Heterogeneous catalyst and process for its manufacture
Assignee: University of Toronto Innovations Foundation
•
Filing: 1982-12-15
•
Granted: 1984-09-18
•
Expires: 2002-12-15
Abstract
Abstract Catalysts for use in promoting heterogeneous chemical reactions, such as hydrogenation, cracking, dehydrogenation and Fischer-Tropsch reactions, are prepared by depositing a catalytically active metal such as nickel electrolytically onto an aluminum substrate in such a manner that the metal particles are deposited in micro-particulate form to enhance their catalytic activity. The aluminum substrate is prepared by cleaning and anodizing it, so as to deposit thereon an aluminum oxide surface film having micro porosity. Then the substrate is immersed into an electrolysis bath of solution of salt of the metal to be deposited, and subjected to alternating current electrolysis to cause the required deposition. Prior to use, the catalysts so prepared should be heated to remove absorbed gases from their porous surfaces.
Inventors
- 👤 Martin Moskovits
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 16:54
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/02; B01J37/024; B01J37/0244; B01J37/0215; B01J37/0225; B01J37/0226; B01J37/34; B01J37/348
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
137 words
A process for preparing catalysts useful in promoting heterogeneous catalytic chemical reactions, and comprising an aluminum or aluminum metal containing substrate having deposited thereon at least one metal selected from nickel, copper, cobalt, iron, manganese, titanium, vanadium, silver, gold, platinum, scandium, hafnium, niobium, chromium, molybdenum, zirconium, tungsten and palladium, said process including the steps of: cleaning the aluminum or aluminum metal containing substrate; anodizing the cleaned metal substrate, to produce a suitably pitted or porous oxide substrate surface; rinsing the anodized substrate, substantially to remove therefrom acid residues remaining from the anodizing step; subjecting the substrate in contact with a liquid solution of a salt of said at least one metal to electrolysis with alternating current, to deposit the metal onto the substrate in small-particle, catalytically active form; and removing excess liquid solution from the so-treated substrate.
Claim 2
Dependent Claim
137 words
A process for preparing catalysts useful in promoting heterogeneous catalytic chemical reactions, and comprising an aluminum or aluminum metal containing substrate having deposited thereon at least one metal selected from nickel, copper, cobalt, iron, manganese, titanium, vanadium, silver, gold, platinum, scandium, hafnium, niobium, chromium, molybdenum, zirconium, tungsten and palladium, said process including the steps of: cleaning the aluminum or aluminum metal containing substrate; anodizing the cleaned metal substrate, to produce a suitably pitted or porous oxide substrate surface; rinsing the anodized substrate, substantially to remove therefrom acid residues remaining from the anodizing step; subjecting the substrate in contact with a liquid solution of a salt of said at least one metal to electrolysis with alternating current, to deposit the metal onto the substrate in small-particle, catalytically active form; and removing excess liquid solution from the so-treated substrate.
Claim 3
Dependent Claim
11 words
The process of claim 1 wherein the substrate is aluminum foil.
Claim 4
Dependent Claim
37 words
The process of claim 2 wherein the process is conducted continuously by passing a continuous long length of aluminum foil through successive cleaning, anodizing, rinsing, AC-electrolyzing and final cleaning stations, with appropriate residence times in each station.
Claim 5
Dependent Claim
19 words
The process of claim 1, wherein the metal is nickel, deposited by AC-electrolysis from an aqueous nickel sulfate solution.
Claim 6
Dependent Claim
19 words
The process of claim 2, wherein the metal is nickel, deposited by AC-electrolysis from an aqueous nickel sulfate solution.
Claim 7
Dependent Claim
19 words
The process of claim 3, wherein the metal is nickel, deposited by AC-electrolysis from an aqueous nickel sulfate solution.
Claim 8
Dependent Claim
90 words
A catalyst for promoting heterogeneous catalytic chemical reactions, said catalyst comprising: a substrate of aluminum or aluminum alloy containing a high proportion of aluminum; at least one metal selected from nickel, copper, cobalt, iron, manganese, titanium, vanadium, silver, gold, platinum, scandium, hafnium, niobium, chromium, molybdenum, zirconium, tungsten and palladium; said at least one metal being present on the oxide surface of the substrate in discrete, micro-particulate form in pits and pores created in the substrate surface by anodizing thereof; said metal being in direct contact with atmosphere surrounding the substrate.
Claim 9
Dependent Claim
90 words
A catalyst for promoting heterogeneous catalytic chemical reactions, said catalyst comprising: a substrate of aluminum or aluminum alloy containing a high proportion of aluminum; at least one metal selected from nickel, copper, cobalt, iron, manganese, titanium, vanadium, silver, gold, platinum, scandium, hafnium, niobium, chromium, molybdenum, zirconium, tungsten and palladium; said at least one metal being present on the oxide surface of the substrate in discrete, micro-particulate form in pits and pores created in the substrate surface by anodizing thereof; said metal being in direct contact with atmosphere surrounding the substrate.
Claim 10
Dependent Claim
33 words
The catalyst of claim 7 wherein said at least one metal is deposited in pits and pores of an aluminum oxide surface layer deposited on the surface of the substrate by anodizing thereof.
Claim 11
Dependent Claim
27 words
The catalyst of claim 8 wherein the metal is deposited by AC-electrolysis of a solution of a salt of the metal in contact with the anodized substrate.
Claim 12
Dependent Claim
13 words
The catalyst of claim 7, wherein said at least one metal is nickel.
Claim 13
Dependent Claim
13 words
The catalyst of claim 8, wherein said at least one metal is nickel.
Claim 14
Dependent Claim
13 words
The catalyst of claim 9, wherein said at least one metal is nickel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-18 | 1988-03-19 | 1988-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-18 | 1992-03-19 | 1992-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-18 | 1996-03-19 | 1996-09-18 | $7700.00 | Window Closed / Lapsed |