High voltage insulators
Assignee: Dow Silicones Corp
•
Filing: 1983-04-18
•
Granted: 1984-10-09
•
Expires: 2003-04-18
Abstract
Abstract A method of manufacturing an improved electrical high voltage coated insulator is described. The method involves applying and curing a one-part, room temperature curable silicone composition to the surface of an insulator, the insulator surface having a minimum designated arc resistance. The silicone composition is the product obtained by mixing in the substantial absence of moisture a specified polydimethylsiloxane fluid containing hydroxyl radicals, finely divided aluminum hydroxide filler, a silane of the formula R b Si(ON═X) 4-b and an optional condensation catalyst. The coating cures on exposure to atmospheric moisture to produce a surface adhered onto the insulator that resists the development of leakage currents and flashover failure upon exposure to electrical stress, moisture, contamination, and other outdoor weathering stresses.
Inventors
- 👤 Randolph G. Niemi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 17:22
CPC Classifications
H; H01; H01B; H01B19/00; H01B19/04; C; C08; C08L; C08L83/00; C08L83/04; H01B3/00; H01B3/18; H01B3/30; H01B3/46; C08G; C08G77/00; C08G77/04; C08G77/14; C08G77/16
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
302 words
A method of improving an electrical high voltage insulator comprising (I) applying to a high voltage insulator whose surface has arc resistance of at least 750 minutes when measured according to ASTM D-2303 at 2.5 KV, a smooth, coherent, coating of a one package, room temperature curable silicone composition wherein the composition comprises the product obtained by mixing in the substantial absence of moisture, (A) from 45 to 70 percent by weight of (1) 100 parts by weight of polydimethylsiloxane fluid of the formula Y(Me.sub.2 SiO).sub.a H in which Y is methyl or hydroxyl radical, at least 85 percent of Y are hydroxyl radicals, a has an average value such that the viscosity is in the range of from 5 to 20 Pa·s at 23° C., and Me is methyl radical and, (2) from 5 to 30 parts by weight of silane of the formula R.sub.b Si(ON═X).sub.4-b in which R is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals, X is selected from the group consisting of R 2 'C═ and ##STR4## radicals in which R' is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals and R" is selected from the group consisting of divalent hydrocarbon radicals and divalent halohydrocarbon radicals and b is an integer from 0 to 1 inclusive, (B) from 30 to 55 percent by weight of aluminum hydroxide having an average particle size of less than 5 micrometers, and the sum of (A) and (B) being 100 percent, (C) optionally, a non-reactive solvent, the product being storage stable in containers which exclude moisture, but which cures when exposed to moisture, then (II) exposing the coating to atmospheric moisture for a time sufficient to cure the coating to produce a bonded, elastomeric coating of at least 0.25 mm thickness.
Claim 2
Independent Claim
302 words
A method of improving an electrical high voltage insulator comprising (I) applying to a high voltage insulator whose surface has arc resistance of at least 750 minutes when measured according to ASTM D-2303 at 2.5 KV, a smooth, coherent, coating of a one package, room temperature curable silicone composition wherein the composition comprises the product obtained by mixing in the substantial absence of moisture, (A) from 45 to 70 percent by weight of (1) 100 parts by weight of polydimethylsiloxane fluid of the formula Y(Me.sub.2 SiO).sub.a H in which Y is methyl or hydroxyl radical, at least 85 percent of Y are hydroxyl radicals, a has an average value such that the viscosity is in the range of from 5 to 20 Pa·s at 23° C., and Me is methyl radical and, (2) from 5 to 30 parts by weight of silane of the formula R.sub.b Si(ON═X).sub.4-b in which R is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals, X is selected from the group consisting of R 2 'C═ and ##STR4## radicals in which R' is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals and R" is selected from the group consisting of divalent hydrocarbon radicals and divalent halohydrocarbon radicals and b is an integer from 0 to 1 inclusive, (B) from 30 to 55 percent by weight of aluminum hydroxide having an average particle size of less than 5 micrometers, and the sum of (A) and (B) being 100 percent, (C) optionally, a non-reactive solvent, the product being storage stable in containers which exclude moisture, but which cures when exposed to moisture, then (II) exposing the coating to atmospheric moisture for a time sufficient to cure the coating to produce a bonded, elastomeric coating of at least 0.25 mm thickness.
Claim 3
Dependent Claim
26 words
The method of claim 1 in which the silane is of the formula R.sub.b Si(ON═CR.sub.2 ').sub.4-b in which R and R' are each monovalent hydrocarbon radicals.
Claim 4
Dependent Claim
19 words
The method of claim 2 in which the silane is selected from the group consisting of methyltri(dimethylketoximo)silane and methyltri(methylethylketoximo)silane.
Claim 5
Dependent Claim
22 words
The method of claim 1 in which mixture (A) also contains a condensation catalyst consisting of a carboxylic acid salt of tin.
Claim 6
Dependent Claim
42 words
The method of claim 4 in which the amount of aluminum hydroxide (B) is in the range from 40 to 55 percent by weight and the viscosity of the polydimethylsiloxane is in the range from 10 to 15 Pa·s at 23° C.
Claim 7
Dependent Claim
51 words
The method of claim 1 in which (A) also contains up to 100 parts by weight of a polydimethylsiloxane fluid (3) of the formula Me(Me.sub.2 SiO).sub.c SiMe.sub.3 in which c has an average value such that the viscosity is greater than 0.05 Pa·s at 23° C. and Me is methyl radical.
