US4458407A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for fabricating semi-conductive oxide between two poly silicon gate electrodes
Assignee: International Business Machines Corp
•
Filing: 1983-04-01
•
Granted: 1984-07-10
•
Expires: 2003-04-01
Abstract
Abstract A process for placing non-continuous Dual Electron Injection Structures (DEIS) between two layers of polysilicon used to form an array of poly devices on an integrated circuit substrate. Separate masks are used to define Poly 1 and Poly 2 devices, respectively. The DEIS structure is disposed above the poly 1 devices. A silicon nitride (Si 3 N 4 ) layer is used to mask the DEIS structure and prevents it from oxidizing during certain processing steps. A thin layer of poly x is placed between the DEIS structure and the Si 3 N 4 . The poly x layer forms a buffer and protects the DEIS during an etching step which removes the Si 3 N 4 layer.
Inventors
- 👤 Anthony J. Hoeg, Jr.
- 👤 Charles T. Kroll
- 👤 Geoffrey B. Stephens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 07:00
CPC Classifications
H; H10; H10B; H10B41/00; H10B69/00; H10D; H10D30/00; H10D30/60; H10D30/68; H10D30/681; H10D30/682
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
252 words
A method for incorporating a non-continuous DEIS material between two layers of polysilicon in an array of devices on an integrated circuit substrate comprising the following steps: (a) fabricating a silicon substrate with at least one thin oxide region surrounded by thick oxide region; (b) depositing a first polysilicon gate interconnect layer on the substrate; (c) depositing on the said first polysilicon gate interconnect layer a first layer of silicon rich oxide, a layer of silicon dioxide, a second layer of silicon rich oxide, a second layer of polysilicon and a layer of non-oxidizing material with the layers being deposited in the order of recitation; (d) patterning a first photoresist mask on the layer of non-oxidizing material with said photoresist defining a profile for the DEIS material; (e) etching the exposed areas through the said non-oxidizing material, through the said second layer of polysilicon; (f) etching the exposed DEIS areas; (g) stripping the first photoresist mask; (h) patterning a second photoresist mask on the layer of the non-oxidizing material; said second photoresist mask being operable to define at least one polysilicon floating gate electrode and polysilicon interconnections; (i) etching the exposed polysilicon areas; (j) stripping the second photoresist mask; (k) thermally oxidizing the structure for isolating at least one floating gate; (l) removing the layer of non-oxidizing material; (m) depositing a third layer of polysilicon on the second layer of polysilicon previously laid down in step (b) above; and (n) forming electrical interconnections and gate electrodes in said third layer of polysilicon.
Claim 2
Independent Claim
252 words
A method for incorporating a non-continuous DEIS material between two layers of polysilicon in an array of devices on an integrated circuit substrate comprising the following steps: (a) fabricating a silicon substrate with at least one thin oxide region surrounded by thick oxide region; (b) depositing a first polysilicon gate interconnect layer on the substrate; (c) depositing on the said first polysilicon gate interconnect layer a first layer of silicon rich oxide, a layer of silicon dioxide, a second layer of silicon rich oxide, a second layer of polysilicon and a layer of non-oxidizing material with the layers being deposited in the order of recitation; (d) patterning a first photoresist mask on the layer of non-oxidizing material with said photoresist defining a profile for the DEIS material; (e) etching the exposed areas through the said non-oxidizing material, through the said second layer of polysilicon; (f) etching the exposed DEIS areas; (g) stripping the first photoresist mask; (h) patterning a second photoresist mask on the layer of the non-oxidizing material; said second photoresist mask being operable to define at least one polysilicon floating gate electrode and polysilicon interconnections; (i) etching the exposed polysilicon areas; (j) stripping the second photoresist mask; (k) thermally oxidizing the structure for isolating at least one floating gate; (l) removing the layer of non-oxidizing material; (m) depositing a third layer of polysilicon on the second layer of polysilicon previously laid down in step (b) above; and (n) forming electrical interconnections and gate electrodes in said third layer of polysilicon.
Claim 3
Dependent Claim
30 words
The method of claim 1 wherein the semiconductor structure is being fabricated through a technique including the steps of formation of Recessed Oxide (ROX), gate oxidation and polysilicon gate deposition.
Claim 4
Dependent Claim
15 words
The method of claim 1 wherein the non-oxidizing material of step (c) includes silicon nitride.
