US4465568A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Electrochemical production of KNO3 /NaNO3 salt mixture
Assignee: Olin Corp
•
Filing: 1981-11-16
•
Granted: 1984-08-14
•
Expires: 2001-11-16
Abstract
Abstract A process for the electrolytic production of a chloride-free mixture consisting essentially of sodium and potassium nitrates is disclosed. In this process, an anolyte brine comprised of a mixture of sodium and potassium chlorides dissolved therein is electrolyzed in a membrane type electrolysis type cell to produce a mixed alkali metal hydroxide catholyte solution. The catholyte is reacted with nitric acid to form a mixed potassium-sodium nitrate solution. By properly adjusting the ratio of potassium chloride to sodium chloride concentration in the anolyte brine, a final nitrate product containing about from about 40% to about 80% NaNO 3 and from about 60% to about 20% KNO 3 by weight can be produced. The resulting product, after drying is suitable for use in many solar panel heat transfer applications.
Inventors
- 👤 Ronald L. Dotson
- 👤 Ronald C. Miles
- 👤 Larry D. Carpenter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 23:03
CPC Classifications
C; C25; C25B; C25B1/00; C25B1/01; C25B1/14; C09; C09K; C09K5/00; C09K5/08; C09K5/10; C09K5/12; Y; Y02; Y02P; Y02P20/00; Y02P20/10; Y02P20/133
Claims Analysis
Total Claims: 50
Claim 1
Independent Claim
113 words
A process for producing a mixture consisting essentially of sodium nitrate and potassium nitrate, which comprises: (a) feeding a brine comprised of a mixture of sodium chloride and potassium chloride to the anolyte compartment of an electrolytic cell having an anolyte compartment and a catholyte compartment sealingly separated by a permselective cation exchange hydraulically impermeable membrane; (b) electrolyzing said brine to produce a catholyte solution comprised of a mixture of sodium hydroxide and potassium hydroxide, said catholyte solution being substantially free of chloride ions; (c) withdrawing said catholyte solution from said catholyte compartment; and (d) reacting said catholyte solution with nitric acid to produce a mixture of sodium nitrate and potassium nitrate therefrom.
Claim 2
Dependent Claim
113 words
A process for producing a mixture consisting essentially of sodium nitrate and potassium nitrate, which comprises: (a) feeding a brine comprised of a mixture of sodium chloride and potassium chloride to the anolyte compartment of an electrolytic cell having an anolyte compartment and a catholyte compartment sealingly separated by a permselective cation exchange hydraulically impermeable membrane; (b) electrolyzing said brine to produce a catholyte solution comprised of a mixture of sodium hydroxide and potassium hydroxide, said catholyte solution being substantially free of chloride ions; (c) withdrawing said catholyte solution from said catholyte compartment; and (d) reacting said catholyte solution with nitric acid to produce a mixture of sodium nitrate and potassium nitrate therefrom.
Claim 3
Dependent Claim
28 words
The process of claim 1 wherein sufficient nitric acid is reacted with said catholyte to adjust the pH to within the range from about 5.0 to about 7.5.
Claim 4
Dependent Claim
28 words
The process of claim 2 wherein sufficient nitric acid is reacted with said catholyte to adjust the pH to within the range from about 6.0 to about 6.5.
Claim 5
Dependent Claim
85 words
A process for producing a mixture consisting essentially of sodium and potassium hydroxides which comprises: (a) feeding a brine comprised of a mixture of sodium chloride and potassium chloride to the anolyte compartment of an electrolytic cell having an anolyte compartment and a catholyte compartment sealingly separated by a permselective, cation exchange hydraulically impermeable membrane, and (b) electrolyzing said brine to produce a catholyte solution comprised of a mixture of sodium hydroxide and a potassium hydroxide, said catholyte solution being substantially free of chloride ions.
Claim 6
Dependent Claim
85 words
A process for producing a mixture consisting essentially of sodium and potassium hydroxides which comprises: (a) feeding a brine comprised of a mixture of sodium chloride and potassium chloride to the anolyte compartment of an electrolytic cell having an anolyte compartment and a catholyte compartment sealingly separated by a permselective, cation exchange hydraulically impermeable membrane, and (b) electrolyzing said brine to produce a catholyte solution comprised of a mixture of sodium hydroxide and a potassium hydroxide, said catholyte solution being substantially free of chloride ions.
