Process for dislocation-free slot isolations in device fabrication
Assignee: Advanced Micro Devices Inc
•
Filing: 1983-12-22
•
Granted: 1984-06-26
•
Expires: 2003-12-22
Abstract
Abstract A semiconductor wafer masked with a masking layer having an opening therethrough exposing a portion of the wafer which is to be etched to form a depression of a desired depth is etched via a first plasma etching step under high bias voltage-high energy conditions with a plasma which includes chlorine and a shape modifier species, e.g., argon, to a first depth which is less than the desired depth. Thereafter, the depression is treated by a second plasma etching step under low bias voltage-low energy plasma etching conditions with a plasma which includes chlorine and is substantially free of the shape modifier species. A wet chemical etch follows to remove damaged silicon and impurities. The resulting depression has relatively straight walls and is relatively free of cusps and apexes. The depression is formed quickly and has a desired shape while only a minimal amount of damage and impurities are introduced into the wafer.
Inventors
- 👤 Atiye Bayman
- 👤 Mammen Thomas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:46
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/24; H10P50/242
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
167 words
A method of etching a silicon wafer masked with a masking layer having an opening therethrough exposing a portion of said wafer which is to be etched to form a depression of a desired depth, comprising: first, plasma etching said portion under relatively high bias voltage-relatively high energy plasma etching conditions with a plasma which includes chlorine and a shape modifier species to a first depth which is less than said desired depth; second, plasma etching said depression from said first depth to said desired depth under relatively low bias voltage-relatively low energy plasma etching conditions with a plasma which includes chlorine and is substantially free of said shape modifier species; and third, contacting a wet chemical etching fluid with said depression, said fluid being selected to etch away a desired thickness of damaged silicon from said depression, said contacting being for a time sufficient to accomplish etching away of said desired thickness of silicon from said depression; and rinsing said chemical etching fluid from said depression.
Claim 2
Independent Claim
167 words
A method of etching a silicon wafer masked with a masking layer having an opening therethrough exposing a portion of said wafer which is to be etched to form a depression of a desired depth, comprising: first, plasma etching said portion under relatively high bias voltage-relatively high energy plasma etching conditions with a plasma which includes chlorine and a shape modifier species to a first depth which is less than said desired depth; second, plasma etching said depression from said first depth to said desired depth under relatively low bias voltage-relatively low energy plasma etching conditions with a plasma which includes chlorine and is substantially free of said shape modifier species; and third, contacting a wet chemical etching fluid with said depression, said fluid being selected to etch away a desired thickness of damaged silicon from said depression, said contacting being for a time sufficient to accomplish etching away of said desired thickness of silicon from said depression; and rinsing said chemical etching fluid from said depression.
Claim 3
Dependent Claim
26 words
A method as set forth in claim 1, wherein said chlorine is produced in the plasma from a compound which forms chlorine under plasma etching conditions.
Claim 4
Dependent Claim
36 words
A method as set forth in claim 1, wherein said shape modifier species is selected from the group consisting of the noble gases, hydrogen, nitrogen, and non-fluoride-containing boron trihalides, silicon tetrahalides, sulfur hexahalides and carbon tetrahalides.
Claim 5
Dependent Claim
20 words
A method as set forth in claim 3, wherein said wet chemical etching fluid comprises an acidic fluoride containing solution.
Claim 6
Dependent Claim
17 words
A method as set forth in claim 4, wherein said wet chemical etching fluid further comprises iodine.
Claim 7
Dependent Claim
19 words
A method as set forth in claim 4, wherein said wet chemical etching fluid further comprises a chromium oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-26 | 1987-12-26 | 1988-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-26 | 1991-12-26 | 1992-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-26 | 1995-12-26 | 1996-06-26 | $7700.00 | Window Closed / Lapsed |