Method of preparing an electrode backing layer
Assignee: Diamond Shamrock Chemicals Co
•
Filing: 1982-12-20
•
Granted: 1984-08-28
•
Expires: 2002-12-20
Abstract
Abstract This disclosure is directed to the preparation of a self-sustaining hydrophobic backing layer which also possesses excellent electrical conductivity so that it can serve as an intermediate layer between the current distributor and the active layer of a complete oxygen cathode. Said backing layer is formed by a simple process in which an intimate liquid dispersion containing finely divided carbon black and not more than equal parts by weight of PTFE particles ranging in size from about 0.05 to about 0.5 microns is dewatered and shaped into a thin layer which is thereafter lightly pressed and consolidated at elevated temperatures. Preferably, the carbon black is an acetylene black of a particle size range between 50 and 3000 Angstroms and the weight proportion of same is greater than the PTFE.
Inventors
- 👤 Frank Solomon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:00
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/88; H01M4/8817; H01M4/8821; C; C25; C25B; C25B11/00; C25B11/04; C25B11/042; C25B11/043; H01M4/8803; H01M4/8807; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
158 words
A method for preparing an electrically conductive, hydrophobic, gas permeable, cohesive, self-sustaining wetproofing sheet for use in forming an oxygen cathode, comprising: (a) introducing a fine particle sized carbon black into water to form a first dispersion thereof, (b) introducing polytetrafluoroethylene particles of about 0.05 to 0.5 microns into water containing a wetting agent agent to form a second dispersion thereof, (c) mixing said first dispersion with said second dispersion to form a third dispersion, (d) filtering said third dispersion to obtain a wet mass of mixed particles, (e) heating said wet mass to produce a dried mass containing said carbon black, and polytetrafluoroethylene particles and residual wetting agent, (f) removing said residual wetting agent from said mass by solvent extraction and/or further heating, (g) chopping said mass to form it into a granular mix, and (h) introducing said granular mix between pressing rollers heated to about 65° to 95° C. to form same into said wet-proofing sheet.
Claim 2
Independent Claim
158 words
A method for preparing an electrically conductive, hydrophobic, gas permeable, cohesive, self-sustaining wetproofing sheet for use in forming an oxygen cathode, comprising: (a) introducing a fine particle sized carbon black into water to form a first dispersion thereof, (b) introducing polytetrafluoroethylene particles of about 0.05 to 0.5 microns into water containing a wetting agent agent to form a second dispersion thereof, (c) mixing said first dispersion with said second dispersion to form a third dispersion, (d) filtering said third dispersion to obtain a wet mass of mixed particles, (e) heating said wet mass to produce a dried mass containing said carbon black, and polytetrafluoroethylene particles and residual wetting agent, (f) removing said residual wetting agent from said mass by solvent extraction and/or further heating, (g) chopping said mass to form it into a granular mix, and (h) introducing said granular mix between pressing rollers heated to about 65° to 95° C. to form same into said wet-proofing sheet.
Claim 3
Dependent Claim
20 words
The method of claim 1 wherein fibers are introduced into one of said dispersions in steps (a), (b) or (c).
Claim 4
Dependent Claim
12 words
The method of claim 2 wherein said fibers are carbon graphite fibers.
Claim 5
Independent Claim
234 words
A method for preparing an electrically conductive, hydrophobic, gas permeable, cohesive, self-sustaining wet proofing sheet for use in forming an oxygen cathode, comprising: (a) introducing a fine particle sized carbon black into water to form a first dispersion thereof, (b) introducing polytetrafluoroethylene particles of about 0.05 to 0.5 microns into water containing a wetting agent to form a second dispersion thereof, (c) mixing said first dispersion with said second dispersion to form a third dispersion, (d) filtering said third dispersion to obtain a wet mass of mixed particles, (e) washing said wet mass with alcohol to render it substantially water-free and with some residual wetting agent, (f) dispersing said substantially water-free mass in alcohol, (g) filtering the resultant dispersion in alcohol from step (f) through a salt bed deposited on a flat filter to form thereon a layer of said mixed particles including some residual wetting agent, (h) heating and drying said layer and said filter, (i) washing said dried layer and filter with water to remove said filter from said layer and to clean said layer of salt, leaving a salt-free layer of said mixed particles, (j) heating and drying said salt-free layer, (k) heating said layer to a temperature higher than in step (j) to drive off said wetting agent, and (1) pressing said layer at elevated pressure and temperature to bond and form the mixed particles therein into said wetproofing sheet.
Claim 6
Independent Claim
234 words
A method for preparing an electrically conductive, hydrophobic, gas permeable, cohesive, self-sustaining wet proofing sheet for use in forming an oxygen cathode, comprising: (a) introducing a fine particle sized carbon black into water to form a first dispersion thereof, (b) introducing polytetrafluoroethylene particles of about 0.05 to 0.5 microns into water containing a wetting agent to form a second dispersion thereof, (c) mixing said first dispersion with said second dispersion to form a third dispersion, (d) filtering said third dispersion to obtain a wet mass of mixed particles, (e) washing said wet mass with alcohol to render it substantially water-free and with some residual wetting agent, (f) dispersing said substantially water-free mass in alcohol, (g) filtering the resultant dispersion in alcohol from step (f) through a salt bed deposited on a flat filter to form thereon a layer of said mixed particles including some residual wetting agent, (h) heating and drying said layer and said filter, (i) washing said dried layer and filter with water to remove said filter from said layer and to clean said layer of salt, leaving a salt-free layer of said mixed particles, (j) heating and drying said salt-free layer, (k) heating said layer to a temperature higher than in step (j) to drive off said wetting agent, and (1) pressing said layer at elevated pressure and temperature to bond and form the mixed particles therein into said wetproofing sheet.
Claim 7
Dependent Claim
21 words
The method of claim 4 wherein fibers are introduced into one of the dispersions in steps (a), (b), (c) or (f).
Claim 8
Dependent Claim
12 words
The method of claim 5 wherein said fibers are carbon graphite fibers.
Claim 9
Dependent Claim
23 words
The method of claim 4 or 5 wherein said salt bed is produced from an equimolar mixture of sodium carbonate and sodium bicarbonate.
Claim 10
Dependent Claim
32 words
The method of claim 1 or 2 or 4 or 5 wherein said carbon black partical size is about 50-3000 Angstroms and its true density is about 1.95 grams per cubic centimeter.
Claim 11
Dependent Claim
23 words
An electrically conductive, hydrophobic, gas permeable, cohesive, self-sustaining wetproofing sheet produced by the method of claim 1 or 2 or 4 or 5.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-28 | 1988-02-27 | 1988-08-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-28 | 1992-02-27 | 1992-08-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-28 | 1996-02-27 | 1996-08-28 | $7700.00 | Window Closed / Lapsed |