Cast polyester resin process and product

Claim 2

A process for producing a cast polyester resin comprising the steps in serial order: (a) formulating a mixture of liquid thermosetting unsaturated polyester resin, including cross-linking monomer and catalyst to form a blend; (b) subjecting said blend to a vacuum within predetermined parameters of time and quantum while concurrently vibrating and shearing said blend to rupture and release entrapped air bubbles; and, (c) vibrating said blend while it is in the mold to reincorporate devolved volatiles to form a matrix capable of setting and curing to form nonporous, machinable cast marble.

Claim 3

The process according to claim 1 wherein said vacuum, shearing and vibrating time of step (b) is about thirty minutes.

Claim 4

The process according to claim 1 wherein said vacuum of step (b) is in the range of fifteen to about thirty inches of mercury.

Claim 5

The process according to claim 1 wherein said shearing of step (b) is accomplished by subjecting said blend to a constantly changing horizontal plane.

Claim 6

The process according to claim 4 wherein said constantly changing horizontal plane is provided by rocking said blend over about a 60 degree arc.

Claim 7

The process according to claim 1 wherein shearing of step (b) is accomplished by subjecting said blend to passage through a baffle comprising a series of fingers placed in said blend perpendicular to said horizontal plane.

Claim 8

The process according to claim 1 wherein said process is performed as a batch process.

Claim 9

The process according to claim 1 wherein said process is performed as a continuous process.

Claim 10

The process according to claim 1 wherein said formulation to step (a) comprises about twenty to about forty weight percent of polyester resin characterized by a viscosity of from about 600 to about 3000 centipoise, and wherein said resin cross-linking monomer is styrene, and containing, additionally, a filler selected from the group consisting of calcium carbonate, glass frit, alumina trihydrate and combinations thereof and wherein said filler is from about seventy to about eighty weight percent and passes a three hundred twenty-five mesh and, further, wherein said formulation includes, as a catalyst, about one weight percent of fifty percent methyl ethyl ketone peroxide.

Claim 11

The process according to claim 9 wherein said mix includes, additionally, a defoaming agent and wherein before step (c) a pigment is added.

Claim 12

A process for pretreating castable polyester resin comprising the following serial steps: (a) formulating and blending a mixture of from about twenty to about thirty weight percent, twelve hundred centipoise liquid propylene glycol esterified with adipic and maleic anhydride, unsaturated polyester resin including styrene as a cross-linking monomer, from about seventy to about eighty weight of a filler selected from the group consisting of calcium carbonate and alumina trihydrate of about three hundred twenty-five mesh and no more than about two hundred parts per million by weight of dimethyl polysiloxane as a defoamer and about one weight percent of fifty percent methyl ethyl ketone peroxide as a catalyst; (b) subjecting said blend to a vacuum of from about fifteen to about twenty-five inches to mercury for about thirty minutes while concurrently rocking said blend by tilting said blend over a total of about a 60 degree arc as measured from a line perpendicular to said horizontal plane at about one to two cycles per minute, all while vibrating said blend at about two thousand to four thousand cycles per minute to rupture and release entrapped air bubbles to form a mold ready matrix; (c) introducing said matrix into a prepared mold; (d) vibrating said mold at from about two thousand to about four thousand cycles per minute for a period of about fifteen minutes to re-incorporate devolving styrene; and, (e) allowing said blend to set and cure to form a nonporous, machinable cast marble molded part.

Claim 13

A process for pretreating castable polyester resin comprising the following serial steps: (a) formulating and blending a mixture of from about twenty to about thirty weight percent, twelve hundred centipoise liquid propylene glycol esterified with adipic and maleic anhydride, unsaturated polyester resin including styrene as a cross-linking monomer, from about seventy to about eighty weight of a filler selected from the group consisting of calcium carbonate and alumina trihydrate of about three hundred twenty-five mesh and no more than about two hundred parts per million by weight of dimethyl polysiloxane as a defoamer and about one weight percent of fifty percent methyl ethyl ketone peroxide as a catalyst; (b) subjecting said blend to a vacuum of from about fifteen to about twenty-five inches to mercury for about thirty minutes while concurrently rocking said blend by tilting said blend over a total of about a 60 degree arc as measured from a line perpendicular to said horizontal plane at about one to two cycles per minute, all while vibrating said blend at about two thousand to four thousand cycles per minute to rupture and release entrapped air bubbles to form a mold ready matrix; (c) introducing said matrix into a prepared mold; (d) vibrating said mold at from about two thousand to about four thousand cycles per minute for a period of about fifteen minutes to re-incorporate devolving styrene; and, (e) allowing said blend to set and cure to form a nonporous, machinable cast marble molded part.

