Process for fabrication of high-speed radiation hard bipolar semiconductor devices
Assignee: HARIS Corp A CORP OF DEL
•
Filing: 1983-02-17
•
Granted: 1984-08-14
•
Expires: 2003-02-17
Abstract
Abstract A thermal oxide is grown on a semiconductor substrate containing single crystal, dielectrically isolated tubs. A silicon nitride layer, serving as a mask for complete self-alignment of collector contacts, bases and emitters is then deposited. After the silicon nitride is patterned, the wafer is reoxidized. The oxide over the emitter and collector contact areas is then etched using the previously patterned silicon nitride film as an alignment mask. The remaining silicon nitride is stripped, a base photoresist pattern is formed and a base impurity ion implant is performed, to define the essential profile of the base. Polysilicon is then deposited and implanted with impurities to form 4000 ohm/square resistors. Silicon dioxide is deposited over the areas of polysilicon which are to become resistors when the polysilicon is patterned, which silicon dioxide masks the polysilicon resistor precursors from the impurities implant conducted for the collector contact, emitter and interconnects. The polysilicon is patterned for resistors, contacts and interconnects. Another photoresist is deposited and patterned to open up contact areas for the formation of schottky barrier diodes and transistor bases. Thereafter, the device is metallized, and processing is completed.
Inventors
- 👤 Kenneth A. Ports
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 13:37
CPC Classifications
H; H10; H10D; H10D1/00; H10D1/40; H10D1/47; H10B; H10B10/00; H10B10/10; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0113; H10P; H10P30/00; H10P30/40; H10P32/00; H10P32/20; H10P76/00; H10P76/40; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/019; H10W10/10; Y; Y10; Y10S; Y10S438/00; Y10S438/953
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
374 words
A process for the fabrication of irradiation hardened bipolar device, comprising the steps of: forming a first protective layer on a surface of a semiconductor substrate having dielectrically isolated tubs of single crystal material; forming a layer of silicon nitride over said first protective layer; patterning and removing said silicon nitride in those areas overlaying said substrate wherein a collector contact, and emitter are to be formed, leaving said silicon nitride overlaying said substrate (a) in regions adjacent those wherein said emitter is to be formed, and (b) in regions adjacent those wherein said collector contact is to be formed; increasing the thickness of said first protective layer in regions where said silicon nitride has been removed; removing the portions of said first protective layer overlaying said substrate in regions wherein said collector contact and emitter are to be formed using said patterned silicon nitride layer as a self-alignment mask; forming a thin second protective layer over those regions wherein said first protective layer has been removed, said second protective layer having a thickness less than that of first protective layer, whereby contoured apertures in said first protective layer are formed over said collector contact and emitter regions; removing all remaining silicon nitride; forming a mask to shield apertures in said first protective layer overlaying said substrate except over said base area; implanting and diffusing dopant of a first conductivity type to form a base in said substrate; removing said second protective layer and thereafter depositing a layer of polysilicon in said contoured apertures and on said first protective layer where formation of resistors and interconnects is desired; doping said polysilicon a first time to form said resistor regions; depositing and patterning a shielding layer on said polysilicon to shield said resistor regions; doping said polysilicon a second time with a dopant of a second conductivity type to form said collector contact and emitter by subsequent high temperature diffusion of said second conductivity type dopant from said polysilicon into said substrates, said second doping simultaneously providing dopant for formation of interconnects in said polysilicon; removing said shielding layer and patterning said polysilicon to form collector contact and emitter regions, interconnects and resistors; and thereafter passivating, metallizing and completing final processing of said semiconductor device.