Claim 7
Dependent Claim
24 words
The process of claims 1 or 4 wherein said electrolysis is performed in a cell temperature range from about 70° to about 100° C.
Claim 8
Dependent Claim
18 words
The process of claim 5 wherein said electrolysis cell temperature is between about 80° and about 90° C.
Claim 9
Dependent Claim
35 words
The process of claims 1 or 4 wherein the total concentration of said dissolved sodium chloride and potassium chloride in said brine is in the range from about 200 grams/liter to a substantially saturated solution.
Claim 10
Dependent Claim
20 words
The process of claim 7 wherein said concentration is in the range of from about 300 to about 400 grams/liter.
Claim 11
Dependent Claim
31 words
The process of claim 7 wherein the potassium chloride in said brine is in the range from about 15% to about 45% by weight of the salts dissolved in said brine.
Claim 12
Dependent Claim
29 words
The process of claim 9 wherein the range of potassium chloride in said brine is from about 20% to 35% by weight of the salts dissolved in said brine.
Claim 13
Dependent Claim
29 words
The process of claim 10 wherein the range of potassium chloride in said brine is from about 25% to 30% by weight of the salts dissolved in said brine.
Claim 14
Dependent Claim
22 words
The process of claim 9 wherein said mixture of sodium chloride and potassium chloride dissolved in said brine is derived from sylrunite.
Claim 15
Dependent Claim
36 words
The process of claim 9 wherein said brine is prepared by dissolving carnallite in aqueous sodium hydroxide so as to precipitate substantially all of the magnesium as magnesium hydroxide, followed by removal of the magnesium hydroxide.
Claim 16
Dependent Claim
30 words
The process of claims 1 or 4 wherein said catholyte solution has a concentration of between about 300 to about 700 grams per liter of sodium hydroxide and potassium hydroxide.
Claim 17
Dependent Claim
28 words
The process of claim 14 wherein the composition of said catholyte solution comprises between about 40% and 80% by weight sodium hydroxide with the balance being potassium hydroxide.
Claim 18
Dependent Claim
28 words
The process of claim 15 wherein the composition of said catholyte solution comprises between about 50% and 70% by weight sodium hydroxide with the balance being potassium hydroxide.
Claim 19
Dependent Claim
27 words
The process of claims 1 or 4 wherein the salt concentration of said anolyte brine is depleted by about 5% to about 40% by weight during electrolysis.
Claim 20
Dependent Claim
21 words
The process of claim 17 wherein said salt concentration is depleted by about 20% to about 30% by weight during electrolysis.
Claim 21
Dependent Claim
32 words
The process of claims 1 or 4 wherein said membrane is selected from a class comprising amine substituted polymers, unmodified perfluorosulfonic acid laminates, homogeneous perfluorosulfonic acid laminates and carboxylic acid substituted polymers.
Claim 22
Dependent Claim
27 words
The process of claim 19 wherein said membrane is diamine substituted perfluorosulfonic acid resin, modified on one side by amine to a depth of about 0.5 mils.
Claim 23
Dependent Claim
65 words
The process of claim 20 wherein said membrane is a diamine substituted membrane comprised of a homogeneous film about 7 mils thick, of about 1150 equivalent weight perfluorosulfonic acid resin which has been chemically modified on one side by ethylene diamine converting a depth of about 1.5 mils of the polymer to perfluorosulfonamide and with the unmodified side being laminated to a fabric of polytetrafluoroethylene.
Claim 24
Dependent Claim
59 words
The process of claim 21 wherein said fabric is characterized by having a basic weave pattern, a thread count of about 6×6 polytetrafluoroethylene, 24×24 rayon per centimeter, a denier of about 200 polytetrafluoroethylene and 50 rayon, a fabric thickness of about 4.6 mils and an open area (Optical) of about 70 percent by volume after the rayon is removed.