Claim 14

A cast polyester resin, said resin produced by: (a) formulating a mixture of liquid thermosetting unsaturated polyester resin, including cross-linking monomer and catalyst to form a blend; (b) subjecting said blend to a vacuum within predetermined parameters of time and quantum while concurrently vibrating and shearing said blend to rupture and release entrapped air bubbles; (c) molding said blend; (d) vibrating said blend while in the mold to reincorporate devolved volatiles; and, (e) allowing said blend to set and cure while in said mold to form thereby a nonporous, machinable cast marble.

Claim 15

A cast polyester resin, said resin produced by: (a) formulating a mixture of liquid thermosetting unsaturated polyester resin, including cross-linking monomer and catalyst to form a blend; (b) subjecting said blend to a vacuum within predetermined parameters of time and quantum while concurrently vibrating and shearing said blend to rupture and release entrapped air bubbles; (c) molding said blend; (d) vibrating said blend while in the mold to reincorporate devolved volatiles; and, (e) allowing said blend to set and cure while in said mold to form thereby a nonporous, machinable cast marble.

Claim 16

A cast polyester resin produced by the following serial steps: (a) formulating and blending a mixture of from about twenty to about thirty weight percent, twelve hundred centipoise liquid propylene glycol esterified with adipic and maleic anhydride, unsaturated polyester resin including styrene as a cross linking monomer, from about seventy to about eighty weight of a filler selected from the group consisting of calcium carbonate and alumina trihydrate of about three hundred twenty-five mesh, and no more than about two hundred parts per million by weight of dimethyl polysiloxane as a defoamer, and about one weight percent of fifty percent methyl ethyl ketone peroxide as a catalyst; (b) subjecting said blend to a vacuum of from about fifteen to about twenty-five inches of mercury for about thirty minutes while concurrently rocking said blend by tilting said blend over a total of about a 60 degree arc as measured from a line perpendicular to said horizontal plane at about one to two cycles per minute, all while vibrating said blend at about two thousand to four thousand cycles per minute to rupture and release entrapped air bubbles to form a mold ready matrix; (c) introducing said matrix into a prepared mold; (d) vibrating said mold at from about two thousand to about four thousand cycles per minute for a period of about fifteen minutes to re-incorporate devolving styrene; and, (e) allowing said blend to set and cure to form a nonporous, machine cast, molded part.

Claim 17

A cast polyester resin produced by the following serial steps: (a) formulating and blending a mixture of from about twenty to about thirty weight percent, twelve hundred centipoise liquid propylene glycol esterified with adipic and maleic anhydride, unsaturated polyester resin including styrene as a cross linking monomer, from about seventy to about eighty weight of a filler selected from the group consisting of calcium carbonate and alumina trihydrate of about three hundred twenty-five mesh, and no more than about two hundred parts per million by weight of dimethyl polysiloxane as a defoamer, and about one weight percent of fifty percent methyl ethyl ketone peroxide as a catalyst; (b) subjecting said blend to a vacuum of from about fifteen to about twenty-five inches of mercury for about thirty minutes while concurrently rocking said blend by tilting said blend over a total of about a 60 degree arc as measured from a line perpendicular to said horizontal plane at about one to two cycles per minute, all while vibrating said blend at about two thousand to four thousand cycles per minute to rupture and release entrapped air bubbles to form a mold ready matrix; (c) introducing said matrix into a prepared mold; (d) vibrating said mold at from about two thousand to about four thousand cycles per minute for a period of about fifteen minutes to re-incorporate devolving styrene; and, (e) allowing said blend to set and cure to form a nonporous, machine cast, molded part.