US4471005A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ohmic contact to p-type Group III-V semiconductors
Assignee: Nokia Bell Labs
•
Filing: 1983-01-24
•
Granted: 1984-09-11
•
Expires: 2003-01-24
Abstract
Abstract A plurality of pairs of layers comprising gold and zinc are successively evaporated onto a p-type Group III-V semiconductor material such as indium phosphide. A final layer of gold is evaporated onto the pairs of layers prior to heating the multilayer contact. Successive layers of chromium and gold may be evaporated onto the final gold layer prior to the annealing step.
Inventors
- 👤 Chu-Liang Cheng
- 👤 Larry A. Coldren
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:52
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0116
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
114 words
A method of making an ohmic contact having a plurality of layers on a surface of a Group III-V semiconductor material of p-type conductivity, the method comprising the steps of depositing a first contact layer comprising gold onto the surface of the semiconductor material, depositing a second contact layer comprising a Group II metallic element over the first contact layer, depositing a third contact layer comprising gold over the second contact layer so that a total thickness for the contact is less than 2000 angstroms, and heating the semiconductor material and the plurality of layers to cause interdiffusion of the Group II metallic element at least partially into the surface of the semiconductor material.
Claim 2
Independent Claim
114 words
A method of making an ohmic contact having a plurality of layers on a surface of a Group III-V semiconductor material of p-type conductivity, the method comprising the steps of depositing a first contact layer comprising gold onto the surface of the semiconductor material, depositing a second contact layer comprising a Group II metallic element over the first contact layer, depositing a third contact layer comprising gold over the second contact layer so that a total thickness for the contact is less than 2000 angstroms, and heating the semiconductor material and the plurality of layers to cause interdiffusion of the Group II metallic element at least partially into the surface of the semiconductor material.
Claim 3
Dependent Claim
15 words
The method as defined in claim 1 wherein the Group II metallic element is zinc.
Claim 4
Dependent Claim
54 words
The method as defined in claim 2 wherein the thickness of the second layer is related to the sum of thicknesses for the first and third layers in a predetermined manner so that the contact has an overall composition in the range of 10 percent to 30 percent by weight of zinc in gold.
Claim 5
Dependent Claim
28 words
The method as defined in claim 3 wherein the thickness of the second layer is substantially equal to the sum of thicknesses for the first and third layers.
Claim 6
Dependent Claim
25 words
The method as defined in claim 3 wherein the contact has an overall composition substantially equal to 25 percent by weight of zinc in gold.
Claim 7
Dependent Claim
20 words
The method as defined in claim 4 wherein the second contact layer has a thickness of less than 200 angstroms.
Claim 8
Dependent Claim
20 words
The method as defined in claim 6 wherein the first contact layer has a thickness of less than 100 angstroms.
Claim 9
Independent Claim
129 words
A method of making an ohmic contact having a plurality of layers on a surface of a Group III-V semiconductor material of p-type conductivity, the method comprising the steps of depositing a first contact layer comprising gold onto the surface of the semiconductor material, depositing a second contact layer comprising a Group II metallic element over the first contact layer, depositing a third contact layer comprising gold over the second contact layer, depositing a fourth contact layer comprising the Group II metallic element over the third contact layer, depositing a fifth contact layer comprising gold over the fourth contact layer, and heating the semiconductor material and the plurality of layers to cause interdiffusion of the Group II metallic element at least partially into the surface of the semiconductor material.
Claim 10
Independent Claim
129 words
A method of making an ohmic contact having a plurality of layers on a surface of a Group III-V semiconductor material of p-type conductivity, the method comprising the steps of depositing a first contact layer comprising gold onto the surface of the semiconductor material, depositing a second contact layer comprising a Group II metallic element over the first contact layer, depositing a third contact layer comprising gold over the second contact layer, depositing a fourth contact layer comprising the Group II metallic element over the third contact layer, depositing a fifth contact layer comprising gold over the fourth contact layer, and heating the semiconductor material and the plurality of layers to cause interdiffusion of the Group II metallic element at least partially into the surface of the semiconductor material.
Claim 11
Dependent Claim
25 words
The method as defined in claim 8 wherein the plurality of layers of the contact have a total thickness which is less than 2000 angstroms.
Claim 12
Dependent Claim
15 words
The method as defined in claim 9 wherein the Group II metallic element is zinc.
Claim 13
Dependent Claim
61 words
The method as defined in claim 10 wherein a sum of thicknesses of the first, third and fifth contact layers is related to a sum of thicknesses for the second and fourth contact layers in a predetermined manner so that the contact has an overall composition in the range of 10 percent to 30 percent by weight of zinc in gold.
