Catalyst dispersion having improved stability against phase separation

Claim 2

In a process for forming a pre-activated catalyst component comprising: (a) co-comminuting a magnesium halide, an aluminum halide, a titanium compound, optionally in the presence of at least one electron donor, and (b) reacting the catalyst component from (a) with a small amount of an alpha-monoolefin having 4 to 12 carbon atoms in the presence of an alkyl aluminum compound to produce low molecular weight poly alpha-monoolefin on the catalyst component, the improvement comprising using for said alkyl aluminum compound in (b) a synergistic mixture of between 40 to 80 mole percent of an alkyl aluminum chloride and 20 to 60 mole percent of an oxygen-containing aluminum compound having oxygen attached to at least one aluminum valence, whereby said catalyst component and said inert solvent forms an extremely stable dispersion which will not separate into catalyst component and supernatant solvent in the normal times required to utilize the dispersion in the polymerization of ethylene or its copolymerization with alpha-monoolefins having 3 to 20 carbon atoms.

Claim 3

The process of claim 1 wherein said alkyl aluminum chloride is selected from the group consisting of alkyl aluminum dichloride, dialkyl aluminum chloride, and mixtures thereof wherein each alkyl refers to linear, branched, or cyclic alkyl groups having 1 to 10 carbon atoms in the group.

Claim 4

The process of claim 1 wherein said oxygen-containing aluminum compound is selected from the group consisting of aluminum oxide, alkyl aluminum dialkoxide, dialkyl aluminum alkoxide, aluminum trialkoxide, tetraalkyldialuminoxane, pentaalkyltrialuminoxane, and hexaalkyltetraaluminoxane, wherein each alkyl refers to linear, branched, or cyclic alkyl groups having 1 to 10 carbon atoms in the group.

Claim 5

In a process for forming a pre-activated catalyst component comprising: (a) co-comminuting a mixture of an anhydrous magnesium halide, anhydrous aluminum halide and a first electron donor, and (b) co-comminuting the mixture from (a) with a complex of titanium halide and a second electron donor, which may be different from or the same as said first electron donor; said co-comminuting being carried out under an inert atmosphere in the presence of an inert solvent, and (c) reacting the catalyst component from (b) with a small amount of an alpha-monoolefin having 4 to 12 carbon atoms in the presence of an alkyl aluminum compound to produce a low molecular weight polyalpha-monoolefin on the catalyst component, the improvement comprising using for said alkyl aluminum compound in (c) a synergistic mixture of between 40 to 80 mole percent of an alkyl aluminum chloride and 20 to 60 mole percent of an oxygen-containing aluminum compound having oxygen attached to at least one aluminum valence, whereby said catalyst component and said inert solvent forms an extremely stable dispersion which will not separate into catalyst component and supernatant solvent in the normal times required to utilize the dispersion in the polymerization of ethylene or its copolymerization with alpha-monoolefins having 3 to 20 carbon atoms.

Claim 6

In a process for forming a pre-activated catalyst component comprising: (a) co-comminuting a mixture of an anhydrous magnesium halide, anhydrous aluminum halide and a first electron donor, and (b) co-comminuting the mixture from (a) with a complex of titanium halide and a second electron donor, which may be different from or the same as said first electron donor; said co-comminuting being carried out under an inert atmosphere in the presence of an inert solvent, and (c) reacting the catalyst component from (b) with a small amount of an alpha-monoolefin having 4 to 12 carbon atoms in the presence of an alkyl aluminum compound to produce a low molecular weight polyalpha-monoolefin on the catalyst component, the improvement comprising using for said alkyl aluminum compound in (c) a synergistic mixture of between 40 to 80 mole percent of an alkyl aluminum chloride and 20 to 60 mole percent of an oxygen-containing aluminum compound having oxygen attached to at least one aluminum valence, whereby said catalyst component and said inert solvent forms an extremely stable dispersion which will not separate into catalyst component and supernatant solvent in the normal times required to utilize the dispersion in the polymerization of ethylene or its copolymerization with alpha-monoolefins having 3 to 20 carbon atoms.