Polymer dispersions or emulsions as temporary surface protectants
Assignee: Henkel AG and Co KGaA
•
Filing: 1982-12-15
•
Granted: 1984-10-09
•
Expires: 2002-12-15
Abstract
Abstract Easily removable protective coatings formed from aqueous dispersions or emulsions of synthetic copolymers that can form a salt and wherein these aqueous coating materials, in addition to water, contain the following constituents: (a) at least one copolymer which: (i) at a temperature of about 5° C. and above will form a film, (ii) contains acid or amino groups wherein the copolymer is water-insoluble therewith, but wherein the copolymer becomes water-soluble when the acid or amino groups are in the form of a salt, and (iii) can exist in the form of an aqueous dispersion or emulsion. (b) at least one water-immiscible non-solvent which: (i) will not dissolve the copolymer in (a), (ii) has low volatility, and (iii) is liquid at room temperature; (c) at least one nonionic emulsifier with an HLB-value of less than 10; and (d) additional adjuvants and/or additives. The invention also relates to the application of these coating materials as temporary surface protectors, especially for metallic and/or painted surfaces, for storage in the open air with exposure to climatic and/or mechanical influences.
Inventors
- 👤 Hans-Christoph Wilk
- 👤 Jurgen Geke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 15:00
CPC Classifications
C; C09; C09D; C09D157/00; C09D157/04; C09D157/06; C09D5/00; C09D5/008
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
171 words
An aqueous coating material for applying an easily removable protective coating to a surface consisting essentially of an aqueous dispersion or emulsion containing: (a) a copolymer capable of forming a film at a temperature of 5° C. or above which contains acid groups or amino groups and is in the form of an aqueous dispersion or emulsion, wherein the acid groups are unsaturated mono and/or dicarboxylic acids and/or derivatives thereof, and the amino groups are esters of unsaturated carboxylic acids with alcohols containing tertiary amino groups and/or amides of unsaturated carboxylic acids with primary amines containing an additional tertiary amino group, and wherein the copolymer is substantially insoluble in water but becomes soluble therein when the acid groups or amino groups are in the form of salt; (b) a non-solvent which is liquid at room temperature, of low volatility, immiscible with water, and insoluble in the copolymer in (a); and (c) an emulsion or dispersion producing quantity of at least one nonionic emulsifying agent having an HLB-value of less than 10.
Claim 2
Dependent Claim
171 words
An aqueous coating material for applying an easily removable protective coating to a surface consisting essentially of an aqueous dispersion or emulsion containing: (a) a copolymer capable of forming a film at a temperature of 5° C. or above which contains acid groups or amino groups and is in the form of an aqueous dispersion or emulsion, wherein the acid groups are unsaturated mono and/or dicarboxylic acids and/or derivatives thereof, and the amino groups are esters of unsaturated carboxylic acids with alcohols containing tertiary amino groups and/or amides of unsaturated carboxylic acids with primary amines containing an additional tertiary amino group, and wherein the copolymer is substantially insoluble in water but becomes soluble therein when the acid groups or amino groups are in the form of salt; (b) a non-solvent which is liquid at room temperature, of low volatility, immiscible with water, and insoluble in the copolymer in (a); and (c) an emulsion or dispersion producing quantity of at least one nonionic emulsifying agent having an HLB-value of less than 10.
Claim 3
Dependent Claim
30 words
An aqueous coating material in accordance with claim 1 wherein the copolymer in (a) contains free carboxyl groups in number sufficient to render the copolymer water soluble under alkaline conditions.
Claim 4
Dependent Claim
101 words
An aqueous coating material in accordance with claim 2 wherein the copolymer in (a) is a copolymer of (i) at least one member selected from the group consisting of an unsaturated monocarboxylic acid and and an unsaturated dicarboxylic acid having up to 5 carbon atoms, and (ii) at least one water insoluble comonomer selected from the group consisting of esters of unsaturated copolymerizable carboxylic acids, unsaturated copolymerizable alcohols, vinyl aromatic compounds, unsaturated nitriles, unsaturated halides, and olefins without other functionality, which is copolymerizable with component (i) to form a copolymer which is capable of forming a dispersed closed phase in water.
Claim 5
Dependent Claim
45 words
An aqueous coating material in accordance with claim 3 wherein the copolymer also contains at least one water soluble comonomer which is a hydroxyalkyl ester of an unsaturated carboxylic acid, an N-substituted or unsubstituted amide of an unsaturated carboxylic acid, and other water-soluble copolymerizable components.
Claim 6
Dependent Claim
62 words
An aqueous coating material in accordance with claim 3 wherein the copolymer component (i) is one or more of the following: acrylic acid, methacrylic acid, itaconic acid, citraconic acid, crotonic acid, fumaric acid, maleic acid, an anhydride of one of the above dicarboxylic acids, and a half ester of one of the above dicarboxylic acids with a C 1 -C 6 alkanol.
Claim 7
Dependent Claim
35 words
An aqueous coating material in accordance with claim 3 wherein the quantity of component (i) in the polymer, calculated as acrylic acid, is in the range of from about 5 to about 35 wt. %.