Claim 5
Dependent Claim
34 words
The method of claim 1 wherein an in situ chemical vapor deposition (CVD) technique is used to deposit the first and second layers of silicon rich oxide and the first layer of silicon dioxide.
Claim 6
Dependent Claim
42 words
The method of claim 4 wherein the first layer of silicon rich oxide is approximately 20 nm thick, the first layer of silicon dioxide is approximately 15 nm thick and the second layer of silicon rich oxide is approximately 20 nm thick.
Claim 7
Dependent Claim
51 words
The method of claim 5 wherein the silicon rich oxide is being deposited with a low pressure CVD reactor having a flow rate of 20 cc/minute of 100% silane (SiH 4 ), 100 cc/minute of nitrous oxide (N 2 O), a temperature of 750° C. and a pressure of 750 millitorr.
Claim 8
Dependent Claim
34 words
The method of claim 5 wherein the second layer of silicon dioxide is being deposited at 7 cc/minute of SiH 4 , 300 cc/minute of N 2 O at 750 millitorr and 750° C.
Claim 9
Dependent Claim
19 words
The method of claim 1 wherein the non-oxidizing material of step (d) defines a non-continuous profile for the DEIS.
Claim 10
Dependent Claim
20 words
The method of claim 1 wherein steps (e), (i) and (l) are being etched in a plasma etch using DE-100.
Claim 11
Dependent Claim
15 words
The method of claim 1 wherein step (f) is being etched in a buffered HF.
Claim 12
Independent Claim
162 words
A method for fabricating an E 2 PROM comprising of the following steps: (a) fabricating a silicon substrate with at least one thin oxide region surrounded by thick oxide region; (b) depositing a first polysilicon layer on a silicon substrate; (c) depositing a DEIS material on top of the first polysilicon layer; (d) depositing a relatively thin second polysilicon layer on top of the DEIS; (e) depositing a layer of silicon nitride on top of said relatively thin second polysilicon layer; (f) patterning a photoresist mask on the silicon nitride layer; (g) etching the exposed areas through the said silicon nitride layer, and said second polysilicon layer and said DEIS material, and said first polysilicon layer; (h) stripping the photoresist; (i) thermally oxidizing the structure for isolating at least one floating gate; (j) removing the layer of silicon nitride; (k) depositing a third layer of polysilicon material; and (l) fabricating electrical interconnections and gate electrodes in said second layer of polysilicon material.
Claim 13
Independent Claim
162 words
A method for fabricating an E 2 PROM comprising of the following steps: (a) fabricating a silicon substrate with at least one thin oxide region surrounded by thick oxide region; (b) depositing a first polysilicon layer on a silicon substrate; (c) depositing a DEIS material on top of the first polysilicon layer; (d) depositing a relatively thin second polysilicon layer on top of the DEIS; (e) depositing a layer of silicon nitride on top of said relatively thin second polysilicon layer; (f) patterning a photoresist mask on the silicon nitride layer; (g) etching the exposed areas through the said silicon nitride layer, and said second polysilicon layer and said DEIS material, and said first polysilicon layer; (h) stripping the photoresist; (i) thermally oxidizing the structure for isolating at least one floating gate; (j) removing the layer of silicon nitride; (k) depositing a third layer of polysilicon material; and (l) fabricating electrical interconnections and gate electrodes in said second layer of polysilicon material.
Claim 14
Dependent Claim
21 words
The method recited in claim 10 wherein the photoresist mask defines a coincident profile for the DEIS and the floating gate.
Claim 15
Independent Claim
259 words
A method for incorporating a non-continuous DEIS material between two layers of polysilicon in an array of devices on an integrated circuit substrate comprising the following steps being performed in the order of recitation: (a) fabricating a silicon substrate with at least one thin oxide region surrounded by thick oxide region; (b) depositing a first polysilicon gate interconnect layer on the substrate; (c) patterning a first photoresist mask on the layer of the non-oxidizing material; said first photoresist mask being operable to define at least one polysilicon floating gate electrode and polysilicon interconnections; (d) etching the exposed polysilicon areas; (e) stripping the first photoresist mask; (f) depositing on the said first polysilicon gate interconnect layer a first layer of silicon rich oxide, a layer of silicon dioxide, a second layer of silicon rich oxide, a second layer of polysilicon and a layer of non-oxidizing material with the layers being deposited in the order of recitation; (g) patterning a second photoresist mask on the layer of non-oxidizing material with said photoresist defining a profile for the DEIS material; (h) etching the exposed areas through the said non-oxidizing material, through the said second layer of polysilicon; (i) etching the exposed DEIS areas; (j) stripping the second photoresist mask; (k) thermally oxidizing the structure for isolating at least one floating gate; (l) removing the layer of non-oxidizing material; (m) depositing a third layer of polysilicon on the second layer of polysilicon previously laid down in step (b) above; and (n) forming electrical interconnections and gate electrodes in said third layer of polysilicon.