Claim 14
Dependent Claim
35 words
The method as defined in claim 11 wherein the sum of thicknesses of the first, third and fifth contact layers is substantially equal to the sum of thicknesses of the second and fourth contact layers.
Claim 15
Dependent Claim
25 words
The method as defined in claim 11 wherein the contact has an overall composition substantially equal to 25 percent by weight of zinc in gold.
Claim 16
Dependent Claim
33 words
A method as defined in claim 12 wherein the second contact layer has a thickness of less than 200 angstroms and the fourth contact layer has a thickness of less than 200 angstroms.
Claim 17
Dependent Claim
20 words
The method as defined in claim 14 wherein the first contact layer has a thickness of less than 100 angstroms.
Claim 18
Independent Claim
155 words
A method of making an ohmic contact having a plurality of layers on a surface of a Group III-V semiconductor material of p-type conductivity, the method comprising the steps of depositing a first contact layer comprising gold onto the surface of the semiconductor material, depositing a second contact layer comprising a Group II metallic element over the first contact layer, depositing a third contact layer comprising gold over the second contact layer, depositing a fourth contact layer comprising the Group II metallic element over the third contact layer, depositing a fifth contact layer comprising gold over the fourth contact layer, depositing a sixth contact layer comprising a transition metal over the fifth contact layer, depositing a seventh contact layer comprising gold over the sixth contact layer, and heating the semiconductor material and the plurality of layers to cause interdiffusion of the Group II metallic element at least partially into the surface of the semiconductor material.
Claim 19
Independent Claim
155 words
A method of making an ohmic contact having a plurality of layers on a surface of a Group III-V semiconductor material of p-type conductivity, the method comprising the steps of depositing a first contact layer comprising gold onto the surface of the semiconductor material, depositing a second contact layer comprising a Group II metallic element over the first contact layer, depositing a third contact layer comprising gold over the second contact layer, depositing a fourth contact layer comprising the Group II metallic element over the third contact layer, depositing a fifth contact layer comprising gold over the fourth contact layer, depositing a sixth contact layer comprising a transition metal over the fifth contact layer, depositing a seventh contact layer comprising gold over the sixth contact layer, and heating the semiconductor material and the plurality of layers to cause interdiffusion of the Group II metallic element at least partially into the surface of the semiconductor material.
Claim 20
Dependent Claim
24 words
The method as defined in claim 16 wherein a sum of thicknesses for the first through fifth contact layers is less than 2000 angstroms.
Claim 21
Dependent Claim
15 words
The method as defined in claim 17 wherein the Group II metallic element is zinc.
Claim 22
Dependent Claim
67 words
The method as defined in claim 18 wherein a sum of thicknesses of the first, third and fifth layers is related to a sum of thicknesses for the second and fourth layers in a predetermined manner so that the contact exclusive of the sixth and seventh contact layers has an overall composition in the range of 10 percent to 30 percent by weight of zinc in gold.
Claim 23
Dependent Claim
33 words
The method as defined in claim 19 wherein the sum of thicknesses of the first, third and fifth layers is substantially equal to the sum of thicknesses of the second and fourth layers.
Claim 24
Dependent Claim
33 words
The method as defined in claim 19 wherein the contact exclusive of the sixth and seventh contact layers has an overall composition substantially equal to 25 percent by weight of zinc in gold.
Claim 25
Dependent Claim
33 words
A method as defined in claim 20 wherein the second contact layer has a thickness of less than 200 angstroms and the fourth contact layer has a thickness of less than 200 angstroms.
Claim 26
Dependent Claim
20 words
The method as defined in claim 22 wherein the first contact layer has a thickness of less than 100 angstroms.
Claim 27
Dependent Claim
13 words
The method as defined in claim 23 wherein the transition metal is chromium.
Claim 28
Dependent Claim
13 words
The method as defined in claim 23 wherein the transition metal is titanium.
Claim 29
Dependent Claim
13 words
The method as defined in claim 23 wherein the transition metal is palladium.
References Cited (Backward Citations)
US3850688A
Cited
US3959036A
Cited
US3975555A
Cited
JPS5469975A
Cited
US4195308A
Cited
US4366186A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-11 | 1988-03-12 | 1988-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-11 | 1992-03-12 | 1992-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-11 | 1996-03-12 | 1996-09-11 | $7700.00 | Window Closed / Lapsed |