (15) and an i-n second junction (17), comprising the steps of: diffusing an acceptor into a low-doped n - -type semiconductor body (12) so as to form an anomalous diffusion profile (FIG. 3) of net impurity concentration versus depth therein, said profile including upper and lower monotonically decreasing segments (VIa and b) connected by an upwardly concave segment (VIc), controlling the conditions of said diffusing step so that the carrier concentration of said body (VII) is below that corresponding to said concave segment, thereby forming said first junction (15) at approximately the depth of said concave segment and said second junction (17) at a depth corresponding to the intersection of said lower segment (VIb) and the carrier concentration of said body, and maintaining the difference in carrier concentration between that of said concave segment and that of said body so that said junctions are formed at depths separated by a distance essentially equal to said predetermined thickness of said active region.
Claim 2
Independent Claim
186 words
A method of fabricating a photodiode (10) having a depleted i-type active region (16) of a predetermined thickness bounded by a p-i type first junction (15) and an i-n second junction (17), comprising the steps of: diffusing an acceptor into a low-doped n - -type semiconductor body (12) so as to form an anomalous diffusion profile (FIG. 3) of net impurity concentration versus depth therein, said profile including upper and lower monotonically decreasing segments (VIa and b) connected by an upwardly concave segment (VIc), controlling the conditions of said diffusing step so that the carrier concentration of said body (VII) is below that corresponding to said concave segment, thereby forming said first junction (15) at approximately the depth of said concave segment and said second junction (17) at a depth corresponding to the intersection of said lower segment (VIb) and the carrier concentration of said body, and maintaining the difference in carrier concentration between that of said concave segment and that of said body so that said junctions are formed at depths separated by a distance essentially equal to said predetermined thickness of said active region.
Claim 3
Dependent Claim
31 words
The method of claim 1 wherein said body comprises a Group III-V compound and said diffusing step includes diffusing an impurity selected from the group consisting of Mn, Zn and Cd.
Claim 4
Dependent Claim
17 words
The method of claim 2 wherein said body comprises InP and said diffusing step includes diffusing Cd.
Claim 5
Dependent Claim
29 words
The method of claim 3 wherein said diffusing step is performed using an elemental source comprising Cd and an element selected from the group consisting of In and P.
Claim 6
Dependent Claim
32 words
The method of claim 4 wherein said source comprises In-Cd, said body is maintained at a temperature of about 680 degrees C., and the Cd activity in said source exceeds about 0.15.
Claim 7
Independent Claim
44 words
The method of claims 3 or 4 wherein said diffusing step takes place in a sealed ampoule for a time in the range of about one to four hours at a temperature of said body in the range of 630 to 850 degrees C.
Claim 8
Dependent Claim
25 words
The method of claim 6 wherein the depth of said junctions is controlled by varying the concentration of said In or P in said source.
Claim 9
Dependent Claim
34 words
The method of claim 1 wherein said active region is p - -type, said first junction, is a p + --p - junction and said second junction is a p - --n - junction.
References Cited (Backward Citations)
US4274103A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-23 | 1988-04-23 | 1988-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-23 | 1992-04-23 | 1992-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-23 | 1996-04-23 | 1996-10-23 | $7700.00 | Window Closed / Lapsed |