Claim 16
Independent Claim
259 words
A method for incorporating a non-continuous DEIS material between two layers of polysilicon in an array of devices on an integrated circuit substrate comprising the following steps being performed in the order of recitation: (a) fabricating a silicon substrate with at least one thin oxide region surrounded by thick oxide region; (b) depositing a first polysilicon gate interconnect layer on the substrate; (c) patterning a first photoresist mask on the layer of the non-oxidizing material; said first photoresist mask being operable to define at least one polysilicon floating gate electrode and polysilicon interconnections; (d) etching the exposed polysilicon areas; (e) stripping the first photoresist mask; (f) depositing on the said first polysilicon gate interconnect layer a first layer of silicon rich oxide, a layer of silicon dioxide, a second layer of silicon rich oxide, a second layer of polysilicon and a layer of non-oxidizing material with the layers being deposited in the order of recitation; (g) patterning a second photoresist mask on the layer of non-oxidizing material with said photoresist defining a profile for the DEIS material; (h) etching the exposed areas through the said non-oxidizing material, through the said second layer of polysilicon; (i) etching the exposed DEIS areas; (j) stripping the second photoresist mask; (k) thermally oxidizing the structure for isolating at least one floating gate; (l) removing the layer of non-oxidizing material; (m) depositing a third layer of polysilicon on the second layer of polysilicon previously laid down in step (b) above; and (n) forming electrical interconnections and gate electrodes in said third layer of polysilicon.
Claim 17
Independent Claim
213 words
A method for incorporating a non-continuous DEIS material between two layers of polysilicon in an array of devices on an integrated circuit substrate comprising the following steps: (a) fabricating a silicon substrate with at least one thin oxide region surrounded by thick oxide region; (b) depositing a first polysilicon gate interconnect layer on the substrate; (c) depositing on the said first polysilicon gate interconnect layer a first layer of silicon rich oxide, a layer of silicon dioxide, a second layer of silicon rich oxide, a second layer of polysilicon and a layer of non-oxidizing material with the layers being deposited in the order of recitation; (d) patterning a photoresist mask on the layer of non-oxidizing material with said photoresist defining a profile for the DEIS material; (e) etching the exposed areas through the said non-oxidizing material, through the said second layer of polysilicon; (f) etching the exposed DEIS areas; (g) etching the exposed polysilicon areas; (h) stripping the photoresist mask; (i) thermally oxidizing the structure for isolating at least one floating gate; (j) removing the layer of non-oxidizing material; (k) depositing a third layer of polysilicon on the second layer of polysilicon previously laid down in step (b) above; and (l) forming electrical interconnections and gate electrodes in said third layer of polysilicon.
Claim 18
Independent Claim
213 words
A method for incorporating a non-continuous DEIS material between two layers of polysilicon in an array of devices on an integrated circuit substrate comprising the following steps: (a) fabricating a silicon substrate with at least one thin oxide region surrounded by thick oxide region; (b) depositing a first polysilicon gate interconnect layer on the substrate; (c) depositing on the said first polysilicon gate interconnect layer a first layer of silicon rich oxide, a layer of silicon dioxide, a second layer of silicon rich oxide, a second layer of polysilicon and a layer of non-oxidizing material with the layers being deposited in the order of recitation; (d) patterning a photoresist mask on the layer of non-oxidizing material with said photoresist defining a profile for the DEIS material; (e) etching the exposed areas through the said non-oxidizing material, through the said second layer of polysilicon; (f) etching the exposed DEIS areas; (g) etching the exposed polysilicon areas; (h) stripping the photoresist mask; (i) thermally oxidizing the structure for isolating at least one floating gate; (j) removing the layer of non-oxidizing material; (k) depositing a third layer of polysilicon on the second layer of polysilicon previously laid down in step (b) above; and (l) forming electrical interconnections and gate electrodes in said third layer of polysilicon.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-10 | 1988-01-09 | 1988-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-10 | 1992-01-09 | 1992-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-10 | 1996-01-09 | 1996-07-10 | $7700.00 | Window Closed / Lapsed |