Paper having calcium sulfate mineral filler for use in the production of gypsum wallboard
Assignee: United States Gypsum Co
•
Filing: 1983-01-31
•
Granted: 1984-09-11
•
Expires: 2003-01-31
Abstract
Abstract A composite paper particularly adapted for use as cover sheets in the production of gypsum wallboard, the paper being sufficiently porous to permit better drainage and more rapid drying in the production of the paper, and when applied to the surfaces of a gypsum slurry for forming wallboard, permits less heat to be utilized in the wallboard conversion, thereby saving energy in the board production required for drying the board. The paper comprises in weight percent: (A) cellulosic fibers in an amount of from about 65% to about 90% and preferably having a fiber freeness of from about 300 ml to about 550 ml Canadian Standard Freeness, (B) calcium sulfate as a filler in an amount of from about 10% to about 35%, (C) a binder in an amount from about 1% to about 31/2%, (D) a flocculant in an amount of from about 0.1% to about 0.2%, (E) a buffering agent in an amount from about 0.25% to about 10%, (F) a neutral sizing agent in an effective amount to prevent water penetration, (G) an anionic polymer in an amount suitable for retaining said filler in said paper, and (H) a cationic starch when a succinic anhydride is used as the neutral sizing agent. In a preferred embodiment, after the paper is treated with a neutral internal sizing agent during its formation, it is subsequently treated with a surface sizing agent after formation of the paper, in order to provide certain properties including better adhesion to the gypsum core when used to make gypsum wallboard.
Inventors
- 👤 Norman E. Johnstone
- 👤 John R. Kehoe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:17
CPC Classifications
D; D21; D21H; D21H13/00; D21H13/36; D21H13/46; D21H11/00; D21H11/02; D21H11/04; D21H11/14; D21H13/38; D21H13/40; D21H17/00; D21H17/63; D21H17/67; D21H17/675; D21H21/00; D21H21/50; D21H21/52; E; E04; E04C; E04C2/00; E04C2/02; E04C2/04; E04C2/043; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31971; Y10T428/31993; Y10T428/31996
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
125 words
Gypsum wallboard comprising a core of set calcium sulfate dihydrate and a paper cover sheet bonded to each surface thereof, each of said paper cover sheets comprising: (A) a major proportion of cellulose fibers, (B) calcium sulfate as a filler in an amount of from about 10% to about 35% in dry weight, (C) a binder in an amount from about 1% to about 31/2%, (D) a neutral sizing agent in an effective amount to prevent water penetration, (E) a buffering agent comprising a salt of a cation of a strong base and an anion of a weak acid in an amount from about 0.25% to about 10%, and (F) an anionic retention aid in an amount suitable for retaining said filler in said paper.
Claim 2
Dependent Claim
125 words
Gypsum wallboard comprising a core of set calcium sulfate dihydrate and a paper cover sheet bonded to each surface thereof, each of said paper cover sheets comprising: (A) a major proportion of cellulose fibers, (B) calcium sulfate as a filler in an amount of from about 10% to about 35% in dry weight, (C) a binder in an amount from about 1% to about 31/2%, (D) a neutral sizing agent in an effective amount to prevent water penetration, (E) a buffering agent comprising a salt of a cation of a strong base and an anion of a weak acid in an amount from about 0.25% to about 10%, and (F) an anionic retention aid in an amount suitable for retaining said filler in said paper.
Claim 3
Dependent Claim
13 words
Gypsum wallboard according to claim 1, wherein said filler is calcium sulfate dihydrate.
Claim 4
Dependent Claim
14 words
Gypsum wallboard according to claim 2, wherein said retention aid is an anionic polymer.
Claim 5
Dependent Claim
14 words
Gypsum wallboard according to claim 3, wherein said anionic polymer is an anionic polyacrylamide.
Claim 6
Dependent Claim
66 words
Gypsum wallboard according to claim 3, wherein said neutral sizing agent is a cyclic dicarboxylic acid anhydride applied as an internal sizing agent having the structural formula: ##STR3## wherein R is selected from the group consisting of dimethylene and trimethylene radicals, and wherein R' is a hydrophobic group containing more than 5 carbon atoms selected from the group consisting of alkyl, alkenyl, aralkyl and aralkenyl groups.
Claim 7
Dependent Claim
27 words
Gypsum wallboard according to claim 5, wherein said cyclic dicarboxylic acid anhydride is a substituted succinic acid anhydride having a total of 15 to 20 carbon atoms.
Claim 8
Dependent Claim
27 words
Gypsum wallboard according to claim 5, wherein said substituted succinic acid anhydride is present in an amount of from about 0.15% to about 0.35% by dry weight.
Claim 9
Dependent Claim
18 words
Gypsum wallboard according to claim 5, wherein an emulsifying agent is added to said cyclic dicarboxylic acid anhydride.
Claim 10
Dependent Claim
24 words
Gypsum wallboard according to claim 2, wherein said neutral sizing agent has the following structural formula: ##STR4## wherein each R has 8-18 carbon atoms.
Claim 11
Dependent Claim
11 words
Gypsum wallboard according to claim 9, additionally containing a cationic polymer.
Claim 12
Dependent Claim
12 words
Gypsum wallboard according to claim 2, wherein said buffer is calcium carbonate.
Claim 13
Dependent Claim
25 words
Gypsum wallboard according to claim 11, wherein said calcium carbonate is present in an amount of from about 2% to about 10% by dry weight.
Claim 14
Dependent Claim
28 words
Gypsum wallboard according to claim 2, wherein a surface size coating comprising a silicone resin is applied to at least the surface of the bondliner of said paper.