Claim 2
Dependent Claim
374 words
A process for the fabrication of irradiation hardened bipolar device, comprising the steps of: forming a first protective layer on a surface of a semiconductor substrate having dielectrically isolated tubs of single crystal material; forming a layer of silicon nitride over said first protective layer; patterning and removing said silicon nitride in those areas overlaying said substrate wherein a collector contact, and emitter are to be formed, leaving said silicon nitride overlaying said substrate (a) in regions adjacent those wherein said emitter is to be formed, and (b) in regions adjacent those wherein said collector contact is to be formed; increasing the thickness of said first protective layer in regions where said silicon nitride has been removed; removing the portions of said first protective layer overlaying said substrate in regions wherein said collector contact and emitter are to be formed using said patterned silicon nitride layer as a self-alignment mask; forming a thin second protective layer over those regions wherein said first protective layer has been removed, said second protective layer having a thickness less than that of first protective layer, whereby contoured apertures in said first protective layer are formed over said collector contact and emitter regions; removing all remaining silicon nitride; forming a mask to shield apertures in said first protective layer overlaying said substrate except over said base area; implanting and diffusing dopant of a first conductivity type to form a base in said substrate; removing said second protective layer and thereafter depositing a layer of polysilicon in said contoured apertures and on said first protective layer where formation of resistors and interconnects is desired; doping said polysilicon a first time to form said resistor regions; depositing and patterning a shielding layer on said polysilicon to shield said resistor regions; doping said polysilicon a second time with a dopant of a second conductivity type to form said collector contact and emitter by subsequent high temperature diffusion of said second conductivity type dopant from said polysilicon into said substrates, said second doping simultaneously providing dopant for formation of interconnects in said polysilicon; removing said shielding layer and patterning said polysilicon to form collector contact and emitter regions, interconnects and resistors; and thereafter passivating, metallizing and completing final processing of said semiconductor device.
Claim 3
Dependent Claim
92 words
The process of claim 1, wherein said passivating, metallizing and final processing comprises: depositing a passivation layer and opening therethrough apertures to regions wherein contact terminals are to be formed; forming PtSi contacts in all said contact terminal regions; depositing and patterning a metal layer over said PtSi; forming an intermetal isolation layer over said metal layer; opening apertures in said isolation layers; forming aluminum interconnects in said isolation layer apertures; depositing a third protective layer over the formed semiconductor device; and conducting electrical probing of said device and backlapping said wafer.
Claim 4
Dependent Claim
17 words
The process of claim 1, wherein said polysilicon is deposited through low pressure chemical vapor deposition techniques.
Claim 5
Dependent Claim
22 words
The process of claim 1, wherein said single crystal material is N-type, has a 0.2-0.3 ohm-cm resistivity and a 1-0-0 crystal orientation.
Claim 6
Dependent Claim
38 words
The process of claim 1, wherein said first protective layer is about 1500 Angstroms thick, said first silicon nitride layer is about 200 Angstroms thick, and said polysilicon is doped said first time to form 4000 ohm/square resistors.
Claim 7
Dependent Claim
54 words
The process of claim 1, wherein said first protective layer adjacent said contoured apertures is of first thickness sufficient to mask said substrate from said doping steps and said first protective layer in said contoured apertures is of a second thickness intermediate said first thickness and the thickness of said thin second protective layer.
Claim 8
Dependent Claim
17 words
The process of claim 2, wherein said metal layer is comprised of a titanium-tungsten and aluminum composition.
Claim 9
Dependent Claim
17 words
The process of claim 2, wherein said intermetal isolation layer is comprised of chemically deposited silicon dioxide.
Claim 10
Dependent Claim
17 words
The process of claim 2, wherein said intermetal isolation layer is comprised of plasma deposited silicon nitride.
Claim 11
Dependent Claim
21 words
The process of claim 2, wherein said third protective layer is comprised of silicon dioxide formed through chemical vapor deposition techniques.
Claim 12
Dependent Claim
277 words
A process for the fabrication of a radiation hardened bipolar device, comprising the steps of: forming a first protective layer on a surface of a semiconductor substrate having dielectrically isolated tubs of single crystal material; forming a layer of silicon nitride over said first protective layer; patterning and removing said silicon nitride in those areas overlaying said substrate wherein a collector contact, and emitter are to be formed, leaving said silicon nitride overlaying said substrate (a) in regions adjacent those wherein said emitter is to be formed and (b) in regions adjacent those wherein said collector contact is to be formed; increasing the thickness of said first protective layer in regions where said silicon nitride has been removed; removing the portions of said first protective layer overlaying said substrate in regions wherein said collector contact and emitter are to be formed using said patterned silicon nitride layer as a self-alignment mask; forming a thin second protective layer over those regions wherein said first protective layer has been removed, said second protective layer having a thickness less than that of first protective layer, whereby contoured apertures in said first protective layer are formed over said collector contact and emitter regions; removing all remaining silicon nitride; forming a mask to shield apertures in said first protective layer except over said base area; implanting and diffusing a first dopant of a first conductivity type to form a base in said substrate; thereafter depositing a source of a second dopant of a second conductivity type in said contoured inserts; and transferring said second dopant from said source into said substrate by high temperature diffusion to form said collector contact and emitter.
