Catalyst regeneration process including metal contaminants removal
Assignee: IFP ENTERPRISES
•
Filing: 1981-11-02
•
Granted: 1984-06-12
•
Expires: 2001-11-02
Abstract
Abstract Spent catalysts removed from a catalytic hydrogenation process for hydrocarbon feedstocks, and containing undesired metals contaminants deposits, are regenerated. Following solvent washing to remove process oils, the catalyst is treated either with chemicals which form sulfate or oxysulfate compounds with the metals contaminants, or with acids which remove the metal contaminants, such as 5-50 W % sulfuric acid in aqueous solution and 0-10 W % ammonium ion solutions to substantially remove the metals deposits. The acid treating occurs within the temperature range of 60°-250° F. for 5-120 minutes at substantially atmospheric pressure. Carbon deposits are removed from the treated catalyst by carbon burnoff at 800°-900° F. temperature, using 1-6 V % oxygen in an inert gas mixture, after which the regenerated catalyst can be effectively reused in the catalytic process.
Inventors
- 👤 Partha S. Ganguli
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 07:45
CPC Classifications
C; C10; C10G; C10G1/00; C10G1/08; C10G1/086; B; B01; B01J; B01J23/00; B01J23/90; B01J23/94
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
138 words
A process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in coal liquefaction and petroleum residua conversion processes, comprising: (a) washing the used catalyst with a hydrocarbon solvent to remove process oils; (b) treating the oil-free catalyst with an aqueous solution consisting of sulphuric acid and an ammonium ion which converts the metal contaminants to their respective sulfate compounds and at a temperature within the range of 60°-250° F. for at least about 5 minutes to remove the metal contaminants from the catalysts; (c) washiing the treated catalyst to remove the aqueous solution; and (d) processing the washed, treated catalyst further by carbon burnoff at a temperature of 800°-900° F. using 1-6 V % oxygen in an inert gas mixture to remove carbon deposits, thereby providing a regenerated catalyst.
Claim 2
Dependent Claim
138 words
A process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in coal liquefaction and petroleum residua conversion processes, comprising: (a) washing the used catalyst with a hydrocarbon solvent to remove process oils; (b) treating the oil-free catalyst with an aqueous solution consisting of sulphuric acid and an ammonium ion which converts the metal contaminants to their respective sulfate compounds and at a temperature within the range of 60°-250° F. for at least about 5 minutes to remove the metal contaminants from the catalysts; (c) washiing the treated catalyst to remove the aqueous solution; and (d) processing the washed, treated catalyst further by carbon burnoff at a temperature of 800°-900° F. using 1-6 V % oxygen in an inert gas mixture to remove carbon deposits, thereby providing a regenerated catalyst.
Claim 3
Dependent Claim
28 words
The process of claim 1, wherein the aqueous solution used for treating the oil-free catalyst is 5-50 W % sulfuric acid and 0-10 W % ammonium ion .
Claim 4
Dependent Claim
13 words
The process of claim 1, wherein the catalyst treating time is 5-120 minutes.
Claim 5
Dependent Claim
148 words
A process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in coal liquefaction and petroelum residua conversion processes, comprising: (a) washing the used catalyst with a hydrocarbon solvent to remove process oils; (b) washing the oil-free catalyst with water to substantially fill the catalyst pores with water; (c) treating the catalyst having pores substantially water filled with an aqueous acid solution which removes the metal contaminants and at a temperature within the range of 60°-250° F. for at least about 5 minutes to remove metal contaminants from the catalyst; (d) washing the treated catalyst with a polar solvent to remove the aqueous solution; and (e) processing the washed, treated catalyst further by carbon burnoff at a temperature of 800°-900° F. using 1-6 V % oxygen in an inert gas mixture to remove carbon deposits, thereby providing a regenerated catalyst.
Claim 6
Dependent Claim
148 words
A process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in coal liquefaction and petroelum residua conversion processes, comprising: (a) washing the used catalyst with a hydrocarbon solvent to remove process oils; (b) washing the oil-free catalyst with water to substantially fill the catalyst pores with water; (c) treating the catalyst having pores substantially water filled with an aqueous acid solution which removes the metal contaminants and at a temperature within the range of 60°-250° F. for at least about 5 minutes to remove metal contaminants from the catalyst; (d) washing the treated catalyst with a polar solvent to remove the aqueous solution; and (e) processing the washed, treated catalyst further by carbon burnoff at a temperature of 800°-900° F. using 1-6 V % oxygen in an inert gas mixture to remove carbon deposits, thereby providing a regenerated catalyst.
Claim 7
Dependent Claim
22 words
The process of claim 4, wherein the acid is selected from the group consisting of sulfuric, sulfonic, nitric, acetic and citric acids.
Claim 8
Dependent Claim
136 words
A process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in coal liquefaction and petroleum residua conversion processes, comprising: (a) washing the used catalyst with a hydrocarbon solvent to remove process oils; (b) treating the oil-free catalyst with a 5-20 W % aqueous solution of ammonium peroxydisulfate which converts metal contaminants to their respective sulfate compounds and at a temperature within the range of 60° to 150° F. for at least about 5 minutes to remove the metal contaminants from the catalyst; (c) washing the treated catalyst to remove the aqueous solution; and (d) processing the washed catalyst further by carbon burnoff at a temperature of 800°-900° F. using 1-6 V % oxygen in an inert gas mixture to remove carbon deposits, thereby providing a regenerated catalyst.
Claim 9
Dependent Claim
136 words
A process for removing metal contaminants of iron, titanium, calcium, sodium, vanadium and nickel from particulate hydrogenation catalysts used in coal liquefaction and petroleum residua conversion processes, comprising: (a) washing the used catalyst with a hydrocarbon solvent to remove process oils; (b) treating the oil-free catalyst with a 5-20 W % aqueous solution of ammonium peroxydisulfate which converts metal contaminants to their respective sulfate compounds and at a temperature within the range of 60° to 150° F. for at least about 5 minutes to remove the metal contaminants from the catalyst; (c) washing the treated catalyst to remove the aqueous solution; and (d) processing the washed catalyst further by carbon burnoff at a temperature of 800°-900° F. using 1-6 V % oxygen in an inert gas mixture to remove carbon deposits, thereby providing a regenerated catalyst.
References Cited (Backward Citations)
US2704281A
Cited
US3220956A
Cited
US3562150A
Cited
US3839191A
Cited
US3791989A
Cited
US4007131A
Cited
US4301125A
Cited
US4089806A
Cited
US4268415A
Cited
US4267032A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-12 | 1987-12-12 | 1988-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-12 | 1991-12-12 | 1992-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-12 | 1995-12-12 | 1996-06-12 | $7700.00 | Window Closed / Lapsed |