Process for production of coated super-hard alloy articles
Assignee: Mitsubishi Metal Corp
•
Filing: 1981-07-17
•
Granted: 1984-07-31
•
Expires: 2001-07-17
Abstract
Abstract A cutting tool or a wear-resistant mechanical part comprises: a substrate of WC, Co, TiC, and TaC with or without an inner coating layer of TiC, TiN or TiCN; an intermediate layer of a titanium oxycarbide formed on the surface of the substrate or the inner coating layer by carrying out a reaction thereon at a temperature of 800 DEG to 1,200 DEG C. of a halide of titanium, hydrogen, and carbon monoxide or carbon dioxide or a mixture thereof; and an outer coating layer of aluminum oxide formed on the outer surface of the intermediate layer. The thicknesses of the inner layer, the intermediate layer, and the outer coating layer are of the order of 0.5 to 20 microns, 0.5 to 20 microns, and 0.5 to 10 microns, respectively.
Inventors
- 👤 Noribumi Kikuchi
- 👤 Yasuo Suzuki
- 👤 Taijiro Onishi
- 👤 Fumio Washizu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 20:53
CPC Classifications
B; B23; B23B; B23B27/00; B23B27/14; B23B27/148; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/403; Y; Y02; Y02T; Y02T50/00; Y02T50/60; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12576; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
171 words
A process for producing a coated superhard alloy article which comprises: forming a substrate of a super-hard alloy comprising at least one member selected from the group consisting of carbides, nitrides, and carbonitrides of metals of Groups 4a, 5a, and 6a of the periodic table and at least one member selected from the group consisting of Fe, Ni, Co, W, Mo, and Cr; reacting, in the presence of the substrate, a halide of titanium with hydrogen and a member selected from the group consisting of carbon monoxide, carbon dioxide, and mixtures of carbon monoxide and carbon dioxide at a temperature of 800° to 1,200° C. in a gaseous phase to deposit a titanium oxycarbide, produced by the reaction, from the gaseous phase onto the substrate and thus form an intermediate layer of a thickness of 0.5 to 20 microns of the titanium oxycarbide on the substrate; and forming an outer coating layer of a thickness of 0.5 to 10 microns of aluminum oxide on the outer surface of the intermediate layer.
Claim 2
Dependent Claim
171 words
A process for producing a coated superhard alloy article which comprises: forming a substrate of a super-hard alloy comprising at least one member selected from the group consisting of carbides, nitrides, and carbonitrides of metals of Groups 4a, 5a, and 6a of the periodic table and at least one member selected from the group consisting of Fe, Ni, Co, W, Mo, and Cr; reacting, in the presence of the substrate, a halide of titanium with hydrogen and a member selected from the group consisting of carbon monoxide, carbon dioxide, and mixtures of carbon monoxide and carbon dioxide at a temperature of 800° to 1,200° C. in a gaseous phase to deposit a titanium oxycarbide, produced by the reaction, from the gaseous phase onto the substrate and thus form an intermediate layer of a thickness of 0.5 to 20 microns of the titanium oxycarbide on the substrate; and forming an outer coating layer of a thickness of 0.5 to 10 microns of aluminum oxide on the outer surface of the intermediate layer.
Claim 3
Dependent Claim
30 words
A process as claimed in claim 1 in which the intermediate layer has a formula of from TiC 0 .9 O 0 .1 to TiC 0 .4 O 0 .6.
Claim 4
Dependent Claim
121 words
A process as claimed in claim 1 in which the substrate comprises WC, Co, TiC, and TaC, and which process comprises the steps of: heating the substrate to a temperature of 800° to 1,200° C. in a reaction vessel; charging into the reaction vessel a reaction gas mixture comprising TiCl 4 , CO, and a predominant quantity of H 2 thereby to carry out a reaction to form the intermediate layer of titanium oxycarbide; and charging into the reaction vessel a gas mixture comprising AlCl 3 , CO 2 , and a predominant quantity of H 2 thereby to carry out a reaction at a temperature of 800° to 1,200° C. to form the outer coating layer of the aluminum oxide.
