Catalytic particles and process for their manufacture
Assignee: Diamond Shamrock Chemicals Co
•
Filing: 1982-04-05
•
Granted: 1984-06-12
•
Expires: 2002-04-05
Abstract
Abstract Catalytic particles with an inert, corrosion resistant support material are provided with a catalyst finely dispersed in a matrix of an insoluble electrically conducting polymer formed in situ on each particle of inert support material. The inert support particles are catalytically activated by: (a) wetting them with a solution containing an inorganic precursor compound for the catalyst and an organic precursor compound for the insoluble polymer matrix, (b) drying the particles, and (c) heat treating them to convert the precursors to the catalyst dispersed in the polymer matrix. An electrode, e.g. an oxygen-evolving anode, is produced by either fixing the catalytic particles to an electrode base, e.g. lead, or by consolidating the catalytic particles into a porous electrode body.
Inventors
- 👤 Jean Hinden
- 👤 Michael Katz
- 👤 Jurgen Gauger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:59
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/90; H01M4/92; H01M4/925; B; B01; B01J; B01J23/00; B01J23/38; B01J23/40; B01J37/00; B01J37/0009; C; C25; C25B; C25B11/00; C25B11/04; C25B11/051; C25B11/055; C25B11/069; C25B11/073; C25B11/091; C25B11/095; H01M4/926; H01M2300/00; H01M2300/0002; H01M2300/0005; H01M2300/0011; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
116 words
A process for converting particles of solid inert support material to particles having a catalytically active and stable surface comprising the steps of: (a) wetting said particles of inert support material with an activating solution in an organic solvent of an organic prepolymer which can be thermally converted to an insoluble, electrically conducting polymer and an inorganic precursor which can be thermally converted to a platinum group catalyst, (b) drying said particles to remove said solvent therefrom, and subjecting them to heat treatment so that said catalyst is obtained in finely dispersed form uniformly distributed within a matrix of the insoluble, electrically conducting polymer formed in situ on each of said particles and firmly attached thereto.
Claim 2
Dependent Claim
116 words
A process for converting particles of solid inert support material to particles having a catalytically active and stable surface comprising the steps of: (a) wetting said particles of inert support material with an activating solution in an organic solvent of an organic prepolymer which can be thermally converted to an insoluble, electrically conducting polymer and an inorganic precursor which can be thermally converted to a platinum group catalyst, (b) drying said particles to remove said solvent therefrom, and subjecting them to heat treatment so that said catalyst is obtained in finely dispersed form uniformly distributed within a matrix of the insoluble, electrically conducting polymer formed in situ on each of said particles and firmly attached thereto.
Claim 3
Dependent Claim
18 words
The process of claim 1, characterized in that said inert support material consists essentially of a valve metal.
Claim 4
Dependent Claim
13 words
The process of claim 2, characterized in that said valve metal is titanium.
Claim 5
Dependent Claim
17 words
The process of claim 1, characterized in that said inert support material is a valve metal oxide.
Claim 6
Dependent Claim
13 words
The process of claim 1, characterized in that said organic precursor is polyacrylonitrile.
Claim 7
Dependent Claim
13 words
The process of claim 1, characterized in that said organic precursor is poly-p-phenylene.
Claim 8
Dependent Claim
25 words
The process of claim 1, characterized in that said heat treatment is carried out at a temperature from about 300° C. to about 900° C.
Claim 9
Dependent Claim
30 words
The process of claim 7, characterized in that said heat treatment is carried out in air at a temperature in the range from about 300° C. to about 600° C.
Claim 10
Dependent Claim
24 words
The process of claim 8, characterized in that the duration of said heat treatment in said temperature range lies between 5 and 120 minutes.
Claim 11
Dependent Claim
23 words
The process of claim 1, characterized in that said particles are subjected to drying and heating for complete removal of said solvent therefrom.
Claim 12
Dependent Claim
68 words
The process of claim 1, characterized in that said heat treatment is carried out in two successive stages, with a first stage which is effected in air at a temperature in the range between 200° and 300° C. and a second stage which is effected in air at a temperature between 300° and 600° C., or in a non-oxidizing atmosphere at a temperature between 400° and 900° C.
Claim 13
Dependent Claim
17 words
The process of claim 1 wherein said inorganic precursor is a salt of a platinum group metal.
Claim 14
Dependent Claim
14 words
The process of claim 1 wherein said particles of inert support material are porous.
Claim 15
Dependent Claim
20 words
The process of claim 1 wherein said particles are titanium sponge of a few to several hundred microns in size.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-12 | 1987-12-12 | 1988-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-12 | 1991-12-12 | 1992-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-12 | 1995-12-12 | 1996-06-12 | $7700.00 | Window Closed / Lapsed |