Claim 8
Dependent Claim
24 words
An aqueous coating material in accordance with claim 6 wherein said range for component (i) is from about 10 to about 25 wt. %.
Claim 9
Dependent Claim
61 words
An aqueous coating material in accordance with claim 1 wherein the comonomer used to form the copolymer is at least one of the following: an ester of an unsaturated carboxylic acid, an ester of an unsaturated alcohol, an N-substituted amide of an unsaturated carboxylic acid, a vinyl aromatic compound, an unsaturated nitrile, an unsaturated halide, and an olefin without further functionality.
Claim 10
Dependent Claim
27 words
An aqueous coating material in accordance with claim 8 wherein the comonomer is selected from the group consisting of an alkyl (meth)-acrylate, a hydroxyalkyl(meth)-acrylate, styrene, and acrylonitrile.
Claim 11
Dependent Claim
28 words
An aqueous coating material in accordance with claim 7 wherein component (i) is at least one of crotonic acid and itaconic acid, and component (ii) is vinyl acetate.
Claim 12
Dependent Claim
27 words
An aqueous coating material in accordance with claim 1 wherein the copolymer in (a) contains from about 5 to about 60 wt. % of amino group-containing monomers.
Claim 13
Dependent Claim
39 words
An aqueous coating material in accordance with claim 11 wherein the amino group-containing monomers are at least one of the following: an amino group-containing ester of an unsaturated carboxylic acid, an amino group-containing amide of an unsaturated carboxylic acid.
Claim 14
Dependent Claim
46 words
An aqueous coating material in accordance with claim 11 wherein the amino group-containing monomer is at least one amino group-containing monomer of a compound selected from the group consisting of dimethylaminoethylacrylate, dimethylaminopropylacrylate, dimethylaminoneopentylacrylate, diethylaminoethylacrylate, diethylaminopropylacrylate, diethylaminoneopentylacrylate, and the methacrylate compound corresponding to any of the above.
Claim 15
Dependent Claim
71 words
An aqueous coating material in accordance with claim 1 wherein component (b) is selected from the group consisting of a mixture of paraffins, a mixture of isoparaffins, a carboxylic acid having more than 6 carbon atoms, an alcohol having more than 6 carbon atoms, an ether alcohol having more than 10 carbon atoms, an ester of said carboxylic acid, an ester of said alcohol, and an ester of said ether alcohol.
Claim 16
Dependent Claim
52 words
An aqueous coating material in accordance with claim 1 wherein component (b) contains at least one of the following: an ester of a naturally occurring straight or branched chain fatty acid with a C 1 -C 4 monoalcohol, and an ester of a dicarboxylic acid with a C 6 -C 8 alcohol.
Claim 17
Dependent Claim
22 words
An aqueous coating material in accordance with claim 15 wherein the ester of a dicarboxylic acid is an ester of phthalic acid.
Claim 18
Dependent Claim
17 words
An aqueous coating material in accordance with claim 1 wherein component (b) is a naturally occurring triglyceride.
Claim 19
Dependent Claim
69 words
An aqueous coating material in accordance with claim 1 wherein the nonionic emulsifying agent in (c) is at least one of the following: a reaction product of one mole of nonylphenol with from 2 to 7 moles of ethylene oxide; a reaction product of one mole of a fatty alcohol having more than 10 carbon atoms with from 2 to 8 moles of ethylene oxide; and a sorbitan ester.
Claim 20
Dependent Claim
77 words
An aqueous coating material in accordance with claim 1 wherein the copolymer in (a) is present in a quantity of from about 30 to about 60 wt. %, component (b) is present in a quantity of from about 5 to about 50 wt. %, and component (c) is present in a quantity of from about 0.05 to about 2.5 wt. %, all weight percents being based on the weight of the aqueous dispersion or emulsion in (a).
Claim 21
Dependent Claim
116 words
An aqueous coating material in accordance with claim 1 wherein the copolymer in (a) contains from about 5 to about 35 wt. % of carboxylic acid-containing monomers and at least one comonomer selected from the group consisting of an alkyl(meth)-acrylate, a hydroxyalkylacrylate, styrene, and acrylonitrile; component (b) is a "softening agent" having a melting point less than 10° C., and wherein the weight ratio of component (a): component (b) is between about 20:1 and about 20:10; and the nonionic emulsifying agent in (c) has an HLB-value between about 2 and about 10, and is present in a quantity of from about 1 to about 5 wt. %, based on the sum of components (a) and (b).
Claim 22
Dependent Claim
48 words
An aqueous coating material in accordance with claim 20 wherein the copolymer in (a) contains monomers, the homopolymer of which have relatively high glass temperatures, and monomers, the homopolymer of which have relatively low glass temperatures, in a weight ratio thereof of from about 4:1 to about 1:1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-09 | 1988-04-09 | 1988-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-09 | 1992-04-09 | 1992-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-09 | 1996-04-09 | 1996-10-09 | $7700.00 | Window Closed / Lapsed |