US4472165A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for reduction of formaldehyde in resin-treated fabrics
Assignee: Air Products and Chemicals Inc
•
Filing: 1982-09-24
•
Granted: 1984-09-18
•
Expires: 2002-09-24
Abstract
Abstract A method for the removal of free formaldehyde from textile fabrics which have been treated with formaldehyde derived resins to make the fabrics crease-resistant is disclosed. The process comprises forming a composition composed of a foaming agent, ethylene urea and an appropriate diluent and then foaming this composition to form a stable foam. The foam is then applied to the resin treated fabric in a layer, the foam is collapsed on the fabric to force it through the fabric and then the fabric is subjected to drying and curing conditions. The process is advantageous in that it utilizes relatively small volumes of liquids and thus is energy efficient and environmentally favorable.
Inventors
- 👤 Razmic S. Gregorian
- 👤 Chettoor G. Namboodri
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 07:38
CPC Classifications
D; D06; D06M; D06M13/00; D06M13/10; D06M13/12; D06M13/127; D06M13/322; D06M13/402; D06M13/432; D06M15/00; D06M15/19; D06M15/37; D06M15/39; D06M15/423; D06M15/43; D06M15/433; D06M23/00; D06M23/04
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
124 words
A method for removing free formaldehyde from textile fabrics which have been treated with ureaformaldehyde type resins to render them crease and wrinkle-resistant comprising foaming a composition of a foaming agent, a formaldehyde scavenging agent, the concentration of the scavenging agent being in the range from about 0.5 to 10% by weight, and a diluent to a blow ratio in the range from about 2:1 to 30:1 and a foam density in the range from about 0.5 g/cc to 0.033 g/cc, applying a layer of the foam onto the resin treated fabric in an amount effective to chemically tie up the free formaldehyde thereon, and collapsing the foam to force it through the fabric, and then subjecting the fabric to drying and curing conditions.
Claim 2
Independent Claim
124 words
A method for removing free formaldehyde from textile fabrics which have been treated with ureaformaldehyde type resins to render them crease and wrinkle-resistant comprising foaming a composition of a foaming agent, a formaldehyde scavenging agent, the concentration of the scavenging agent being in the range from about 0.5 to 10% by weight, and a diluent to a blow ratio in the range from about 2:1 to 30:1 and a foam density in the range from about 0.5 g/cc to 0.033 g/cc, applying a layer of the foam onto the resin treated fabric in an amount effective to chemically tie up the free formaldehyde thereon, and collapsing the foam to force it through the fabric, and then subjecting the fabric to drying and curing conditions.
Claim 3
Dependent Claim
18 words
The method of claim 1 wherein the scavenger foam is applied to the fabric using a floating knife.
Claim 4
Dependent Claim
19 words
The method of claim 1 wherein the thickness of the foam layer is from about 5 to 50 mils.
Claim 5
Dependent Claim
13 words
The method of claim 1 wherein the foam is applied by horizontal padding.
Claim 6
Dependent Claim
29 words
The method of claim 1 wherein the amount of foam applied to the fabric produces a wet pick-up in the range from about 5 to 30 percent by weight.
Claim 7
Dependent Claim
18 words
The method of claim 5 wherein the wet pick-up is from about 10 to 20 percent by weight.
Claim 8
Dependent Claim
13 words
The method of claim 1 wherein the foam is collapsed by mechanical means.
Claim 9
Dependent Claim
34 words
The method of claim 1, 2, 3, 4, 5 or 6, wherein the fabric containing the scavenging agent is heated at a temperature from about 300°to 350° F. in the drying and curing step.
Claim 10
Dependent Claim
30 words
The method of claim 1 wherein the formaldehyde scavenger agent is selected from the group consisting of urea, ethylene urea, ethylene glycol, polyols, amides, hydrazides, sorbitol, carbohydrazide, and combinations thereof.
Claim 11
Dependent Claim
163 words
In a method for treating textile fabric to render the fabric crease and wrinkle-resistant wherein a urea-formaldehyde type resin is applied to the fabric and the thus treated fabric is then subjected to a heat treatment to cure the resin and dry the fabric, the improvement which comprises immediately after the heat treatment and while the fabric is still hot, applying a layer of a foam prepared by foaming a composition of a foaming agent, a formaldehyde scavenging agent, the concentration of the scavenging agent being in the range from about 0.5 to 10% by weight, and a diluent to a blow ratio in the range from about 2:1 to 30:1 and a foam density in the range from about 0.5 g/cc to 0.033 g/cc, in an amount effective to chemically tie up the free formaldehyde thereon, and collapsing the foam to force it through the fabric, wherein the heat retained by the fabric is sufficient to dry and cure the scavenging agent.
Claim 12
Dependent Claim
163 words
In a method for treating textile fabric to render the fabric crease and wrinkle-resistant wherein a urea-formaldehyde type resin is applied to the fabric and the thus treated fabric is then subjected to a heat treatment to cure the resin and dry the fabric, the improvement which comprises immediately after the heat treatment and while the fabric is still hot, applying a layer of a foam prepared by foaming a composition of a foaming agent, a formaldehyde scavenging agent, the concentration of the scavenging agent being in the range from about 0.5 to 10% by weight, and a diluent to a blow ratio in the range from about 2:1 to 30:1 and a foam density in the range from about 0.5 g/cc to 0.033 g/cc, in an amount effective to chemically tie up the free formaldehyde thereon, and collapsing the foam to force it through the fabric, wherein the heat retained by the fabric is sufficient to dry and cure the scavenging agent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-18 | 1988-03-19 | 1988-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-18 | 1992-03-19 | 1992-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-18 | 1996-03-19 | 1996-09-18 | $7700.00 | Window Closed / Lapsed |