Claim 15
Dependent Claim
27 words
Gypsum wallboard according to claim 13, wherein said surface size also includes an acidic agent in an amount suitable for promoting the polymerization of said silicone resin.
Claim 16
Dependent Claim
12 words
Gypsum wallboard according to claim 14, wherein said acidic agent is alum.
Claim 17
Dependent Claim
41 words
Gypsum wallboard according to claim 15, wherein said silicone resin is present in an amount of from about 0.015% to about 0.025%, and said alum is present in an amount of about 21/2 times the dry weight of said silicone resin.
Claim 18
Dependent Claim
15 words
Gypsum wallboard according to claim 13, wherein said silicone resin is a dimethyl polysiloxane resin.
Claim 19
Dependent Claim
173 words
Gypsum wallboard comprising a core of set calcium sulfate dihydrate and a paper cover sheet bonded to each surface thereof, each of said paper cover sheets comprising a composite paper which comprises in dry weight percent: (A) cellulosic fibers in an amount of from about 65% to about 90% and having a fiber freeness of from about 300 ml to 550 ml Canadian Standard Freeness, (B) a particulate mineral filler in an amount of from about 10% to about 35%, (C) a binder in an effective amount to retain said mineral filler, (D) a neutral sizing agent in an effective amount to prevent water penetration, and (E) an anionic polymer as a retention aid for said mineral filler, said paper being sufficiently porous to permit good drainage and rapid drying during its production, and when applied to the surfaces of a gypsum slurry for forming wallboard, permits less heat to be utilized in the wallboard conversion, the use of said paper thereby conserving energy both in paper production and in the board production.
Claim 20
Dependent Claim
173 words
Gypsum wallboard comprising a core of set calcium sulfate dihydrate and a paper cover sheet bonded to each surface thereof, each of said paper cover sheets comprising a composite paper which comprises in dry weight percent: (A) cellulosic fibers in an amount of from about 65% to about 90% and having a fiber freeness of from about 300 ml to 550 ml Canadian Standard Freeness, (B) a particulate mineral filler in an amount of from about 10% to about 35%, (C) a binder in an effective amount to retain said mineral filler, (D) a neutral sizing agent in an effective amount to prevent water penetration, and (E) an anionic polymer as a retention aid for said mineral filler, said paper being sufficiently porous to permit good drainage and rapid drying during its production, and when applied to the surfaces of a gypsum slurry for forming wallboard, permits less heat to be utilized in the wallboard conversion, the use of said paper thereby conserving energy both in paper production and in the board production.
Claim 21
Dependent Claim
13 words
Gypsum wallboard according to claim 18, wherein said binder is cationic potato starch.
Claim 22
Dependent Claim
13 words
Gypsum wallboard according to claim 18, wherein said mineral filler is calcium carbonate.
Claim 23
Dependent Claim
25 words
Gypsum wallboard according to claim 19, wherein said mineral filler is present in an amount of from about 25% to about 30% in dry weight.
Claim 24
Dependent Claim
14 words
Gypsum wallboard according to claim 19, wherein said retention aid is an anionic polyacrylamide.
Claim 25
Dependent Claim
137 words
Gypsum wallboard comprising a core of set calcium sulfate dihydrate and a paper cover sheet bonded to each surface thereof, each of said paper cover sheets comprising a composite paper which comprises in dry weight percent: (A) fibers in an amount of from about 65% to about 90% and having a fiber freeness of from about 300 ml to 550 ml Canadian Standard Freeness, (B) a particulate mineral filler in an amount of from about 10% to about 35%, (C) a binder in an effective amount to retain said mineral filler, (D) a cationic flocculant in an amount of from about 0.1% to about 0.2%, and (E) a neutral sizing agent in an effective amount to prevent water penetration, and having the following structural formula: ##STR5## wherein each radical R has from 8 to 18 carbon atoms.
Claim 26
Dependent Claim
137 words
Gypsum wallboard comprising a core of set calcium sulfate dihydrate and a paper cover sheet bonded to each surface thereof, each of said paper cover sheets comprising a composite paper which comprises in dry weight percent: (A) fibers in an amount of from about 65% to about 90% and having a fiber freeness of from about 300 ml to 550 ml Canadian Standard Freeness, (B) a particulate mineral filler in an amount of from about 10% to about 35%, (C) a binder in an effective amount to retain said mineral filler, (D) a cationic flocculant in an amount of from about 0.1% to about 0.2%, and (E) a neutral sizing agent in an effective amount to prevent water penetration, and having the following structural formula: ##STR5## wherein each radical R has from 8 to 18 carbon atoms.
Claim 27
Dependent Claim
13 words
Gypsum board according to claim 23, wherein said mineral filler is calcium carbonate.
Claim 28
Dependent Claim
13 words
Gypsum board according to claim 24, wherein said binder is a cationic starch.
Claim 29
Dependent Claim
21 words
Gypsum wallboard according to claim 1, additionally comprising a cationic flocculant in an amount of from about 0.1% to about 0.2%.
Claim 30
Dependent Claim
21 words
Gypsum wallboard according to claim 18, additionally comprising a cationic flocculant in an amount of from about 0.1% to about 0.2%.
Claim 31
Dependent Claim
23 words
Gypsum wallboard according to claim 23, additionally comprising an anionic retention aid in an amount suitable for retaining said filler in said paper.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-11 | 1988-03-12 | 1988-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-11 | 1992-03-12 | 1992-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-11 | 1996-03-12 | 1996-09-11 | $7700.00 | Window Closed / Lapsed |