Claim 13
Dependent Claim
277 words
A process for the fabrication of a radiation hardened bipolar device, comprising the steps of: forming a first protective layer on a surface of a semiconductor substrate having dielectrically isolated tubs of single crystal material; forming a layer of silicon nitride over said first protective layer; patterning and removing said silicon nitride in those areas overlaying said substrate wherein a collector contact, and emitter are to be formed, leaving said silicon nitride overlaying said substrate (a) in regions adjacent those wherein said emitter is to be formed and (b) in regions adjacent those wherein said collector contact is to be formed; increasing the thickness of said first protective layer in regions where said silicon nitride has been removed; removing the portions of said first protective layer overlaying said substrate in regions wherein said collector contact and emitter are to be formed using said patterned silicon nitride layer as a self-alignment mask; forming a thin second protective layer over those regions wherein said first protective layer has been removed, said second protective layer having a thickness less than that of first protective layer, whereby contoured apertures in said first protective layer are formed over said collector contact and emitter regions; removing all remaining silicon nitride; forming a mask to shield apertures in said first protective layer except over said base area; implanting and diffusing a first dopant of a first conductivity type to form a base in said substrate; thereafter depositing a source of a second dopant of a second conductivity type in said contoured inserts; and transferring said second dopant from said source into said substrate by high temperature diffusion to form said collector contact and emitter.
Claim 14
Dependent Claim
239 words
A process for fabrication of a radiation hardened bipolar device, comprising the steps of: forming a first protective layer on a surface of a semiconductor substrate of single crystal material; forming a layer of silicon nitride over said first protective layer; patterning and removing said silicon nitride in those areas overlaying said substrate wherein a collector contact, and emitter are to be formed, leaving said silicon nitride overlaying said substrate (a) in regions adjacent those wherein said emitter is to be formed and (b) in regions adjacent those wherein said collector contact is to be formed; increasing the thickness of said first protective layer in regions where said silicon nitride has been removed; removing the portions of said first protective layer overlaying said substrate in regions wherein said collector contact and emitter are to be formed using said patterned silicon nitride layer as a self-alignment mask; removing all remaining silicon nitride whereby contoured apertures in said first protective layer are formed over said collector contact and emitter regions; forming a mask to shield apertures in said first protective layer except over said base area; diffusing a first dopant of a first conductivity type to form a base in said substrate; thereafter depositing a source of a second dopant of a second conductivity type in said contoured inserts; and transferring said second dopant from said source into said substrate by high temperature diffusion to form said collector contact and emitter.
Claim 15
Dependent Claim
239 words
A process for fabrication of a radiation hardened bipolar device, comprising the steps of: forming a first protective layer on a surface of a semiconductor substrate of single crystal material; forming a layer of silicon nitride over said first protective layer; patterning and removing said silicon nitride in those areas overlaying said substrate wherein a collector contact, and emitter are to be formed, leaving said silicon nitride overlaying said substrate (a) in regions adjacent those wherein said emitter is to be formed and (b) in regions adjacent those wherein said collector contact is to be formed; increasing the thickness of said first protective layer in regions where said silicon nitride has been removed; removing the portions of said first protective layer overlaying said substrate in regions wherein said collector contact and emitter are to be formed using said patterned silicon nitride layer as a self-alignment mask; removing all remaining silicon nitride whereby contoured apertures in said first protective layer are formed over said collector contact and emitter regions; forming a mask to shield apertures in said first protective layer except over said base area; diffusing a first dopant of a first conductivity type to form a base in said substrate; thereafter depositing a source of a second dopant of a second conductivity type in said contoured inserts; and transferring said second dopant from said source into said substrate by high temperature diffusion to form said collector contact and emitter.
References Cited (Backward Citations)
US4160991A
Cited
US4269636A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-14 | 1988-02-13 | 1988-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-14 | 1992-02-13 | 1992-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-14 | 1996-02-13 | 1996-08-14 | $7700.00 | Window Closed / Lapsed |