Claim 25
Dependent Claim
55 words
The process of claim 22 wherein said diamine substituted membrane is a perfluorosulfonic acid polymer comprised of a homogeneous film about 7 mils thick, of about 1200 equivalent weight perfluorosulfonic acid resin which has been chemically modified on one side by ethylene diamine converting a depth of about 1.5 mils of the polymer to perfluorosulfonamide.
Claim 26
Dependent Claim
55 words
The process of claim 23 wherein said diamine substituted membrane is a perfluorosulfonic acid polymer comprised of a homogeneous film about 7 mils thick, of about 1150 equivalent weight perfluorosulfonic acid resin which has been chemically modified on one side by ethylene diamine converting a depth of about 1.2 mils of the polymer to perfluorosulfonamide.
Claim 27
Dependent Claim
24 words
The process of claim 19 wherein said membrane is an amine substituted membrane, said membrane being laminated to a fabric of polytetrafluoroethylene and rayon.
Claim 28
Dependent Claim
16 words
The process of claim 25 wherein said amine substituted membrane is a primary amine substituted membrane.
Claim 29
Dependent Claim
15 words
The process of claim 26 wherein said amine substituted membrane is a diamine substituted membrane.
Claim 30
Dependent Claim
15 words
The process of claim 27 wherein said amine substituted membrane is a polyamine substituted membrane.
Claim 31
Dependent Claim
30 words
The process of claim 28 wherein said polyamine is comprised of at least two amino groups with one primary amino group and the second amino group either primary or secondary.
Claim 32
Dependent Claim
36 words
The process of claim 29 wherein said amine substituted membrane is prepared by reacting said amine with a precursor sulfonyl fluoride polymer wherein pendant sulfonyl fluoride groups react to form N-monosubstituted sulfonamido groups or salts thereof.
Claim 33
Dependent Claim
24 words
The process of claim 30 wherein the thickness of said amine substituted membrane is in the range from about 4 to about 10 mils.
Claim 34
Dependent Claim
24 words
The process of claim 31 wherein the thickness of said amine substituted membrane is in the range from about 5 to about 9 mils.
Claim 35
Dependent Claim
29 words
The process of claim 32 wherein said amine is reacted with said precursor sulfonyl fluoride polymer to a depth in the range from about 0.5 to about 7 mils.
Claim 36
Dependent Claim
29 words
The process of claim 33 wherein said amine is reacted with said precursor sulfonyl fluoride polymer to a depth in the range from about 1 to about 2 mils.
Claim 37
Dependent Claim
11 words
The process of claim 34 wherein said amine is ethylene diamine.
Claim 38
Dependent Claim
27 words
The process of claim 19 wherein said membrane comprises two unmodified homogeneous perfluorosulfonic acid films, said films being laminated together with a fabric of tetrafluoroethylene and rayon.
Claim 39
Dependent Claim
64 words
The process of claim 36 wherein said laminate of perfluorosulfonic acid membrane is comprised of a first membrane having a thickness in the range from about 1 to about 2 mils, of about 1500 equivalent weight perfluorosulfonic acid resin, and a second membrane having a thickness in the range from about 4 to about 5 mils of about 1100 equivalent weight perfluorosulfonic acid resin.
Claim 40
Dependent Claim
52 words
The process of claim 37 wherein said laminate of perfluorosulfonic acid membrane is comprised of a first membrane having a thickness of about 2 mils of about 1500 equivalent weight perfluorosulfonic acid resin and a second membrane having a thickness of about 4 mils of about 1100 equivalent weight perfluorosulfonic acid resin.
Claim 41
Dependent Claim
52 words
The process of claim 38 wherein said laminate of perfluorosulfonic acid membrane is comprised of a first membrane having a thickness of about 1 mil of about 1500 equivalent weight perfluorosulfonic acid resin and a second membrane having a thickness of about 5 mils of about 1100 equivalent weight perfluorosulfonic acid resin.
Claim 42
Dependent Claim
52 words
The process of claim 39 wherein said laminate of perfluorosulfonic acid membrane is comprised of a first membrane having a thickness of about 1.5 mils of about 1500 equivalent weight perfluorosulfonic acid resin and a second membrane having a thickness of about 5 mils of about 1100 equivalent weight perfluorosulfonic acid resin.
