Multiple stage process for preparing mixed hydroxyalkylcellulose ethers
Assignee: Dow Chemical Co
•
Filing: 1983-09-22
•
Granted: 1984-06-26
•
Expires: 2003-09-22
Abstract
Abstract Mixed hydroxyalkyl cellulose ethers are prepared in a multi-stage etherification process, for example, hydroxyethylmethylcellulose is prepared by reacting alkali cellulose sequentially with ethylene oxide, methyl chloride, ethylene oxide and methyl chloride to form a product having uniform substitution. Products made by this process have improved solubility and other properties.
Inventors
- 👤 Christopher D. Messelt
- 👤 Glenda P. Townsend
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 07:59
CPC Classifications
C; C08; C08B; C08B11/00; C08B11/193
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
102 words
A process for preparing mixed hydroxyalkyl cellulose ethers comprising sequentially reacting an alkali cellulose with (a) an alkylene oxide under conditions sufficient to attach to the cellulose a portion of the amount of hydroxyalkyl groups to be attached thereto, (b) an etherifying agent which is different from the alkylene oxide employed in steps (a) and (c) and which reduces the formation of poly(alkylene oxide) chains, under conditions such that ether groups are attached to the cellulose, and (c) an alkylene oxide under conditions sufficient to attach to the cellulose a second portion of the amount of hydroxyalkyl groups to be attached thereto.
Claim 2
Dependent Claim
102 words
A process for preparing mixed hydroxyalkyl cellulose ethers comprising sequentially reacting an alkali cellulose with (a) an alkylene oxide under conditions sufficient to attach to the cellulose a portion of the amount of hydroxyalkyl groups to be attached thereto, (b) an etherifying agent which is different from the alkylene oxide employed in steps (a) and (c) and which reduces the formation of poly(alkylene oxide) chains, under conditions such that ether groups are attached to the cellulose, and (c) an alkylene oxide under conditions sufficient to attach to the cellulose a second portion of the amount of hydroxyalkyl groups to be attached thereto.
Claim 3
Dependent Claim
20 words
The process of claim 1 wherein the alkylene oxide is ethylene oxide and the etherifying agent is an alkyl chloride.
Claim 4
Dependent Claim
73 words
The process of claim 1 wherein in step (a) 20-85 weight percent of the amount of hydroxyalkyl groups to be attached to the cellulose are attached thereto and step (b) 15-80 weight percent of the amount of ether groups to be attached to the cellulose are attached thereto and after attaching said second portion of hydroxyalkoxyl groups to the cellulose, the cellulose contains the entire amount of hydroxyalkoxyl groups to be attached thereto.
Claim 5
Dependent Claim
28 words
The process of claim 1 wherein in steps (a) and (c), the alkylene oxide is ethylene oxide and said ethylene oxide is added continuously to the alkali cellulose.
Claim 6
Dependent Claim
58 words
The process of claim 1 wherein steps (a) and (b) are conducted by simultaneously adding the alkylene oxide and etherifying agent to the alkali cellulose, reacting the alkali cellulose with the alkylene oxide under conditions such that the etherifying agent does not substantially react with the alkali cellulose and then reacting the etherifying agent with the alkali cellulose.
Claim 7
Dependent Claim
43 words
The process of claim 2 wherein the etherifying agent is methyl chloride and the mixed hydroxyalkyl cellulose ether is hydroxyethylmethylcellulose having a hydroxyethyl molar substitution of about 1.0 to about 4.0 and a methoxy degree of substitution of about 0.05 to about 1.0.
Claim 8
Dependent Claim
46 words
The process of claim 1 wherein after step (c), the alkali cellulose is contacted with an etherifying agent which is different from the alkylene oxide employed in steps (a) and (c), said contact being made under conditions such that ether groups are attached to the cellulose.
Claim 9
Dependent Claim
27 words
The process of claim 7 wherein the etherifying agent employed in step (b) is different from the etherifying agent contacted with the alkali cellulose following step (c).
Claim 10
Dependent Claim
15 words
The process of claim 1 wherein the etherifying agent is a halo-substituted aliphatic carboxylic acid.
References Cited (Backward Citations)
US24116A
Cited
USRE24116E
Cited
US2831852A
Cited
US2835666A
Cited
GB973952A
Cited
US3296247A
Cited
US3839319A
Cited
US4096325A
Cited
FR2372177A2
Cited
US4292426A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-26 | 1987-12-26 | 1988-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-26 | 1991-12-26 | 1992-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-26 | 1995-12-26 | 1996-06-26 | $7700.00 | Window Closed / Lapsed |