Voltage stable nonlinear resistor containing minor amounts of aluminum, boron and selected alkali metal additives
Assignee: ABB Inc USA
•
Filing: 1983-02-18
•
Granted: 1984-06-05
•
Expires: 2003-02-18
Abstract
Abstract A sintered nonlinear resistor body, useful in gapless lightning arresters comprises a major amount of ZnO and additional metal oxides including at least Al2O3 and an amount of boron oxide of from about 0.005 mole % to about 0.6 mole %, in combination with a total amount of at least one selected alkali metal oxide of from about 0.005 mole % to about 0.3 mole %.
Inventors
- 👤 William G. Carlson
- 👤 Tapan K. Gupta
- 👤 Andrew S. Sweetana, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 07:03
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/10; H01C7/12; H01C7/105; H01C7/108; H01C7/112
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
128 words
A sintered high voltage resistor body which can exhibit long lasting nonlinear V-I characteristics, consisting essentially of at least about 90 mole % of ZnO and up to about 10 mole % of additional metal oxides effective to provide electrical nonlinearity within the resistor and including the combination of: (1) from about 0.002 mole % to about 0.02 mole % of aluminum oxide, and (2) from about 0.005 mole % to 0.4 mole % of boron oxide and a total amount of from about 0.005 mole % to about 0.3 mole % of at least one alkali metal oxide selected from the group consisting of sodium oxide, potassium oxide, rubidium oxide, and cesium oxide as essential ingredients, where all the oxides are homogeneously distributed through the resistor body.
Claim 2
Dependent Claim
128 words
A sintered high voltage resistor body which can exhibit long lasting nonlinear V-I characteristics, consisting essentially of at least about 90 mole % of ZnO and up to about 10 mole % of additional metal oxides effective to provide electrical nonlinearity within the resistor and including the combination of: (1) from about 0.002 mole % to about 0.02 mole % of aluminum oxide, and (2) from about 0.005 mole % to 0.4 mole % of boron oxide and a total amount of from about 0.005 mole % to about 0.3 mole % of at least one alkali metal oxide selected from the group consisting of sodium oxide, potassium oxide, rubidium oxide, and cesium oxide as essential ingredients, where all the oxides are homogeneously distributed through the resistor body.
Claim 3
Dependent Claim
134 words
The sintered nonlinear resistor of claim 1, where the amount of boron oxide present is from about 0.05 mole % to about 0.4 mole %, the amount of alkali metal oxide present is from about 0.025 mole % to about 0.2 mole %, ZnO is present from about 90 mole % to about 97 mole %, the additional metal oxides are effective to provide electrical nonlinearity completely within the bulk of the resistor and are selected from the group consisting of Bi 2 O 3 , Co 3 O 4 , MnO 2 , Sb 2 O 3 , SiO 2 , and ZrO 2 , and mixtures thereof, where the resistor is characterized as having the ability to retain its initial nonlinear V-I characteristics and its initial resistive current values during extended use.
Claim 4
Dependent Claim
15 words
The sintered nonlinear resistor of claim 1, where the alkali metal oxide is sodium oxide.
Claim 5
Dependent Claim
15 words
The sintered nonlinear resistor of claim 1, where the alkali metal oxide is potassium oxide.
Claim 6
Dependent Claim
15 words
The sintered nonlinear resistor of claim 1, where the alkali metal oxide is rubidium oxide.
Claim 7
Dependent Claim
15 words
The sintered nonlinear resistor of claim 1, wherein the alkali metal oxide is cesium oxide.
Claim 8
Dependent Claim
48 words
A plurality of the sintered nonlinear resistors of claim 1, where the resistors have flat parallel surfaces with electrodes applied to said surfaces, said resistors being enveloped in an insulator with their electrode surfaces electrically contacting each other without air gaps therebetween, to provide a gapless lightning arrestor.
