Impact resistant polymer with improved flow characteristics
Assignee: Bayer Antwerpen NV
•
Filing: 1983-03-03
•
Granted: 1984-09-11
•
Expires: 2003-03-03
Abstract
Abstract An olefin copolymer rubber graft composition having a viscoelastic performance index of not greater than 100 as defined by the expression PI=(DSxMV)/i.v. where DS is the die swell of the composition, MV is the melt viscosity of the composition and i.v. is the intrinsic viscosity of a resinous portion extracted from the composition.
Inventors
- 👤 Paul G. Andersen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 15:43
CPC Classifications
C; C08; C08F; C08F255/00; C08F255/02; C08F255/04; C08F255/06
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
197 words
An impact resistant thermoplastic polymer composition with improved flow characteristics having a grafted olefin copolymer rubber portion and a resinous portion, said graft copolymer having been produced by graft copolymerizing monoethylenically unsaturated polymerizable resin-forming monomeric material on said rubber, and said composition having a viscoelastic performance index of not greater than 100 as defined by the expression DS×MV/i.v. where DS is the die swell of the composition expressed as the ratio of the extrudate diameter to the die diameter, MV is the melt viscosity of the composition expressed in poises ×10 -3 and i.v. is the intrinsic viscosity of the ungrafted resinous portion extracted from the composition expressed in deciliters per gram, the said die swell and melt viscosity being measured on a Sieglaff-McKelvey rheometer at a shear rate of 32 reciprocal seconds and at a temperature of 400° F., and the said intrinsic viscosity being measured in dimethyl formamide at 30° C., the said composition containing from 0 to 80% by weight of added separately prepared resin, said added resin having an intrinsic viscosity of from 0.55 to 1.0 in dimethyl formamide at 30° C., the overall rubber level being from 18 to 40% by weight.
Claim 2
Dependent Claim
197 words
An impact resistant thermoplastic polymer composition with improved flow characteristics having a grafted olefin copolymer rubber portion and a resinous portion, said graft copolymer having been produced by graft copolymerizing monoethylenically unsaturated polymerizable resin-forming monomeric material on said rubber, and said composition having a viscoelastic performance index of not greater than 100 as defined by the expression DS×MV/i.v. where DS is the die swell of the composition expressed as the ratio of the extrudate diameter to the die diameter, MV is the melt viscosity of the composition expressed in poises ×10 -3 and i.v. is the intrinsic viscosity of the ungrafted resinous portion extracted from the composition expressed in deciliters per gram, the said die swell and melt viscosity being measured on a Sieglaff-McKelvey rheometer at a shear rate of 32 reciprocal seconds and at a temperature of 400° F., and the said intrinsic viscosity being measured in dimethyl formamide at 30° C., the said composition containing from 0 to 80% by weight of added separately prepared resin, said added resin having an intrinsic viscosity of from 0.55 to 1.0 in dimethyl formamide at 30° C., the overall rubber level being from 18 to 40% by weight.
Claim 3
Dependent Claim
22 words
A composition as in claim 1 in which the olefin copolymer is an EPR bipolymer of terpolymer and the resin is styrene-acrylonitrile.
Claim 4
Dependent Claim
43 words
A composition as in claim 1 containing from 20 to 45% of added separately prepared resin, said added resin having an intrinsic viscosity of from 0.62 to 0.78 in dimethyl formamide at 30° C., the overall rubber level being from 20 to 30%.
Claim 5
Dependent Claim
21 words
A composition as in claims 1 or 3 in which the olefin copolymer rubber is EPDM and the resin is styrene-acrylonitrile.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-11 | 1988-03-12 | 1988-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-11 | 1992-03-12 | 1992-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-11 | 1996-03-12 | 1996-09-11 | $7700.00 | Window Closed / Lapsed |