Coated phosphors, method for producing same and articles employing same
Assignee: Osram Sylvania Inc
•
Filing: 1982-02-12
•
Granted: 1984-09-25
•
Expires: 2002-02-12
Abstract
Abstract The red and blue color cathode ray tube phosphors for color television are pigmented with a coating of an aqueous-insoluble silicate-based glass matrix containing pigment particles. When incorporated into a tridot color cathode ray tube, the contrast of the tube is improved. The coated particles are formed by dispersing the particles in a slurry with a silicate, the pigment particles and an optional wetting agent, and evaporating the slurry to dryness. The dried coated particles are then heated in order to insolubilize the glass matrix, and soluble ions are then removed by washing.
Inventors
- 👤 Robert E. Dodds
- 👤 Carl E. Landmesser
- 👤 Henry B. Minnier
- 👤 Harry O. Schulze
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 19:40
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/02; C09K11/025; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
101 words
A composite article of manufacture comprising a phosphor particle and a coating on the surface of the particle, said coating including particles of a light modifying material, characterized in that said light modifying particles are supported by a matrix of a continuous aqueous-insoluble silicate-based glass selected from the group consisting of alkali metal silicate-based glass and ammonium silicate-based glass wherein said coating is formed by suspending the phosphor particles in a aqueous silicate solution, heating the suspension until substantial complete evaporation of the water thereby coating the phosphor particles, and then heating the coated phosphor particles to form a glass coating.
Claim 2
Dependent Claim
101 words
A composite article of manufacture comprising a phosphor particle and a coating on the surface of the particle, said coating including particles of a light modifying material, characterized in that said light modifying particles are supported by a matrix of a continuous aqueous-insoluble silicate-based glass selected from the group consisting of alkali metal silicate-based glass and ammonium silicate-based glass wherein said coating is formed by suspending the phosphor particles in a aqueous silicate solution, heating the suspension until substantial complete evaporation of the water thereby coating the phosphor particles, and then heating the coated phosphor particles to form a glass coating.
Claim 3
Dependent Claim
14 words
The article of claim 1 wherein the light modifying particles are inorganic pigment particles.
Claim 4
Dependent Claim
14 words
The article of claim 1 wherein the silicate glass is a potassium silicate-based glass.
Claim 5
Dependent Claim
14 words
The article of claim 1 wherein the phosphor particle is a cathode ray phosphor.
Claim 6
Dependent Claim
26 words
The article of claim 4 wherein the phosphor particle is selected from the group consisting of red, blue and green emitting color cathode ray tube phosphors.
Claim 7
Dependent Claim
123 words
An article of manufacture comprising a cathode ray tube faceplate and an array of elemental areas on the cathode ray tube faceplate, the areas comprising coated particles of a cathode ray phosphor distributed in a matrix of a photoresist, the particle coating containing particles of a light modifying material, characterized in that the light modifying particles are supported by a matrix of a continuous aqueous-insoluble silicate-based glass selected from the group consisting of alkali metal silicate-based glass and ammonium silicate-based glass wherein said coating is formed by suspending the phosphor particles in a aqueous silicate solution, heating the suspension until substantial complete evaporation of the water thereby coating the phosphor particles, and then heating the coated phosphor particles to form a glass coating.
Claim 8
Dependent Claim
123 words
An article of manufacture comprising a cathode ray tube faceplate and an array of elemental areas on the cathode ray tube faceplate, the areas comprising coated particles of a cathode ray phosphor distributed in a matrix of a photoresist, the particle coating containing particles of a light modifying material, characterized in that the light modifying particles are supported by a matrix of a continuous aqueous-insoluble silicate-based glass selected from the group consisting of alkali metal silicate-based glass and ammonium silicate-based glass wherein said coating is formed by suspending the phosphor particles in a aqueous silicate solution, heating the suspension until substantial complete evaporation of the water thereby coating the phosphor particles, and then heating the coated phosphor particles to form a glass coating.
Claim 9
Dependent Claim
14 words
The article of claim 6 wherein the light modifying particles are inorganic pigment particles.
Claim 10
Dependent Claim
14 words
The article of claim 6 wherein the silicate-based glass is a potassium silicate-based glass.
Claim 11
Dependent Claim
27 words
The article of claim 6 wherein the cathode ray phosphor particle is selected from the group of red, blue and green emitting color cathode ray tube phosphors.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-25 | 1988-03-26 | 1988-09-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-25 | 1992-03-26 | 1992-09-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-25 | 1996-03-26 | 1996-09-25 | $7700.00 | Window Closed / Lapsed |