Process and apparatus for forming a composite foamed polymeric sheet structure having comparatively high density skin layers and a comparatively low density core layer
Assignee: Mobil Oil AS
•
Filing: 1982-12-13
•
Granted: 1984-06-26
•
Expires: 2002-12-13
Abstract
Abstract A method and apparatus for producing a foamed polymeric sheet having comparatively high density skin layers. Molten polymer containing a foaming agent is extruded from a die into a post-extrusion region defined by the die and a spaced pair of rotating chill rolls which are spaced from the die. The post-extrusion region is maintained at a pressure sufficient to at least inhibit expansion of the foamable molten polymer through the use of cooled sealing elements which occupy a substantial portion of the space between the die and the chill rolls, and are spaced from the chill rolls. The rolls and the sealing elements are cooled so that foamable molten polymer in the space between the sealing elements and the rolls becomes solidified, completing the seal. The chill rolls are maintained at a temperature below the temperature of the molten polymer to aid the skin formation on the surfaces of the polymer. If desired, the polymer can pass directly from the chill rolls into a water bath.
Inventors
- 👤 David E. Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:58
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/20; B29C44/22; B29C44/34; B29C44/36; B29C44/46; B29C44/50; B29C44/505; B29C48/00; B29C48/03; B29C48/07; B29C48/08; B29C48/25; B29C48/30; B29C48/35; B29L; B29L2007/00; Y; Y10; Y10S; Y10S264/00; Y10S264/05
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
177 words
A method for forming a polymeric sheet structure having comparatively high density skin layers and a comparatively low density core layer comprising: (a) extruding molten polymer containing a foaming agent therein through a slot die, into a post extrusion region defined by said die and two spaced rotating chill rolls which are spaced from said die; (b) maintaining said post extrusion region at a pressure sufficient to at least inhibit expansion of said formable molten polymer with cooled sealing means which occupy a substantial portion of the space between said die and said rolls and are spaced from said rolls, said rolls and said sealing means being cooled so that said foamble molten polymer in the space between said rolls and said sealing means is solidified; (c) transporting said extruded foamable molten polymer between, and into contact with and through the chill rolls, the chill roll surfaces being maintained at a temperature lower than the solidification temperature of said polymer; and (d) transporting the foamable polymer from between said chill rolls to a region of lower pressure.
Claim 2
Independent Claim
177 words
A method for forming a polymeric sheet structure having comparatively high density skin layers and a comparatively low density core layer comprising: (a) extruding molten polymer containing a foaming agent therein through a slot die, into a post extrusion region defined by said die and two spaced rotating chill rolls which are spaced from said die; (b) maintaining said post extrusion region at a pressure sufficient to at least inhibit expansion of said formable molten polymer with cooled sealing means which occupy a substantial portion of the space between said die and said rolls and are spaced from said rolls, said rolls and said sealing means being cooled so that said foamble molten polymer in the space between said rolls and said sealing means is solidified; (c) transporting said extruded foamable molten polymer between, and into contact with and through the chill rolls, the chill roll surfaces being maintained at a temperature lower than the solidification temperature of said polymer; and (d) transporting the foamable polymer from between said chill rolls to a region of lower pressure.
Claim 3
Dependent Claim
19 words
The process of claim 1 wherein said polymer is a polystyrene and said foaming agent is CO 2 .
Claim 4
Dependent Claim
29 words
The process of claim 1 wherein said polymer is transported from between said rotating chill rolls into an aqueous bath maintained at below the solidification temperature of said polymer.
Claim 5
Dependent Claim
39 words
The process of claim 3, wherein said aqueous bath is a water bath which is in contact with at least the region between said chill rolls so that the polymer issues from between said rolls into said water bath.
Claim 6
Dependent Claim
175 words
Apparatus for producing a polymeric film structure having comparatively high density skin layers and a comparatively low density core layer comprising in combination: (a) extruder means for transporting molten resin containing a foaming agent under pressure from a feed point to a slot die discharge point; (b) a pair of spaced driven chill rolls in association with and spaced from said slot die and adapted to receive extruded molten foaming agent-containing polymer therebetween and into contact therewith; (c) chill means for maintaining said chill rolls at a temperature below that of said foamable molten polymer; and (d) cooled sealing means between said die and said chill rolls, spaced from said chill rolls and occupying a substantial portion of the space between said die and said chill rolls, said rolls and said sealing means being cooled so that the foamable molten polymer in the space between said rolls and said sealing means is solidified to at least substantially pressure seal the region between said slot die and chill rolls and permit a back-pressure to develop therein.
Claim 7
Dependent Claim
175 words
Apparatus for producing a polymeric film structure having comparatively high density skin layers and a comparatively low density core layer comprising in combination: (a) extruder means for transporting molten resin containing a foaming agent under pressure from a feed point to a slot die discharge point; (b) a pair of spaced driven chill rolls in association with and spaced from said slot die and adapted to receive extruded molten foaming agent-containing polymer therebetween and into contact therewith; (c) chill means for maintaining said chill rolls at a temperature below that of said foamable molten polymer; and (d) cooled sealing means between said die and said chill rolls, spaced from said chill rolls and occupying a substantial portion of the space between said die and said chill rolls, said rolls and said sealing means being cooled so that the foamable molten polymer in the space between said rolls and said sealing means is solidified to at least substantially pressure seal the region between said slot die and chill rolls and permit a back-pressure to develop therein.
Claim 8
Dependent Claim
47 words
The apparatus of claim 5 including bath means for maintaining at least the region between said chill rolls in contact with water maintained at a temperature below the soldification temperature of said extruded foamable polymer so that the polymer issues from between said rolls into the water.
References Cited (Backward Citations)
US2893877A
Cited
US3299192A
Cited
US3431164A
Cited
US3444036A
Cited
US3459274A
Cited
US3810965A
Cited
US4071591A
Cited
US3864444A
Cited
US3900544A
Cited
US4017245A
Cited
US4154785A
Cited
US4290248A
Cited
US4128369A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-26 | 1987-12-26 | 1988-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-26 | 1991-12-26 | 1992-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-26 | 1995-12-26 | 1996-06-26 | $7700.00 | Window Closed / Lapsed |