Abstract In a batch process for the treatment of the surface of a solid polymeric material by a gas reactive therewith comprising the following steps: (a) providing a closed system comprising a chamber; (b) introducing the material into the chamber; (c) heating the chamber and the material to a selected temperature in the range of about 100° F. to about 200° F.; (d) evacuating the system; (e) introducing the reactive gas into the system in an amount (i) of up to about 10 percent in excess of the theoretical amount of gas required to react with the surface of the polymeric material to a desired depth and (ii) sufficient to provide a partial pressure in the system in the range of about 0.1 psia to about 3 psia; (f) introducing an inert gas into the system in an amount sufficient to provide a total pressure in the system or about one atmosphere; (g) maintaining the selected temperature for a period of time sufficient for the reaction to take place between the gas and the surface; (h) evacuating the system; (i) introducing air into the system to provide about atmospheric pressure; and (j) removing the material, the improvement comprising carrying out the following step prior to step (c): providing an electrostatic charge on the surface of the solid polymer material in such a manner that the charge is maintained throughout steps (c) through (g).
Inventors
👤 Gregorio Tarancon
Bibliographic Details
Application Number—
JurisdictionUS
Data Sourcegoogle_patents
Last Synchronized2026-11-08 10:58
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J7/126
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
233 words
In a batch process for the treatment of the surface of a solid polymeric material by a gas reactive therewith comprising the following steps: (a) providing a closed system comprising a chamber; (b) introducing the material into the chamber; (c) heating the chamber and the material to a selected temperature in the range of about 100° F. to about 200° F.; (d) evacuating the system; (e) introducing the reactive gas into the system in an amount (i) of up to about 10 percent in excess of the theoretical amount of gas required to react with the surface of the polymeric material to a desired depth and (ii) sufficient to provide a partial pressure in the system in the range of about 0.1 psia to about 3 psia; (f) introducing an inert gas into the system in an amount sufficient to provide a total pressure in the system of about one atmosphere; (g) maintaining the selected temperature for a period of time sufficient for the reaction to take place between the gas and the surface; (h) evacuating the system; (i) introducing air into the system to provide about atmospheric pressure; and (j) removing the material, the improvement comprising carrying out the following step prior to step (c): providing an electrostatic charge on the surface of the solid polymer material by contact or induction manner that the charge ia maintained throughout steps (c) through (g).
Claim 2
Dependent Claim
233 words
In a batch process for the treatment of the surface of a solid polymeric material by a gas reactive therewith comprising the following steps: (a) providing a closed system comprising a chamber; (b) introducing the material into the chamber; (c) heating the chamber and the material to a selected temperature in the range of about 100° F. to about 200° F.; (d) evacuating the system; (e) introducing the reactive gas into the system in an amount (i) of up to about 10 percent in excess of the theoretical amount of gas required to react with the surface of the polymeric material to a desired depth and (ii) sufficient to provide a partial pressure in the system in the range of about 0.1 psia to about 3 psia; (f) introducing an inert gas into the system in an amount sufficient to provide a total pressure in the system of about one atmosphere; (g) maintaining the selected temperature for a period of time sufficient for the reaction to take place between the gas and the surface; (h) evacuating the system; (i) introducing air into the system to provide about atmospheric pressure; and (j) removing the material, the improvement comprising carrying out the following step prior to step (c): providing an electrostatic charge on the surface of the solid polymer material by contact or induction manner that the charge ia maintained throughout steps (c) through (g).
Claim 3
Dependent Claim
38 words
The process defined in claim 1 wherein the temperature range in step (c) is about 120° F. to about 180° F. and the percent in excess of gas in step (e) (i) is up to about 5 percent.
Claim 4
Dependent Claim
18 words
The process defined in claim 1 wherein the gas is fluorine or a mixture of fluorine and bromine.
Claim 5
Dependent Claim
18 words
The process defined in claim 2 wherein the gas is fluorine or a mixture of fluorine and bromine.