Process for the pretreatment of a polyolefin product before coating
Assignee: Toyoda Gosei Co Ltd
•
Filing: 1981-06-26
•
Granted: 1984-08-14
•
Expires: 2001-06-26
Abstract
Abstract A process for the pretreatment of a polyolefin product before coating consisting essentially of the steps of treating the surface of the polyolefin product before coating using an organic solvent having a solubility parameter (SP value) equal or similar to that of the polyolefin and subsequently applying a plasma treating thereto in the presence of an active gas by microwave treating the active gas under vacuum. As a result of the process, the surface of the polyolefin product is activated and the adhesion of the coating film is improved.
Inventors
- 👤 Katsuhide Manabe
- 👤 Yutaka Sato
- 👤 Ryoichi Muroi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 11:55
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J7/123; B; B05; B05D; B05D3/00; B05D3/04; B05D3/0466; B05D3/0473; B05D3/10; B05D3/101; B05D3/14; B05D3/141; B05D3/142; B05D3/144; C08J7/02; C08J7/04; C08J7/0427; C08J7/043; B05D2201/00; C08J2323/00; C08J2323/02; C08J2433/00; C08J2433/04; C08J2433/06; C08J2433/08; H; H05; H05K; H05K3/00; H05K3/38; H05K3/381
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
74 words
A process for the pretreatment of a polyolefin product before coating, said process consisting essentially of steps of treating the surface of the polyolefin product before coating using an organic solvent having a solubility parameter (SP value) equal or similar to that of the polyolefin and subsequently applying a plasma treating thereto in the presence of an active gas, wherein said plasma treating is conducted by microwave treating an active gas under a vacuum.
Claim 2
Dependent Claim
74 words
A process for the pretreatment of a polyolefin product before coating, said process consisting essentially of steps of treating the surface of the polyolefin product before coating using an organic solvent having a solubility parameter (SP value) equal or similar to that of the polyolefin and subsequently applying a plasma treating thereto in the presence of an active gas, wherein said plasma treating is conducted by microwave treating an active gas under a vacuum.
Claim 3
Dependent Claim
40 words
A process for the pretreatment of a polyolefin product before coating according to claim 1, wherein said polyolefin product is selected from the group consisting of polyethylene homopolymer, ethylene vinylacetate copolymer, ethylene acrylate copolymer, polypropylene homopolymer and ethylene propylene copolymer.
Claim 4
Dependent Claim
53 words
A process for the pretreatment of a polyolefin product before coating according to claim 2, wherein said treating using an organic solvent is vapor treating using an organic solvent of a chlorine compound selected from the group consisting of trichloroethylene, trichloroethane, dichloroethane, ethyl chloride, pentachloroethylene, tetrachloroethylene, methylene chloride, ethylene dichloride and acetyl chloride.
Claim 5
Dependent Claim
45 words
A process for the pretreatment of a polyolefin product before coating according to claim 2, wherein said treating using an organic solvent is vapor treating using an organic solvent of an aromatic compound selected from the group consisting of benzene, toluene, xylene, chlorotoluene and chlorobenzene.
Claim 6
Dependent Claim
43 words
A process for the pretreatment of a polyolefin product before coating according to claim 3 or 4, wherein said active gas is selected from the group consisting of O 2 , Br 2 , NH 3 , O 3 and Cl 2 .
Claim 7
Dependent Claim
60 words
A process for the pretreating of a polyolefin product before coating according to claim 5, wherein said plasma treating is conducted in an apparatus wherein the active gas is microwave treated at a microwave output of 0.2˜3.0 Kw and an oscillation frequency of 2,450±50 MHz under a degree of vacuum of 0.1˜1.0 Torr, for a treating time of 10˜30 seconds.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-14 | 1988-02-13 | 1988-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-14 | 1992-02-13 | 1992-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-14 | 1996-02-13 | 1996-08-14 | $7700.00 | Window Closed / Lapsed |