Claim 43
Dependent Claim
29 words
The process of claim 19 wherein said membrane comprises at least two unmodified perfluorosulfonic acid films of about 1200 equivalent weight laminated together with an inert cloth supporting fabric.
Claim 44
Dependent Claim
26 words
The process of claim 41 wherein said membrane is a homogeneous film of about 7 mils thickness and said inert cloth comprises a polytetrafluoroethylene basket weave.
Claim 45
Dependent Claim
46 words
The process of claim 19 wherein said membrane comprises a carboxylic acid substituted polymer prepared by reacting a fluorinated olefin with a comonomer having a functional group selected from the group consisting of carboxylic acid and a functional group which can be converted to carboxylic acid.
Claim 46
Dependent Claim
68 words
The process of claim 43 wherein said carboxylic acid substituted polymer is a copolymer of tetrafluoroethylene and ##STR4## copolymerized with a catalyst of azobisisobutyronitrile in trichlorotrifluoroethane to obtain a fluorinated copolymer having an ion exchange capacity of about 1.17 meq/g polymer and a T g of 190° C. press molded to form a film about 200 microns thick thereafter hydrolyzed in an aqueous methanol solution of sodium hydroxide.
Claim 47
Dependent Claim
74 words
The process of claim 44 wherein said carboxylic acid substituted polymer is a copolymer of tetrafluoroethylene and CF 2 ═CFO--(CF 2 ) 3 --COOCH 3 copolymerized with a catalyst of azobisisobutyronitrile to obtain a fluorinated copolymer having an ion exchange capacity of about 1.45 meq/g polymer and a T g of about 235° C., press molded to form a film of thickness about 200 microns, hydrolyzed in an aqueous methanol solution of sodium hydroxide.
Claim 48
Dependent Claim
96 words
The process of claim 45 wherein said carboxylic acid substituted polymer is a copolymer of tetrafluoroethylene and CF 2 ═CFO--(CF 2 ) 3 --COOCH 3 (A) and CF 2 ═CFOCF 2 CF(CF 3 )O(CF 2 ) 3 COOCH 4 (B) copolymerized with a catalyst of azobisisobutyronitrile (mole ratios A/B of about 4:1) to obtain a fluorinated copolymer having an ion exchange capacity of about 1:45 meq/g polymer and T g of about 220° C., press molded to obtain a film of about 200 microns thickness, and hydrolyzed in an aqueous solution of methanol of sodium hydroxide.
Claim 49
Dependent Claim
113 words
The process of claim 46 wherein said carboxylic acid substituted polymer is a copolymer of tetrafluoroethylene and CF 2 ═CFO(CF 2 ) 3 --COOCH 3 with a catalyst of ammonium persulfate in water to obtain a fluorinated copolymer having an ion-exchange capacity of 1.20 meq/g polymer and Tg of 210° C., said copolymer being extruded to obtain a film having a thickness of 250 microns and width of 15 cm., and plied to a cloth made of copolymer of tetrafluoroethylene and ethylene (50 mesh: thickness 150 microns) compress-molded to form a reinforced film and hydrolyzed in an aqueous methanol solution of sodium hydroxide to obtain a carboxylic acid type fluorinated cation exchange membrane.
Claim 50
Dependent Claim
34 words
The process of claim 41 wherein said membrane is a homogeneous film of about 7 mils thick laminated with a leno weave with a fabric comprised of polytetrafluoroethylene fibers having rayon fibers interspersed therein.
References Cited (Backward Citations)
US2715608A
Cited
US4036714A
Cited
US4085071A
Cited
US4030988A
Cited
US4080270A
Cited
US4021327A
Cited
US4065366A
Cited
US4065366B1
Cited
US4062743A
Cited
US4147599A
Cited
US4191618A
Cited
US4253923A
Cited
US4358545A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-14 | 1988-02-13 | 1988-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-14 | 1992-02-13 | 1992-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-14 | 1996-02-13 | 1996-08-14 | $7700.00 | Window Closed / Lapsed |