Josephson device fabrication method
Assignee: Nokia Bell Labs
•
Filing: 1982-11-29
•
Granted: 1984-09-11
•
Expires: 2002-11-29
Abstract
Abstract A method for changing Josephson device parameters, e.g., the critical current of a Josephson junction. The method comprises incorporating doping material into the device, or part of the device, followed by a light anneal. Exemplary dopants include In, Sn, Sb, Te, Bi, Hg, Mg, Li, Cd, Na and Ta, with In, Sn, and Sb being preferred dopants for changing the critical current of a Josephson junction having a Pb-containing counter electrode. The dopant can be incorporated into the device by in-diffusion after deposition onto the surface, by ion implantation, or by any other convenient method. The amount of dopant required is typically small. For example, deposition of a Sn layer of 0.05 nm effective thickness onto the 200 nm thick Pb-Sb(1.5 wt. %) counter electrode of a cross-type Josephson junction, and annealing at 80 DEG C. for about 3 hours, resulted in an increase in the critical current of the junction by a factor of about 2.5. The method is considered to have wide applicability in the manufacture of Josephson devices, and can be applied globally, i.e., to all the devices on a wafer or chip, or locally, i.e., to selected devices.
Inventors
- 👤 Theodore A. Fulton
- 👤 Shin-Shem Pei
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:52
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0912; Y; Y10; Y10S; Y10S505/00; Y10S505/825; Y10S505/917; Y10S505/922
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
75 words
Method for producing a Josephson device comprising at least one Josephson junction, the method comprising (a) incorporating, subsequent to producing at least part of the device, an effective amount of dopant material into at least a part of the previously produced device part, and (b) maintaining at least the part of the device part at a reaction temperature above room temperature for a time effective for changing the value of at least one device parameter.
Claim 2
Dependent Claim
75 words
Method for producing a Josephson device comprising at least one Josephson junction, the method comprising (a) incorporating, subsequent to producing at least part of the device, an effective amount of dopant material into at least a part of the previously produced device part, and (b) maintaining at least the part of the device part at a reaction temperature above room temperature for a time effective for changing the value of at least one device parameter.
Claim 3
Dependent Claim
57 words
Method of claim 1, wherein the device parameter is the critical current, or the device parameter is the critical current density, or the device parameter is the quasi-particle resistance of the Josephson junction, or the device parameter is the inductance of a superconducting device component, or the device parameter is the resistivity of a normal device component.
Claim 4
Dependent Claim
27 words
Method of claim 2, wherein incorporating the dopant comprises depositing at least a part of the dopant material onto at least the surface of the device part.
Claim 5
Dependent Claim
27 words
Method of claim 2, wherein incorporating the dopant comprises implanting at least a part of the dopant material into at least the part of the device part.
Claim 6
Dependent Claim
31 words
Method of claim 2, wherein the dopant material consists essentially of material selected from the group consisting of In, Sn, Sb, Te, Bi, Au, Hg, Mg, Li, Cd, Na, and Ta.
Claim 7
Dependent Claim
16 words
Method of claim 2, wherein the Josephson device comprises at least one further superconducting device component.
Claim 8
Dependent Claim
16 words
Method of claim 2, wherein the Josephson device further comprises at least one normal device component.
Claim 9
Dependent Claim
21 words
Method of claim 2, wherein the Josephson device is a member of a multiplicity of Josephson devices formed on a substrate.
Claim 10
Dependent Claim
41 words
Method of claim 8, wherein, prior to incorporating the dopant, at least a part of at least one member of the multiplicity of devices is covered with a patterned masking layer, thereby substantially preventing incorporation of dopant into the covered part.
Claim 11
Dependent Claim
139 words
Method for fabricating a Josephson device comprising at least one Josephson junction, the junction comprising a superconducting base electrode and a superconducting counter electrode, at least a part of the counter electrode overlying at least a part of the base electrode, with a nonsuperconducting layer comprising a tunnel barrier region separating the base electrode and the counter electrode, at least the counter electrode comprising Pb, the method comprising (a) incorporating into at least the counter electrode an effective amount of dopant consisting essentially of material selected from the group consisting of In, Sn, Sb, Te, Bi, Au, Hg, Mg, Li, Cd, and Na, and (b) maintaining at least the counter electrode at a temperature above room temperature but not greater than about 200° C. for a time effective to produce a change in the current-voltage characteristic of the junction.
Claim 12
Dependent Claim
139 words
Method for fabricating a Josephson device comprising at least one Josephson junction, the junction comprising a superconducting base electrode and a superconducting counter electrode, at least a part of the counter electrode overlying at least a part of the base electrode, with a nonsuperconducting layer comprising a tunnel barrier region separating the base electrode and the counter electrode, at least the counter electrode comprising Pb, the method comprising (a) incorporating into at least the counter electrode an effective amount of dopant consisting essentially of material selected from the group consisting of In, Sn, Sb, Te, Bi, Au, Hg, Mg, Li, Cd, and Na, and (b) maintaining at least the counter electrode at a temperature above room temperature but not greater than about 200° C. for a time effective to produce a change in the current-voltage characteristic of the junction.
Claim 13
Dependent Claim
30 words
Method of claim 10, wherein the time is less than about 10 hours and the counter electrode is maintained at a temperature between about 50° C. and about 150° C.
Claim 14
Dependent Claim
22 words
Method of claim 10, wherein the amount of dopant corresponds to a dopant layer having an effective thickness less than 10 nm.
Claim 15
Dependent Claim
22 words
Method of claim 10, wherein the dopant material consists essentially of material selected from the group consisting of Sn, Sb, and In.
Claim 16
Dependent Claim
21 words
Method of claim 10, wherein at least part of the dopant material is incorporated into the counter electrode by ion implantation.
Claim 17
Dependent Claim
23 words
Method of claim 14, wherein the ion implantation has a projected range in the electrode less than about 50% of the electrode thickness.
Claim 18
Dependent Claim
25 words
Method of claim 10, wherein incorporating the dopant comprises depositing at least a part of the dopant material onto the surface of the counter electrode.
Claim 19
Dependent Claim
10 words
Method of claim 16, wherein depositing is by vapor deposition.
Claim 20
Dependent Claim
33 words
Method of claim 10, wherein the change in the voltage-current characteristic comprises a change in the critical current, or a change in the critical current density, or a change in the quasi-particle resistance.
Claim 21
Dependent Claim
21 words
Method of claim 10, wherein the Josephson junction is a member of a multiplicity of Josephson junctions formed on a substrate.
Claim 22
Dependent Claim
41 words
Method of claim 19, wherein, prior to incorporating the dopant, at least a part of at least one member of the multiplicity of junctions is covered with a patterned masking layer, thereby substantially preventing incorporation of dopant into the covered part.
References Cited (Backward Citations)
US3521133A
Cited
US3897276A
Cited
US3966501A
Cited
US4050967A
Cited
US4263603A
Cited
US4176365A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-11 | 1988-03-12 | 1988-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-11 | 1992-03-12 | 1992-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-11 | 1996-03-12 | 1996-09-11 | $7700.00 | Window Closed / Lapsed |