Claim 5
Dependent Claim
131 words
A process as claimed in claim 5 in which the substrate comprises WC, Co, TiC, and TaC, and which process comprises the steps of: coating the substrate with the inner layer of TiC; heating the resulting coated substrate to a temperature of 800° to 1,200° C. in a reaction vessel; charging into the reaction vessel a reaction gas mixture comprising TiCl 4 , CO, and a predominant quantity of H 2 thereby to carry out a reaction to form the intermediate layer of titanium oxycarbide; and charging into the reaction vessel a gas mixture comprising AlCl 3 , CO 2 , and a predominant quantity of H 2 thereby to carry out a reaction at a temperature of 800° to 1,200° C. to form the outer coating layer of aluminum oxide.
Claim 6
Dependent Claim
213 words
A process for producing a super-hard alloy article which comprises: forming a substrate of a super-hard alloy comprising at least one member selected from the group consisting of carbides, nitrides and carbonitrides of metals of Groups 4a, 5a and 6a of the periodic table and at least one member selected from the group consisting of Fe, Ni, Co, W, Mo and Cr; forming on the surface of the substrate an inner layer of a thickness of 0.5 to 20 microns of at least one member selected from the group consisting of titanium carbide, titanium nitride, and titanium carbonitride; reacting, in the presence of the substrate having the inner layer thereon, a halide of titanium with hydrogen and a member selected from the group consisting of carbon monoxide, carbon dioxide, and mixtures of carbon monoxide and carbon dioxide at a temperature of 800° to 1,200° C. in a gaseous phase to deposit a titanium oxycarbide, produced by the reaction, from the gaseous phase onto the inner layer and thus form an intermediate layer of a thickness of 0.5 to 10 microns of the titanium oxycarbide on the inner layer; and forming an outer coating layer of a thickness of 0.5 to 10 microns of aluminum oxide on the outer surface of the intermediate layer.
Claim 7
Dependent Claim
213 words
A process for producing a super-hard alloy article which comprises: forming a substrate of a super-hard alloy comprising at least one member selected from the group consisting of carbides, nitrides and carbonitrides of metals of Groups 4a, 5a and 6a of the periodic table and at least one member selected from the group consisting of Fe, Ni, Co, W, Mo and Cr; forming on the surface of the substrate an inner layer of a thickness of 0.5 to 20 microns of at least one member selected from the group consisting of titanium carbide, titanium nitride, and titanium carbonitride; reacting, in the presence of the substrate having the inner layer thereon, a halide of titanium with hydrogen and a member selected from the group consisting of carbon monoxide, carbon dioxide, and mixtures of carbon monoxide and carbon dioxide at a temperature of 800° to 1,200° C. in a gaseous phase to deposit a titanium oxycarbide, produced by the reaction, from the gaseous phase onto the inner layer and thus form an intermediate layer of a thickness of 0.5 to 10 microns of the titanium oxycarbide on the inner layer; and forming an outer coating layer of a thickness of 0.5 to 10 microns of aluminum oxide on the outer surface of the intermediate layer.
Claim 8
Dependent Claim
30 words
A process as claimed in claim 5 in which the intermediate layer has a formula of from TiC 0 .9 O 0 .1 to TiC 0 .4 O 0 .6.
References Cited (Backward Citations)
US3656995A
Cited
US3802933A
Cited
DE2106103A1
Cited
US3736107A
Cited
DE2233699A1
Cited
DE2233700A1
Cited
US3836392A
Cited
US4162338B1
Cited
US4162338A
Cited
US3837894A
Cited
US4026730A
Cited
DE2317447A1
Cited
US3955038A
Cited
DE2528255A1
Cited
US4018631A
Cited
US4035541A
Cited
FR2357321A1
Cited
US4052530A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-31 | 1988-01-30 | 1988-07-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-31 | 1992-01-30 | 1992-07-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-31 | 1996-01-30 | 1996-07-31 | $7700.00 | Window Closed / Lapsed |