Continuous process for the production of vinyl chloride polymers in aqueous suspension
Assignee: Hoechst AG
•
Filing: 1982-08-09
•
Granted: 1984-06-26
•
Expires: 2002-08-09
Abstract
Abstract The process is described for the continuous suspension polymerization of vinyl chloride in aqueous phase, in which the polymerization mixture is subjected, in 2 zones, to treatment employing different process parameters in respect of final conversion, dwell time, number of theoretical cascade stages and stirrer power applied. This procedure gives, at good space-time yields, very uniform products which have a narrow particle size distribution, a high bulk density, good flow and a low speck count. In spite of using standard kettle material, only a very low formation of deposit on the kettle walls is observed.
Inventors
- 👤 Manfred Engelmann
- 👤 Heinz Klippert
- 👤 Eberhard Tzschoppe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:34
CPC Classifications
C; C08; C08F; C08F14/00; C08F14/02; C08F14/04; C08F14/06
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
239 words
A continuous process for the production of a vinyl chloride polymer by homopolymerization, or copolymerization in the presence of at least one monomer which can be copolymerized with vinyl chloride, or graft polymerization of vinyl chloride in the presence of at least one polymer which can be graft polymerized with vinyl chloride in aqueous suspension in the presence of at least one activator which decompose to form free radicals and of at least one suspending agent in at least two zones, the mixture being cooled, released from pressure and freed from unreacted monomers after leaving the last zone and, after the removal of the bulk of the aqueous liquid, being processed to give a dry polymer powder, which comprises agitating the polymerization mixture in the first zone at a volume-specific stirrer power of 0.6 to 6 kWm -3 until a vinyl chloride monomer conversion of 0 to 3 percent by weight has been reached, in an apparatus, at a number of theoretical cascade stages of 3 to 20 and at average dwell times of the polymerization mixture of 5 to 60 minutes and agitating the polymerization mixture in the second zone at a volume-specific stirrer power of 0.01 to 0.6 kWm -3 in an apparatus, at a number of theoretical cascade stages of 10 to 100 and carrying out polymerization at temperatures of 40° to 80° C. until a conversion of 70 to 98% by weight has been reached.
Claim 2
Dependent Claim
239 words
A continuous process for the production of a vinyl chloride polymer by homopolymerization, or copolymerization in the presence of at least one monomer which can be copolymerized with vinyl chloride, or graft polymerization of vinyl chloride in the presence of at least one polymer which can be graft polymerized with vinyl chloride in aqueous suspension in the presence of at least one activator which decompose to form free radicals and of at least one suspending agent in at least two zones, the mixture being cooled, released from pressure and freed from unreacted monomers after leaving the last zone and, after the removal of the bulk of the aqueous liquid, being processed to give a dry polymer powder, which comprises agitating the polymerization mixture in the first zone at a volume-specific stirrer power of 0.6 to 6 kWm -3 until a vinyl chloride monomer conversion of 0 to 3 percent by weight has been reached, in an apparatus, at a number of theoretical cascade stages of 3 to 20 and at average dwell times of the polymerization mixture of 5 to 60 minutes and agitating the polymerization mixture in the second zone at a volume-specific stirrer power of 0.01 to 0.6 kWm -3 in an apparatus, at a number of theoretical cascade stages of 10 to 100 and carrying out polymerization at temperatures of 40° to 80° C. until a conversion of 70 to 98% by weight has been reached.
Claim 3
Dependent Claim
29 words
The process as claimed in claim 1, wherein the polymerization mixture remains in the first zone only until a conversion of 0 to 0.5% by weight has been reached.
Claim 4
Dependent Claim
32 words
The process as claimed in either of claims 1 to 2, wherein the polymerization mixture is agitated in the first zone at a number of theoretical cascade stages of 5 to 10.
Claim 5
Dependent Claim
29 words
The process as claimed in either of claims 1 or 2, wherein the average dwell time of the polymerization mixture in the first zone is 10 to 30 minutes.
