Method of deposition of silicon carbide layers on substrates and product
Assignee: United States Department of Energy
•
Filing: 1982-03-19
•
Granted: 1984-07-10
•
Expires: 2002-03-19
Abstract
Abstract A method for direct chemical vapor deposition of silicon carbide to substrates, especially nuclear waste particles, is provided by the thermal decomposition of methylsilane at about 800 DEG C. to 1050 DEG C. when the substrates have been confined within a suitable coating environment.
Inventors
- 👤 Peter Angelini
- 👤 Charles E. Devore
- 👤 Walter J. Lackey
- 👤 Raymond E. Blanco
- 👤 David P. Stinton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 01:05
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/32; C23C16/325; G; G21; G21F; G21F9/00; G21F9/28; G21F9/34; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/24992; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
116 words
A method for providing a nuclear waste particle with a coating consisting of crystalline silicon carbide directly on exposed surfaces thereof, comprising the steps of contacting the particle with a gaseous mixture of methylsilane in an inert gas selected from the group consisting of argon, helium, nitrogen and mixtures thereof while concurrently heating the gaseous mixture and the particle to a temperature in the range of about 800° to 1,050° C. to effect the thermal decomposition of the methylsilane for providing carbon and silicon donors for forming silicon carbide and the chemical vapor deposition of these carbon and silicon donors onto said exposed surfaces as an essentially uniform coating of crystalline silicon carbide on said particle.
Claim 2
Independent Claim
116 words
A method for providing a nuclear waste particle with a coating consisting of crystalline silicon carbide directly on exposed surfaces thereof, comprising the steps of contacting the particle with a gaseous mixture of methylsilane in an inert gas selected from the group consisting of argon, helium, nitrogen and mixtures thereof while concurrently heating the gaseous mixture and the particle to a temperature in the range of about 800° to 1,050° C. to effect the thermal decomposition of the methylsilane for providing carbon and silicon donors for forming silicon carbide and the chemical vapor deposition of these carbon and silicon donors onto said exposed surfaces as an essentially uniform coating of crystalline silicon carbide on said particle.
Claim 3
Dependent Claim
50 words
The method claimed in claim 1 wherein said steps are repeated to form the coating from at least two layers of silicon carbide, and wherein the innermost layer is deposited in the particle at a more rapid growth rate than any subsequent layer to provide a coating of varying density.
Claim 4
Dependent Claim
83 words
The method claimed in claim 2 wherein the innermost layer is deposited on the particle at a growth rate in the range of about 1-5 microns per minute to provide the innermost layer with a density of about 40% of theoretical density, and wherein any subsequent layer of said coating is deposited on the innermost layer at a growth rate in the range of about 0.05-0.5 micron per minute to provide any subsequent layer with a density of about 98% of theoretical density.
Claim 5
Dependent Claim
17 words
The method claimed in claim 1 wherein the ratio of methylsilane to inert gas is about 1:160.
Claim 6
Dependent Claim
9 words
The product derived by the method of claim 1.
Claim 7
Dependent Claim
9 words
The product derived by the method of claim 2.
Claim 8
Dependent Claim
35 words
The product of claim 6 wherein the innermost layer is of a density of about 40% theoretical density, and wherein any other layer forming said coating is of a density of about 98% theoretical density.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-10 | 1988-01-09 | 1988-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-10 | 1992-01-09 | 1992-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-10 | 1996-01-09 | 1996-07-10 | $7700.00 | Window Closed / Lapsed |