Claim 8
Dependent Claim
26 words
The method of claim 1 in which the product obtained in mixing (A) and (B) is dispersed in a non-reactive solvent to yield a homogeneous mixture.
Claim 9
Dependent Claim
53 words
The method of claim 7 in which the polydimethylsiloxane fluid (1) and aluminum hydroxide (B) are combined into a homogeneous mixture, then heated for a time at a temperature sufficient to remove any free water, cooling, then slowly adding the solvent while mixing, then admixing the silane (2), to yield a homogeneous mixture.
Claim 10
Dependent Claim
38 words
The method of claim 8 in which the polydimethylsiloxane fluid (1) has a viscosity in the range from 10 to 15 Pa·s at 23° C., and (B) is in the range from 40 to 55 percent by weight.
Claim 11
Dependent Claim
13 words
The method of claim 1 in which the high voltage insulator is porcelain.
Claim 12
Dependent Claim
13 words
The method of claim 1 in which the high voltage insulator is glass.
Claim 13
Dependent Claim
17 words
The method of claim 1 in which the high voltage insulator is an organic resin or elastomer.
Claim 14
Dependent Claim
233 words
A composition suitable for coating the surface of a high voltage insulator comprising the product obtained by mixing in the substantial absence of moisture (A) from 45 to 70 percent by weight of (1) 100 parts by weight of polydimethylsiloxane fluid of the formula Y(Me.sub.2 SiO).sub.a H in which Y is methyl or hydroxyl radical, at least 85 percent of Y are hydroxyl radicals, a has an average value such that the viscosity is in the range of from 5 to 20 Pa·s at 23° C., and Me is methyl radical, and (2) from 5 to 30 parts by weight of silane of the formula R.sub.b Si(ON═X).sub.4-b in which R is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals, X is selected from the consisting of R 2 'C═ and ##STR5## radicals in which R' is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals and R" is selected from the group consisting of divalent hydrocarbon radicals and divalent halohydrocarbon radicals and b is an integer from 0 to 1 inclusive, (B) from 30 to 55 percent by weight of aluminum hydroxide having an average particle size of less than 5 micrometers, the sum of (A) and (B) being 100 percent, and (C) optionally, a non-reactive solvent, the product being storage stable in containers which exclude moisture, but which cures when exposed to moisture.
Claim 15
Dependent Claim
233 words
A composition suitable for coating the surface of a high voltage insulator comprising the product obtained by mixing in the substantial absence of moisture (A) from 45 to 70 percent by weight of (1) 100 parts by weight of polydimethylsiloxane fluid of the formula Y(Me.sub.2 SiO).sub.a H in which Y is methyl or hydroxyl radical, at least 85 percent of Y are hydroxyl radicals, a has an average value such that the viscosity is in the range of from 5 to 20 Pa·s at 23° C., and Me is methyl radical, and (2) from 5 to 30 parts by weight of silane of the formula R.sub.b Si(ON═X).sub.4-b in which R is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals, X is selected from the consisting of R 2 'C═ and ##STR5## radicals in which R' is selected from the group consisting of monovalent hydrocarbon radicals and monovalent halohydrocarbon radicals and R" is selected from the group consisting of divalent hydrocarbon radicals and divalent halohydrocarbon radicals and b is an integer from 0 to 1 inclusive, (B) from 30 to 55 percent by weight of aluminum hydroxide having an average particle size of less than 5 micrometers, the sum of (A) and (B) being 100 percent, and (C) optionally, a non-reactive solvent, the product being storage stable in containers which exclude moisture, but which cures when exposed to moisture.
Claim 16
Dependent Claim
57 words
The composition of claim 13 in which the (A) also contains up to 100 parts by weight of a polydimethylsiloxane fluid (3) of the formula Me(Me.sub.2 SiO).sub.c SiMe.sub.3 in which c is an average value such that the viscosity is in the range of from 5 to 20 Pa·s at 23° C. and Me is methyl radical.
Claim 17
Dependent Claim
72 words
The composition of claim 13 in which the polydimethylsiloxane fluid (1) has a viscosity in the range from 10 to 15 Pa·s at 23° C., the amount of (B) is in the range from 40 to 55 percent by weight, the silane is of the formula CH.sub.3 Si(ON═CR.sub.2 ').sub.3 wherein R' is methyl or ethyl, and the mixture (A) also contains a condensation catalyst consisting of a carboxylic acid salt of tin.
Claim 18
Dependent Claim
26 words
The composition of claim 13 in which the product obtained in mixing (A) and (B) is dispersed in a non-reactive solvent to yield a homogeneous mixture.
Claim 19
Dependent Claim
26 words
The composition of claim 15 in which the product obtained in mixing (A) and (B) is dispersed in a non-reactive solvent to yield a homogeneous mixture.
Claim 20
Dependent Claim
12 words
An electrical high voltage insulator produced by the method of claim 1.
Claim 21
Dependent Claim
12 words
An electrical high voltage insulator produced by the method of claim 6.
Claim 22
Dependent Claim
12 words
An electrical high voltage insulator produced by the method of claim 7.
References Cited (Backward Citations)
CA889898A
Cited
US3511698A
Cited
US4001128A
Cited
US4011168A
Cited
US3965065A
Cited
US4189392A
Cited
US4177322A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-09 | 1988-04-09 | 1988-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-09 | 1992-04-09 | 1992-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-09 | 1996-04-09 | 1996-10-09 | $7700.00 | Window Closed / Lapsed |