Claim 6
Dependent Claim
42 words
The process as claimed in either of claims 1 or 2, wherein the number of theoretical cascade stages and the average dwell time in the first zone are so adjusted that the product of these two quantities is 30 to 300 minutes.
Claim 7
Dependent Claim
33 words
The process as claimed in either of claims 1 or 2, wherein the polymerization mixture is agitated in the first zone at a volume-specific stirrer power of 1 to 3 kWm -3 .
Claim 8
Dependent Claim
38 words
The process as claimed in either of claims 1 or 2, wherein the polymerization mixture in the first zone is kept between 15° C. and a temperature 10° C. less than the polymerization temperature in the second zone.
Claim 9
Dependent Claim
32 words
The process as claimed in either of claims 1 or 2, wherein, the polymerization mixture is agitated in the second zone at a number of theoretical cascade stages of 15 to 50.
Claim 10
Dependent Claim
33 words
The process as claimed in either of claims 1 or 2, wherein the polymerization mixture is agitated in the second zone at a volume-specific stirrer power of 0.02 to 0.2 kWm -3 .
Claim 11
Dependent Claim
29 words
The process as claimed in either of claims 1 or 2, wherein agents for preventing deposits on the walls of the reaction space are used in the second zone.
Claim 12
Dependent Claim
85 words
The process is claimed in either of claims 1 or 2, wherein polymerization is carried out in the presence of 0.05 to 3.0% by weight, relative to monomers employed, of at least one polyvinyl alcohol which contains acetate groups and which has a saponification number of 140 to 560 and a weight average molecular weight of 10,000 to 100,000 the quantity of this polyvinyl alcohol amounting to 100 to 50% by weight, relative to the quantity of all the suspending agents present in the polymerization.
Claim 13
Dependent Claim
187 words
A continuous process for suspension polymerization, in a plurality of zones, of a polymerization mixture comprising vinyl chloride monomer, an aqueous liquor for suspension polymerization, and an activator capable of decomposing to form free radicals, said process comprising: agitating the polymerization mixture in the first zone at a volume-specific stirrer power of 0.6 to 6 Kwm -3 until a vinyl chloride monomer conversion of 0 to 3 percent by weight has been reached, in an apparatus, at a number of theoretical cascade stages of 3 to 20 and at average dwell times of the polymerization mixture of 5 to 60 minutes; agitating the polymerization mixture in the second zone at a volume-specific stirrer power of 0.01 to 0.6 kWm -3 in an apparatus, at a number of theoretical cascade stages of 10 to 100 and carrying out polymerization at temperatures of 40° to 80° C. until a conversion of 70 to 98% by weight has been reached; and removing the aqueous liquor and unreacted monomer from the polymerization mixture to obtain a dry polymer powder after said conversion of 70 to 98% by weight has been reached.
Claim 14
Dependent Claim
187 words
A continuous process for suspension polymerization, in a plurality of zones, of a polymerization mixture comprising vinyl chloride monomer, an aqueous liquor for suspension polymerization, and an activator capable of decomposing to form free radicals, said process comprising: agitating the polymerization mixture in the first zone at a volume-specific stirrer power of 0.6 to 6 Kwm -3 until a vinyl chloride monomer conversion of 0 to 3 percent by weight has been reached, in an apparatus, at a number of theoretical cascade stages of 3 to 20 and at average dwell times of the polymerization mixture of 5 to 60 minutes; agitating the polymerization mixture in the second zone at a volume-specific stirrer power of 0.01 to 0.6 kWm -3 in an apparatus, at a number of theoretical cascade stages of 10 to 100 and carrying out polymerization at temperatures of 40° to 80° C. until a conversion of 70 to 98% by weight has been reached; and removing the aqueous liquor and unreacted monomer from the polymerization mixture to obtain a dry polymer powder after said conversion of 70 to 98% by weight has been reached.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-26 | 1987-12-26 | 1988-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-26 | 1991-12-26 | 1992-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-26 | 1995-12-26 | 1996-06-26 | $7700.00 | Window Closed / Lapsed |