Claim 9
Dependent Claim
163 words
A sintered high voltage bulk-type resistor body which can exhibit long lasting nonlinear V-I characteristics, consisting essentially of at least about 90 mole % of ZnO and up to about 10 mole % of additional metal oxides selected from the group consisting of Bi 2 O 3 , Co 3 O 4 , MnO 2 , Sb 2 O 3 , SiO 2 and ZrO 2 , and mixtures thereof, and including the combination of: (1) from about 0.002 mole % to about 0.02 mole % of Al 2 O 3 , and (2) from about 0.005 mole % to 0.4 mole % of B 2 O 3 and a total amount of from about 0.005 mole % to about 0.3 mole % of at least one alkali metal oxide selected from the group consisting of Na 2 O, K 2 O, Rb 2 O and Cs 2 O, as essential ingredients, where all the oxides are homogeneously distributed through the resistor body.
Claim 10
Dependent Claim
163 words
A sintered high voltage bulk-type resistor body which can exhibit long lasting nonlinear V-I characteristics, consisting essentially of at least about 90 mole % of ZnO and up to about 10 mole % of additional metal oxides selected from the group consisting of Bi 2 O 3 , Co 3 O 4 , MnO 2 , Sb 2 O 3 , SiO 2 and ZrO 2 , and mixtures thereof, and including the combination of: (1) from about 0.002 mole % to about 0.02 mole % of Al 2 O 3 , and (2) from about 0.005 mole % to 0.4 mole % of B 2 O 3 and a total amount of from about 0.005 mole % to about 0.3 mole % of at least one alkali metal oxide selected from the group consisting of Na 2 O, K 2 O, Rb 2 O and Cs 2 O, as essential ingredients, where all the oxides are homogeneously distributed through the resistor body.
Claim 11
Dependent Claim
84 words
The sintered nonlinear resistor of claim 8, where the amount of B 2 O 3 present is from about 0.05 mole % to about 0.4 mole %, the amount of alkali metal oxide present is from about 0.025 mole % to about 0.2 mole %, ZnO is present from about 90 mole % to about 97 mole %, and where the resistor is characterized as having the ability to retain its initial nonlinear V-I characteristics and its initial resistive current values during extended use.
Claim 12
Dependent Claim
16 words
The sintered nonlinear resistor of claim 5, where the alkali metal oxide is Na 2 O.
Claim 13
Dependent Claim
16 words
The sintered nonlinear resistor of claim 8, where the alkali metal oxide is K 2 O.
Claim 14
Dependent Claim
16 words
The sintered nonlinear resistor of claim 8, where the alkali metal oxide is Rb 2 O.
Claim 15
Dependent Claim
16 words
The sintered nonlinear resistor of claim 8, where the alkali metal oxide is Cs 2 O.
Claim 16
Dependent Claim
75 words
The nonlinear resistor of claim 8, where the amount of Bi 2 O 3 present is from about 0.5 mole % to about 3 mole %, the amount each of Co 3 O 4 , MnO 2 and Sb 2 O 3 present is from about 0.5 mole % to about 1.5 mole %, and the amount of SiO 2 and ZrO 2 present is from about 0.05 mole % to about 0.8 mole %.
Claim 17
Dependent Claim
26 words
The sintered nonlinear resistor of claim 8, having a thickness of over about 0.4 cm. and having flat parallel surfaces with electrodes applied to said surfaces.
Claim 18
Dependent Claim
48 words
A plurality of the sintered nonlinear resistors of claim 8, where the resistors have flat parallel surfaces with electrodes applied to said surfaces, said resistors being enveloped in an insulator with their electrode surfaces electrically contacting each other without air gaps therebetween, to provide a gapless lightning arrester.
References Cited (Backward Citations)
US3663458A
Cited
US3760318A
Cited
US3903226A
Cited
US4094061A
Cited
US4160748A
Cited
US4338223A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-05 | 1987-12-05 | 1988-06-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-05 | 1991-12-05 | 1992-06-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-05 | 1995-12-05 | 1996-06-05 | $7700.00 | Window Closed / Lapsed |